This study explores the profound impact of varying oxygen content on microstructural and mechanical properties in specimens HO and LO. The higher oxygen concentration in specimen HO is found to significantly influence alpha lath sizes, resulting in a size of 0.5-1 μm, contrasting with the 1-1.5 μm size observed in specimen LO. Pore fraction, governed by oxygen concentration, is high in specimen HO, registering a value of 0.11%, whereas specimen LO exhibits a lower pore fraction (0.02%). Varied pore types in each specimen further underscore the role of oxygen concentration in shaping microstructural morphology. Despite these microstructural variations, the average hardness remains consistent at ~370 HV. This study emphasizes the pivotal role of oxygen content in influencing microstructural features, contributing to a comprehensive understanding of the intricate interplay between elemental composition and material properties.

In Korea, most temporary storage facilities for spent nuclear fuel are nearing saturation. As an alternative to this, the 2nd basic plan for high-level radioactive waste management specified the operation plan of dry interim storage facility. Meanwhile, the NSSC No. 2021-19 stipulates that it is necessary to evaluate the possibility and potential effect of accident before operating interim storage facility. Therefore, this study analyzed the categories of accident scenarios that may occur in dry storage facility as part of prior research on this. We investigated the case of categorization of dry storage facility accident scenarios of IAEA, NRC, KAREI, and KINS. The IAEA presented accident scenarios that could occur in on-site dry storage facility operated with silo and cask method. NRC has classified accident scenarios in dry storage facility and estimated the probability of accidents for each. KAERI and KINS selected major accident scenarios and analyzed the processes for each, in preparation for the introduction of dry storage facility in Korea in the future. Overall, a total of 10 accident scenarios were considered, and the scenarios considered by each institution were different. Among 10 scenarios, cask drop and aircraft collision were included in the categorization of most institutions. The results of this study can be used as basic data for cataloging accidents subject to safety evaluation when introducing dry interim storage facility in Korea in the future.

Exploring earth-abundant, highly effective and stable electrocatalysts for electrochemical water splitting is urgent and essential to the development of hydrogen (H2) energy technology. Iron-cobalt layered double hydroxide (FeCo-LDH) has been widely used as an electrocatalystfor OER due to its facile synthesis, tunable components, and low cost. However, LDH synthesized by the traditional hydrothermal method tends to easily agglomerate, resulting in an unstable structure that can change or dissolve in an alkaline solution. Therefore, studying the real active phase is highly significant in the design of electrochemical electrode materials. Here, metal-organic frameworks (MOFs) are used as template precursors to derive FeCo-LDH from different iron sources. Iron salts with different anions have a significant impact on the morphology and charge transfer properties of the resulting materials. FeCo-LDH synthesized from iron sulfate solution (FeCo-LDH-SO4) exhibits a hybrid structure of nanosheets and nanowires, quite different from other electrocatalysts that were synthesized from iron chloride and iron nitrate solutions. The final FeCo-LDH-SO4 had an overpotential of 247 mV with a low Tafel-slope of 60.6 mV dec-1 at a current density of 10 mA cm-2 and delivered a long-term stability of 40 h for the OER. This work provides an innovative and feasible strategy to construct efficient electrocatalysts.

역세척이 가능한 평막형 분리막 모듈을 분리막 생물반응기(MBR)에 침지시켜 운전 시간에 따른 흡입 압력을 측 정하였다. MLSS 8,000 mg/L 활성 슬러지 수용액에 공칭 세공크기가 0.2 μm, 유효막면적이 128 cm2인 분리막 모듈을 침지 시킨 후 투과 유속, quorum qeunching (QQ) 비드를 변화하며 흡입 압력을 확인하였다. Vacant bead (VB), BH4와 DKY-1의 실험군에서 FR과 SFCO 운전방식에 따른 효과를 비교, 분석하였다. 투과 유속 40 L/m2⋅h 이고 DKY-1 QQ 비드를 주입할 경우 흡입 압력 감소는 가장 효과적이었다. 또한 역세척에 의한 흡입 압력 감소 효과는 DKY-1 QQ 비드의 경우보다 2배 이 상 높게 나타났다.

The oxygen evolution reaction (OER) is very sluggish compared to the hydrogen evolution reaction (HER). Considering this difference is essential when designing and developing a cost-effective and facile synthesis method for a catalyst that can effectively perform OER activity. The material should possess a high surface area and more active sites. Considering these points, in this work we successfully synthesized sheets of cobalt phosphate hydrate (CP) and sulphurated cobalt phosphate hydrate (CPS) material, using simple successive ionic layered adsorption and reaction (SILAR) methods followed by sulfurization. The CP and CPS electrodes exhibited overpotentials of 279 mV with a Tafel slope of 212 mV dec1 and 381 mV with a Tafel slope of 212 mV dec1, respectively. The superior performance after sulfurization is attributed to the intrinsic activity of the deposited well-aligned nanosheet structures, which provided a substantial number of electrochemically active surface sites, speeded electron transfer, and at the same time improved the diffusion of the electrolyte.

