The objective of this study was to evaluate the possibility of simultaneous removal of ammonium, nitrate and phosphorus in water using the zeocarbon. In this study, the surface of zeocarbon was modified by acid because of difficulty in application of water treatment. After surface modification, the strength was enhanced about 62% higher than that of original one. The removal efficiency of ammonium and nitrate using the modified zeocarbon was about 47% and 32%, respectively and were higher than that of zeocarbon. In batch type experiment on the simultaneous removal of ammonium, nitrate and phosphorus, the presence of phosphorus did not have influence on nitrogen removal efficiency. Concomitantly, removal efficiency of phosphorus was obtained was about 35%. This indicates that the surface modified zeocarbon can be applied for simultaneous removal of nitrogen and phosphorus. Consequently, our results could be used as basic data to design of one-stage nitrogen/phosphorus simultaneous removal system.

The objective of this study was to investigate the possibility of application for water treatment using the zeocarbon. The zeocarbon was mixture of zeolite and activated carbon. In general, the application of commercial zeocarbon to water treatment is difficult because of weak strength in water and the high pH value of effluents after water treatment. Therefore, we have modified the surface of zeocarbon. For the surface modification, we used the acid treatment to make surface functional group. As a result of modification, was created functional group on zeocarbon surface and was formed mesopore in zeocarbon. The surface modified zeocarbon was applied to removal of nitrogen. In removal experiments of nitrogen, removal efficiency was very high. And, strength of zeocarbon after water treatment and pH of effluents were stabilized. This indicates that the surface modified zeocarbon was easy to recover and reuse. Consequently, our results were shown the possibility of application for water treatment using the surface modified zeocarbon.

MCMB (Mesocarbon microbeads) is a kind of anode material for lithium-ion secondary battery. MCMB charge/discharge cycle stability is one of the important criterion at lithium-ion battery operation. In this study, the cycling stability of a lithium-ion secondary battery has been examined. MCMB was made by the direct solvent extraction method. After the MCMB was carbonized and graphitized, the measurement of charge/discharge capacity and efficiency were carried out. In the result, discharge capacity of MCMB in the initial cycle was above 290.0 mAh/g. After the second cycle, efficiency of charge/discharge MCMB was about 98%. These results were similar to the commercial MCMB product.

MCMB (mesocarbon microbeads) has been synthesized from coal tar pitch, petroleum pitch and polymer compound generally. But yield of MCMB was low about 20~40 wt% and was not above 50 wt%. Neither MCMB was replaced with natural graphite because of economic performance, refining MCMB, and control of the particle size distribution. This study was performed to elevate yield of MCMB and to develop technique of particle size distribution. As the result, yield of MCMB that was synthesized from coal tar pitch increased more than 60 wt% about raw material and particle size of MCMB was restrained according to control of QI (quinoline insoluble) ingredient in raw pitch, heat treatment temperature and time.