UV-Curable hybrid coatings were synthesized to improve the surface properties of plastic film. Organic-inorganic coating solutions were prepared by the sol-gel method using urethane-acrylate oligomer, acrylate monomer, photo initiator and tetraethoxysilane (TEOS). Methacryloyloxypropyltrimethoxysilane(MPTMS) was used as a silane coupling agent to improve chemical interaction between inorganic phases and UV curable acrylate. In this study, the surface hardness and adhesive properties were improved with the use of inorganic component. The experimental results showed that UV-Curable hybrid films containing aliphatic urethane oligomer, hexanedioldiacrylate, trimethylolpropanetriacrylate, hydroxy dimethyl acetophenone exhibited good surface properties. Also, the optimum curing conditions were investigated.

Organic acid salt of fatty polyamide (DDDT) and acrylate of fatty carbamide (DDTCA) were synthesized as a main component for the softener. O/W type non-ionic softener (NSC) was prepared by blending DDDT and DDTCA with beef tallow, lanolin anhydride. polyoxyethylene(7) stearyl ether, and polyoxyethylene(50) oleyl ether. After treatment of NSC to all cotton fabrics, the physical properties such as tear strength, crease recovery, and flexing abrasion resistance were measured. As a result of the measurement, NSC was proved to be durable non-ionic softener with good softness.

Two-component polyurethane flame retardant coatings (ATTBC) were prepared by blending polyisocyanate (TDI-adduct) with ATTBs mentioned at the previous paper. Most of the physical properties of the flame retardant coatings were comparable to those of non-flame retardant coatings. Especially, the hardness, impact resistance, and accelerated weathering resistance were remarkably improved with the increase of the content of 1,4-butanediol. Coatings containing 10 and 15 wt% 1,4-butanediol, ATTBC-10C and ATTBC-15C, were not flammable in vertical flame-retardancy test. Their char area recorded 1.1~11.6 cm2 in 45˚ eckel burner method.

Acidic degreasing agent(AADA) was prepared by blending sorbitol, Newpol PE-68, Na-dioctyl sulfosuccinate, Tetronix T-70l, MJU-100A, n-octanoic acid, and phosphoric acid, The physical properties of AADA tested with aluminum specimen showed the following results ; when 3wt% AADA-5 was performed at 70℃, the degreasing rate was 95% which is comparitively good, and the percentage of etching was 0.277% which was found to be less than that of commercialized product. when 20wt% of AADA-5 was added at 65℃, the percentage of derusting was 91% and the good defoaming effect proved by following low foaming power tests respectively : Ross and Miles, and Ross and Clark methods.

Environmental friendly acrylics/urea high-solid paints (BEHCU) were prepared through the curing reaction of acrylics resin(BEHC) containing 70wt% of solids content and butylated urea curing agent. BEHC was synthesized by addition copolymerization of caprolactone acrylate(CLA), 2-hydroxypropyl methacrylate(2-HPMA), ethyl methacrylate, and n-butyl acrylate. The addition polymerization of these monomers, especially including flexible CLA monomer and 2-HPMA monomer with OH funtional group, under appropriate reaction conditions resulted in polymers with controlled glass transition temperature(Tg) and crosslinking density. The molecular weight(Mw) of these polymers(BEHCs) was 2940~3240 and polydispersity (Mw/Mn) was in the range of 1.61~1.72. The viscosity and the molecular weight of these acrylic resins increased with increasing Tg. The coated films were prepared using curing reaction between BEHC resin and butylated urea curing agent at 100℃ for 30 minutes. Our experimental resulted showed that enhancement of the coating properties such as adhesion, flexibility, impact resistance, water resistance, and abrasion resistance could be expected through introducing CLA component in acrylic resin for the high-solid content acrylics/urea coatings.

Environmental friendly acrylic/urea high-solid paint(MUHC) were prepared through the curing reaction of acrylics resin(EBHC) containing 70wt% of solids content and butylated urea curing agent. The synthesis of EBHC Was done at 150℃ for 6 hours, and the results were obtained as follows : Mn=1830~2190, Mw 3290~4000, Mw/Mn=1.80~1.83 viscosity=110~352 cps, and conversion=82~92%. After the film was coated with MUHC, the various physical properties were measured. They showed that enhancement of the coating properties such as adhesion, flexibility, abrasion resistance, impact resistance, and water resistance could be expected through introdl1cing caprolactone acrylate component in acrylics resin for the high-solids content acrylics/urea coatings.

Fatty polyamide that gives softness, lubrication and bulky property and alkyl imidazoline that gives durable softness and antistatic property were synthesized. then, an O/W-type durable softener (DSN) was prepared by the emulsion of the synthesized fatty polyamide and alkyl imidazoline. Emulsion stability of the DSN was good, and the mixed HLB value was 11.2. From the measurement of softness, lubrication, antistatic property, bending resistance, and color fastness, it was proved that the prepared DSN was a good durable softener for nylon.

Two PU flame-retardant coatings, 2,3-DBPO/N-l00 (DBPON) and 2,3-DBPO/IL (DBPOI), were prepared by curing 2,3-dibromo modified polyester (2,3-DBPO) with isocyanate curing agent Desmodur N-l00 (or Desmodur IL) at room temperature. The physical properties and flame-retardancy of the two coatings were tested and compared. As a result, the pot-life, yellowness index, lightness index difference, 60˚ specular gloss, cross-hatch adhesion, viscosity, and accelerated weathering resistance of DBPON were better than those of DBPOI; the fineness of grind of the two coatings were the same; and the drying time, hardness, and abrasion resistance of DBPOI were better than those of DBPON. The flame retardancy of the flame-retardant coatings increased with the content of the flame retarding component, 2,3-dibromopropanoic acid (2,3-DBP); and the LOI values of the two coatings were in a range of 27~29% when the content of 2,3-DBP was 30wt%.

