An intermediate, tetramethylene bis (orthophosphate), was prepared by the esterification of pyrophosphoric acid and l,4-butanediol. Then pyrophosphoric-containing modified polyesters (ATTBs) were synthesized by polycondensation of tetramethylene bis(orthophosphate), trimethylolpropane, adipic acid, and l,4-butanediol. The content of l,4-butanediol was varied from 10 to 20wt% for the reaction. The increase of the amount of l,4-butanediol in the synthesis of ATTBs resulted in increase in average molecular weight and decrease in kinematic viscosity owing to the excellent flowability and reactivity of l,4-butanediol.

Environmental friendly acrylic/urea high-solid paint(MUHC) were prepared through the curing reaction of acrylics resin(EBHC) containing 70wt% of solids content and butylated urea curing agent. The synthesis of EBHC Was done at 150℃ for 6 hours, and the results were obtained as follows : Mn=1830~2190, Mw 3290~4000, Mw/Mn=1.80~1.83 viscosity=110~352 cps, and conversion=82~92%. After the film was coated with MUHC, the various physical properties were measured. They showed that enhancement of the coating properties such as adhesion, flexibility, abrasion resistance, impact resistance, and water resistance could be expected through introdl1cing caprolactone acrylate component in acrylics resin for the high-solids content acrylics/urea coatings.

Our study is aimed at proposal of systematic verification method of molecular structure using measuring method of selective ionic determination and spectrometry on 34 kinds of surfactants such as sodium dodecyl sulfate(SDS) which are most widely used today. In the IR spectrum, unsaturated fatty acids reveal themselves by HC= at 3000~3020cm-1, and intensity of 720cm-1 depends on carbon length of alkyl group. Also ethylene oxide(EO) adducts exhibit weak characteristic bands by -CH2-CH2-O at 1350, 1100 and 950cm-1. Isethionate can be distinguished from diester succinate by intensity ratio of 1740 and 1200cm-1 spectrums, the ratio of latter is close to 1 due to 2 carboxylate radical in diester succinate. Quaternary ammonium salts exhibit characteristic band of C4N+ at 1000-900㎝-1. In the case of dialkyl dimethyl ammonium salts in quaternary ammonium surfactants, the spectrum of 3000cm-1 by N-CH3 collapses to a very weak band at 3020cm-1. In ammonium heterocyclic derivatives, pyridinium salts show characteristic bands at 1640 and 1460cm-1, while imidazolinium salts exhibit characteristic band at 1620-1610cm-1. In the characteristic spectrum at 1080-1050cm-1 on OH radicals of the alkyl esters, primary alcohol appears as weak band and the 2 bands show in almost same intensity when primary and secondary alcohols exist together in one molecule. Also, alkyl ester of polyhydric alcohols appears as various broad band.