현재 기계적 합금화법에서는 주로 합금을 구성하는 성분원소 분말을 불활성분위기에서 볼밀처리 함으로써 함금화를 시키거나 모합금에 산화물을 분산시켜 복합화시키는 공정을 통하여 각종 화합물, 비정질상 및 과포화고용체등의 준안정상의 합성 뿐만이 아니라 초미세조직의 생성에 관한 폭 넓은 분야의 연구가 행하여지고 있다. 한편 MA에서는 볼멀처리중 기계적 에너지의 투여에 의하여 실제 반응온도보다 낮은 온도에서 발생하는 특이한 화학반응 즉 Mechanochemical

A study was made on the fabrication of nanostructured Fe-Co powders by mechanical alloying and their magnetic properties. Microstrural development during the process of MA was inverstigated by means of X-ray diffraction, differential thermal analyzer, scanning electron microscopy and transmission electron microscopy. The magnetic properties of NS Fe-Co powders were evaluated through the measurements of the saturation magnetization as well as the coercivity . The average grain size calculated from line braodening in XRD peak was about 10nm or less and confirmed by TEM. In this experiment, two different milling methods (cycle opertion and conventional milling) were used. Cycle operation had an advantage over the conventional milling method in that more refined powders can be obtained. Solid state alloying of the components was confirmed from both the change of the saturation magnetization and the change of lattice parameter with Co contentration. Maxium was obtained at the composition of 30at.%Co. Relatively high coercivities of 10~150e were obtained for the compositions investigated, and this seems to be due to the high amount of internal strain introduced during milling.