An ACR/HMMM film was prepared by blending high-solid ACR with curing agent, hexamethoxymethyl melamine (HMMM). An active curing reaction was observed at 170℃. The dynamic viscoelastic Tg of the final film increased with the static viscoelastic Tg of the film. The log damp value, which means a viscoelastic ratio, decreased with the increase in the curing temperature of the film. Physical properties of the films were within a suitable range for films, and by an accelerated weathering resistance test the films were proved weather resistible ones.

In many climatic conditions, there is UV ray, which is called ultraviolet rays, which has the greatest effect on sealing materials. Because UV has high energy, it changes the internal structure of polymer and causes quality deterioration. In addition, temperature, humidity, and rainfall, snowfall, and atmospheric pollutants are also factors to be avoided in maintaining the integrity of the sealant. In this study, we tried to obtain reproducibility by using a composite deterioration test device which can describe the environment of the outside air as a part of the research project to investigate the weather change in the prototype of the structural sealant. The outdoor exposure test result and the composite deterioration test device Correlation analysis. In the future, it will be possible to predict the changes in the physical properties of the structural sealant by applying the composite deterioration test equipment and outdoor exposure test data.

The curtain wall performance test is mainly carried out to prevent any problems that may occur after the installation by checking whether there is a problem beforehand in the construction of the outer wall of the middle and large type construction. Since it is tested under harsh environmental conditions by applying domestic and foreign standards, many problems are found, and the biggest purpose is to improve the problems of design and construction through testing and to install better quality window products. In this study, the structural sealant products distributed in Korea were exposed to the outdoor exposure zone of the Seosan outdoor exposure test site, and compared with the curtain wall performance test of the product and the degradation of the product after 12 months outdoor exposure. In the future, it will be possible to apply the performance evaluation to the product comparison evaluation after exposing for more than 2 years.

본 최근 건축물 외벽공사에 커튼월 공법의 사용이 증가하고 있다. 외벽 커튼월 공법은 공기단축 및 경제적 효용이 크다는 장점으로 인해 건물의 외벽으로도 널리 시공되고 있다. 그러나, 커튼월 공법의 프레임과 유리를 연결해 주는 구조용 실란트에 대한 내후성 및 구조물의 거동에 대한 열화를 대체한 시험은 KS F 4910 규격에는 부재한 실정으로 안정적인 커튼월 공법 도입과 품질향상을 위해서는 필요한 요소이다. 본 연구에서는 외기환경하에서 거동에 대한 탄성복원력시험을 실시하였다. 구조용 실란트를 대상으로 열에 대한 실링재의 열화를 평가하였다. 국내에서는 구조용 실란트의 가변형 변위거동에 대한 연구는 부족한 실정으로 본 연구에서는 외기 환경에 노출된 열화조건을 대체하여 실 험실 조건에서 재현한 결과를 확인하고, 설계에 반영하고자 한다. 본 연구 결과에 따르면, 기존의 구조용 실링재는 KS F 4910의 품질기준은 만 족하지만, 본 연구에서 실시한 조건에서는 시험체의 파단과 표면의 균열 등이 발생하는 것을 확인하였다. 특히, 내후성 시험에서는 시험체 모두 불용의 상태를 확인하여 향후, 커튼월 공법에 사용되는 구조용 실링재의 장기적인 내구성능 평가가 필요한 것으로 판단된다. 따라서, 기존의 구조용 실링재가 현장에 적용되기 위해서는 별도의 내구성능 평가를 실시가 요구된다.

Selection of a typical four companies products of domestic structural one-component sealant, high temperature, low temperature, room temperature to set up the environment for each of 80, -20, 20 ℃ and the left and right displacement of the test piece 30, 15, 0% of the maximum compression / expansion It was carried out by the repeated fatigue.

본 연구는 실리콘계 정포제의 특성에 따른 폴리우레탄 폼 지수제의 cell 구조와 흡수량 변화를 알아보기 위하여 6종의 정포제를 사 용하여 폴리우레탄 폼 지수제를 제조하여 FE-SEM으로 분석한 결과 실리콘 정포제의 실록산 주사슬 말단에 PO n개가 결합되어 있는 DC-193, DC-2585, DC-5125, DC-198의 cell 구조는 close cell로 확인이 되었고, 실리콘 정포제의 실록산 주사슬 말단에 EO n개가 결합 되어 있는 DC-5043과 DC-5598은 open cell 구조로 나타났다. 또한 cell 구조 변화에 따른 흡수량 에서는 close cell의 크기가 가장 세밀하고 균일한 DC-193의 흡수량이 가장 적게 나타나 내수성이 가장 우수한 것으로 나타났으며 open cell의 크기가 가장 크게 형성된 DC-5043의 흡수량이 가 장 많은 것으로 나타났다. 이들의 방수성능을 콘크리트 구조물을 모사하여 시험한 결과 누수가 없음을 확인하였다.

The ceiling finishes and concrete structure, rather than problems with the performance of the acrylic panel to crack and leak, and poor adhesion between the acrylic panels has occurred. This is a cause that is generated based on different designs and structures, such as construction and finishing materials mainframe sealing materials, construction, coordination of the three principles of design appeared to be urgently necessary.

To improve the quality of polyurea paints, the conventional polyurea heat resistance and wear resistance performance was confirmed with the test method of KS F 4922 and KS M 6080. The test results showed that the enhanced polyurea paints increase the applicability of concrete and asphalt concrete.

This study is to introduce the results of physical property test on the polyurea ultra rapid curing membrane according to the test method by the KS F 2622