In this study, the relationship between the pore size distribution and the adsorption amount of adsorbates is investigated in detail. Adsorption amounts of non-polar adsorbates were greater than those of polar adsorbates because of slight negative charge on surfaces of adsorbents. The adsorption of benzene on the surface of absorbents was largely influenced by the specific pore size of 2～4 times of benzene diameter. But in case of toluene, the adsorption of toluene was affected by pore sizes of 2～4 times as well as 4～6 times of the diameter of toluene. Both acetone and MEK were examined by the same method. The adsorption of acetone was influenced by pore sizes of 2～4 times of the diameter of acetone. But acetone does not look to be built up multi-layer on those pore sizes. Since acetone molecule is small and its mobility is so fast, it is assumed that the adsorption and desorption of acetone is simultaneously occurred at the same time even at room temperature. In case of MEK, MEK was effected by pore sizes of 2～4 times of the diameter of MEK.

This study is to investigate the relationship between pore structures of activated carbons and adsorption characteristics of toluene vapor using dynamic adsorption method. The surface areas of below 10Å in the pore diameter of activated carbons used in this experiment were in the range of 72～93％ of total cumulative surface area and the toluene vapor equilibrium adsorption capacities were in the range of 350～390mg/g. Activated carbons having larger toluene adsorption capacity than the compared activated carbons had relatively pores in the pore diameter range of 7～10Å. Linear relationship between equilibrium adsorption capacity and cumulative surface area was in the diameter range of over 7Å. It was thought that toluene vapor was relatively well adsorbed on surfaces of pores of over 7Å.