In this study, experiment and analysis of high-strength bolt connection under shear fatigue loading was conducted to evaluate reduction of axial force of bolt. Three type of bolt size and initial axial force were applied to specimens. As a results, it was observed that the reduction ratio of axial force, and that would be used to additional parametric study.

Authors investigated the fatigue bond performance on the grouted joint connection of wind tower. High strength cementeous grout has 140MPa of a compressive strength was incerted in the gap of small scaled steel tube simulated the wind tower joint. The stress level was 65 and 74% of static strength that is 35MPa, respectevely. From the test, each specimens endured the repeated loads up to 2,000,000 cycles.

Rolling fatigue test was performed to study the behavioral characteristics of prestressed rib-type UHPC deck built-in optical sensors for cable-stayed bridges. As the result, it was verified that this deck has sufficient structural fatigue performance and serviceability as a bridge deck.

본 연구에서는 기존의 교면포장 공법인 아스팔트와 라텍스 개질 콘크리트 포장의 단점을 극복한 교면포장용 고성능 콘크리트의 개발을 위하여 교면포장용 콘크리트 슬래브의 내구성을 평가하였다.교면포장용 고성능 콘크리트의 배합으로는 A-Type (실리카퓸 6%), B-Type (실리카퓸 6%+플라이애쉬 20%), C-Type (실리카퓸 6%+고로슬래그 40%)의 3가지 종류를 고려하였고 현재 교면 포장에 사용되고 있는 라텍스 개질 콘크리트 포장(LMC)과 일반 콘크리트 포장(OPC)에 대하여 비교 평가하였다. 내구성 평가를 위한 실험으로는 정적재하실험과 피로실험을 실시하였으며 처짐 및 균열폭과 콘크리트 및 철근 변형률을 측정하여 비교하였다. 또한 범용 프로그램인 ABAQUS를 이용한 유한요소 해석을 통하여 실험결과를 검증하였다. 실험결과, 정적재하시험의 경우 고성능 콘크리트 배합이 LMC 및 OPC에 비하여 역학적 특성 및 내구성에 있어서 우수한 성능을 보여주었다. 고성능 콘크리트 배합 중에선 A-Type이 처짐 및 균열저항성에 있어서 가장 우수한 것으로 나타났다. 피로시험의 경우에는 고성능 콘크리트 배합이 LMC 및 OPC에 비하여 균열저항성이 우수한 것으로 나타났으나 전체적인 거동은 모든 시험체가 일정하게 유지되어 반복하중에 대하여 충분한 내하력 및 강성을 확보하고 있는 것으로 판단된다. 유한요소 해석 결과, 처짐의 경우 1~4mm, 변형률의 경우 최대 12%의 상대오차를 보여 실험결과와 유사한 변형을 보였다

This study is to evaluate fatigue resisting capacity of insulated sandwich wall panel under wind-induced fatigue loading. The fatigue loading is calculated based on the probability distribution function (Weilbull and Rayleigh). The serviceability of the insulated sandwich panel was evaluated subjected to the probability-based fatigue loading.

This test is accomplished by one for performance evaluation of FRP which takes center stage for new material recently. generally, FRP is CFRP, AFRP, GFRP which are high tensile rebar and light material than steel reinforcement. Therefore, the research about the long-term performance assessment of FRP is needed. we performed fatigue test in this study as part of the test.

에폭시 모르타르의 적정 배합비를 결정하기 위해서 규사의 입도 조정을 통해 적정 입도비를 알아보고, 규사인 60목과 4호의 배합비를 달리한 공시체를 제작하여 각각의 압축 및 인장 실험을 실시한다. 체의 치수(mm)종류체통과 중량 백분율(%)2.51.20.60.30.15모래80-10050-9025-6010-302-102.2 규사의 입도 조정