In order to clarify the wear resistance as cutting tools, the effect of oxygen addition on oxidation behavior of the β-Si3N4 ceramics with 5 mass% Y2O3 and 2 or 4 mass% Al2O3 was investigated by performing oxidation tests in air at 1300° to 1400°C and cutting performance tests. From test results, we could conclude that the mechanical properties of β-Si3N4 ceramics depending on oxygen introduction are much effective on cutting performance improvements of β-Si3N4 ceramics.

The effect of TiC content on oxidation behavior of the sintered WC-TiC-TaC alloys with 2 mass% TaC and different TiC amounts of 3-45 mass% was investigated through oxidation tests in air at 973K. As a result of the tests, it was revealed that with increasing TiC content in the alloys, mass changes caused by oxidation and thickness of the scale decreased. Thus, it is considered that the main component of the scales changed gradually from to with increasing TiC content in the alloys, and oxygen diffusion through the scale to the alloys was inhibited gradually.