High surface area and high pore volume activated carbon was prepared by KOH activation of rice hull. The electrodes were fabricated by compounding the commercial and rice hull activated carbons with PVdF and PVdF-PVP mixed binders without addition of conductivity improver. The electrodes fabricated with rice hull activated carbon and PVdF-PVP mixed binders showed the best performance because the PVP played as a pore-forming agent. The electrode exhibited excellent electrochemical characteristics having 7.9 W.h/kg of energy density, 33.5 F/g of speific capacitance, 0.7 Ω of ESR and good efficiency of self-discharge compared with that fabricated with commercial activated carbons.

Electrochemical promotion of the reaction rate was investigated for CO oxidation in a solid electrolyte catalytic reactor where a thin film of Pt was deposited on the yttria stabilized zirconia as an electrode as well as a catalyst. It was shown under open circuit condition that potential was a mixed potential of O2exchange reaction and electrochemical reaction induced by CO. The effect of electrochemical modification on the CO oxidation rate was studied at various overpotentials and PCOPO2.

In consideration that a high tensile strength and ion exchange capacity are maintained as the swℓing of membrane is controlled by the coagulation of PSf with the introduction of ion exchange groups and PPSS without the introduction of ion exchange groups, the block copolymer of PSf and PPSS were synthesized. The cation exchange membrane was prepared by sulfonation with CSA and casted. The synthesized block copolymer and cation exchange membrane were characterized by FT-IR and their thermal stability was confirmed by TGA. The optimum sulfonation could be accomplished at a mole ratio of BPSf to CSA 1:3. The best electrochemical properties obtained by the optimal condition were area resistance of 4.37 Ωㆍtextrmcm2, ion exchange capacity of 1.71 meq/g dry membrane, water content of 0.2941 g H2O/g dry membrane, and fixed ion concentration of 5.81 meq/g H2O. When GBL was used as an additive, area resistance was increased by 13.7 % and ion exchange capacity was increased by 14.6%. When the membrane was fabricated in a form of composite using non woven cloth as a support. the tensile strength of membrane could be improved, but the electrochemical characteristics were not influenced.

운반체(감응물질)로 제 4급 인산염을 사용하여 PVC를 지지체로 하여 과염소산이온의 농도 10-6 M까지 선형적인 이온선택성 전극을 제작하였다. 운반체의 화학적구조와 함량 가소제의 종류 및 막 두께에 따른 전극의 기울기 선형응답범위 및 한계측정농도 등 전극전위특성을 고려하여 최적의 과염소산 이온선택성 PVC막 전극을 제조한 다음 측정 가능한 pH 범위 선택계수 및 전극의 교류임피던스 특성을 비교 검토하였다 운반체로 tetraoctyl-phosphonium perchlorate(TOPP) tetraphenylphosphonium perchlorate(TPPP) 및 tetrabutylphosponium perchlorate (TBPP) 등의 제 4급 인산염의 과염소산 이온 치환체를 사용하였다 알킬기의 탄소고리 수가 증가할수록 전극특성은 TBPP, 선형응답범위 10-1×10-6 M 및 한계측정농도는 9.66×10-7 M 이었으며 시판되고 있는 Orion 전극특성보다 좋은 결과를 나타내었다 전극전위는 pH3~11범위에서 ph의 영향을 받지 않았으며 CIO4 에 대한 방해이온의 선택계수 서열은 SO24 < F < Br < I 이었다 임피던스 측정결과 TOPP의 경우 등가회로는 용액저항 이중층용량과 벌크저항의 병렬 및 Warburg 임피던스의 직렬이었다 이 경우 용액저항은 거의 나타나지 않았고 확산에 의한 Warburg 임피던스는 크게 나타났으며 Warburg 계수는 1.32×1074 Ω cdot cm2/s1/2이었다.

본 연구에서는 복합막의 합성을 위한 기초연구로 상용막에 대한 전기화학적 물성과 레독스-흐름전지의 충방전실험을 통해 셀저항과 막저항을 특정하였다. 셀저항율과 막저항율은 충전할 때보다 방전할 때가 더 높았으며 동일한 막에서는 충전심도가 커질수록 저항율이 커짐을 알 수 있었다. hydrocarbon type인 Selemion CMV막이 perfluoro type인 nafion 117, 551막보다 저항율이 작음을 알 수 있었으며 2N 염산수용액에서 충전심도가 0%일 때 셀 저항율과 막저항율이 각각 12.864Ωcm2 , 8.751Ωcm2 였다.

감응물질로 제4급 암모늄염을 사용하여 PVC를 지지체로 과염소산이온의 농도 10-6M까지 측정가능한 이온 선택성 전극을 제작하였다. 감응물질의 화학적 구조와 함량, 가소제의 종류 및 막 두께에 따른 선형응답 범위와 Nernst의 기울기 등 전극특성을 검토하여, 최적 막조건을 구한 다음 측정가능 pH범위와 여러 방해이온에 대한 선택계수를 비교 검토하였다. 과염소산 이온선택성 전극에서 감응물질의 화학적 구조 즉, 알킬기의 탄소고리수가 증가할수록 선형응답 범위 등 전극 특성은 Aliquat 336P, TOAP, TDAP 및 TDDAP의 순서로 좋아졌다. 가소제는 DBP가 가장 좋았고, 감응물질의 양은 최적 함량 이상에서 적을수록 좋았다. 최적 막 조성은 TDDAP 9.09, PVC 30.3 및 DBP 60.61wt%이었고, 막두께 0.45mm이었다. 이 조건에서 선형응답 범위 10-1~1.2 × 10-6M, 검출한계 5.1×10-7M 및 Nernst기울기 57mV/pClO4이었다. 막전위는 pH 4~11 범위에서 pH의 영향을 받지 않았으며, 선택계수 서열은 다음과 같았다. SCN->I->NO3->Br->ClO3->F->Cl->SO42-