Cement is widely used as representative industrial material. In Korea, about 50 million tons of cement are consumed every year. In the manufacture of cement, raw materials containing NORM such as fly ash and bauxite are used. Therefore, the workers can be subjected to radiation exposure. The major exposure pathway in NORM industries is internal exposure due to inhalation of aerosol. Internal radiation dose due to aerosol inhalation varies depending on physicochemical properties of the aerosol. Therefore, the objective of this study was to investigate aerosol properties influencing inhalation dose in cement industries. In this study, aerosol properties were measured for two cement manufacturers. A particulate size distribution and concentration at various processing areas in cement manufacturing industries in Korea were analyzed using a cascade impactor. The mass density of raw materials and byproducts were measured using pycnometer. Shape of particulates was analyzed using SEM. The radioactivity concentration of Ra-226, Ra-228 for U/Th decay series was measured using HPGe. Particulate concentration by size was distributed log-normally with maximum at particle size about 7.2 μm in manufacturer A and 5.2 μm in manufacturer B. The mass density of fly ash and cement were 2.3±0.06, 3.2±0.02 g/cm3 respectively in manufacturer A. In manufacturer B, the mass density of bauxite and cement were 3.4±0.02, 2.9±0.01 g/cm3 respectively. The shape of particulates appeared as spherical shape in manufacturer A and B regardless of sampling area. Thus, a shape factor of unity could be assumed. The radioactivity concentrations of Ra-226, Ra-228 were 82±9, 82±8 Bq/kg for fly ash, and 25±4, 23±3 Bq/kg for cement in manufacturer A. In manufacturer B, the radioactivity concentrations of Ra-226, Ra-228 were 344±34, 391±32 Bq/kg for bauxite, and 122±13, 145±12 Bq/kg for cement. The radioactivity concentrations of Ra-226, Ra-228 in cement were less than raw materials such as fly ash and bauxite. It is because the dilution of the radioactivity concentration occurred during mixing with other raw materials in cement production process. This study results will be used as database for accurate dose assessment due to airborne particulate inhalation by workers in cement industries.

Designing and producing a low-cost, high-current-density electrode with good electrocatalytic activity for the oxygen evolution reaction (OER) is still a major challenge for the industrial hydrogen energy economy. In this study, nanostructured Fe-doped CuCo(OH)2 was discovered to be a precedent electrocatalyst for OER with low overpotential, low Tafel slope, good durability, and high electrochemically active surface sites at reduced mass loadings. Fe-doped CuCo(OH)2 nanosheets are made using a hydrothermal synthesis process. These nanosheets are clumped together to form a highly open hierarchical structure. When used as an electrocatalyst, the Fe-doped CuCo(OH)2 nanosheets required an overpotential of 260 mV to reach a current density of 50 mA cm−2. Also, it showed a small Tafel slope of 72.9 mV dec−1, and superior stability while catalyzing the generation of O2 continuously for 20 hours. The Fe-doped CuCo(OH)2 was found to have a large number of active sites which provide hierarchical and stable transfer routes for both electrolyte ions and electrons, resulting in exceptional OER performance.

In Korea, research on the introduction of dry storage facility is being conducted as an alternative to saturation of temporary storage facilities for spent nuclear fuel. The introduction of dry storage facilities requires a radiological impact assessment on the workers of the facility, and for this, an appropriate exposure scenario must be derived through work procedure analysis. In this study, the procedure for storing spent nuclear fuel in dry storage facilities was analyzed based on the case of evaluating the radiological impact of workers in dry storage facilities abroad. We investigated cases of radiological impact assessment on workers at on-site dry storage facilities by PNNL, Dominion, and P. F. Weck. PNNL and Dominion analyzed the storage work procedure of the VSC (Vertical Storage Cask) method using CASTOR V/21, TN-32, respectively, and conducted a radiological impact assessment. P. F. Weck analyzed the storage work procedure of various spent nuclear fuel casks for VSC and HSM (Horizontal Storage Module), conducted a radiological impact assessment. As a result of comparing the procedure for storing spent nuclear fuel by case, it was found that the storage procedure was determined by the storage method and the cask type. In the case of VSC method, canister-type casks and basket-type casks are used, and the storage procedure are partially different according to each. Canister-type cask requires repackaging from transfer overpack to storage overpack, but basket-type cask doesn’t require that procedure. In the case of the HSM method, only the canister type cask was found to be used. However, the storage procedure was different depending on the type of HSM system. Depending on the type of HSM system, the necessity of cask for on-site transport was different. In this study, we investigated and analyzed the work procedure according to the storage method of dry storage facilities abroad. It was found that the dry storage procedure of spent nuclear fuel different according to the storage method and type of cask. The results of this study can be used as basic when deriving the exposure scenario for spent nuclear fuel dry storage workers suitable for the domestic situation.