Concrete behaves as a brittle material with low tensile strain capacity. By adding fibers, the cracking in concrete matrix is controlled, and the mechanical properties are improved. In this study, the mechanical properties of fiber reinforced concrete are compared with fiber type and fiber volume fraction. From the results, the fiber mixed in concrete must be at least 0.5% regardless fiber type, in order to ensure the compressive and flexural strength equivalent or higher than OPC.

Concrete behaves as a brittle material with low tensile strain capacity. By adding fibers, the cracking in concrete matrix is controlled, and the durability is improved. In this study, the microstructure and Chloride diffusion resistance of fiber reinforced concrete are compared with fiber type and fiber volume fraction. From the results, the fiber mixed in concrete must be at least 0.5% regardless fiber type, in order to ensure the chloride diffusion coefficient higher than OPC at 91days. However, the micro structure distribution is affected with fiber volume fraction and fiber type at range 10~100nm.

Concrete shrinkage is happened due to the cement hydration and water evaporation from early ages, and it induces crack of concrete. In this study, the crack resistance of fiber reinforced concrete was compared with fiber type and fiber volume fraction. From the results, cracking is delayed when the volume fraction is increased. And, crack resistance is improved regardless of fiber type.

본 연구는 SIFCON 형태의 고성능 강섬유보강 시멘트 복합체의 섬유혼입률에 따른 휨실험을 수행하였고, 실험결과를 바탕으로 휨성능을 평가하였다. 슬러리를 충전하는 형태로 일반 섬유보강시멘트와 달리 높은 섬유혼입률을 확보할 수 있는 장점을 가지고 있다. 주요 실험변수는 섬유혼입률 8.0%, 7.5%, 7.0%, 6.5% 및 6.0% 이며, 각 변수에 대한 휨강도 및 휨인성 특성을 분석하였다. 그 결과, 높은 섬유혼입률로 인하여 초기균열 발생 이후에도 계속적으로 하중이 증가하였으며, 최대강도 이후 충분한 잔류강도를 확보하였다. 또한 최대 50MPa 수준의 높은 휨강도를 발현하였으며, 섬유혼입률에 따른 휨강도 및 휨인성은 비례하여 증가하는 경향으로 나타났다.

The purpose of this study was to effects on flexural performance of SFRC prism with different fiber volume fraction. The test variables such as aggregate maximum size(8, 13, 20mm) and steel fiber volume faction(0, 1, 2%). Specimen size is 100×100×400mm and tested in for points loading. Test results indicated that increase the fiber volume fraction increase with flexural strength and smaller aggregate size more than higher performance with concrete.

The purpose of this study is to estimate basic mechanical properties of steel fiber reinforced Alkali-Activated Slag(AAS) concrete. Principle variable is the fiber volume fraction: 0, 0.5, 1%. Two type cement composites were used: Steel Fiber Reinforced Concrete(SFRC) and AAS. Mechanical properties of AAS concrete and SFRC, including compressive strength, elastic modulus, flexural strength, splitting tension.

This paper present results from effect of fiber volume fraction on direct shear property of steel fiber reinforced concrete(SFRC). Steel fiber with crimped end was used this work. Principal variable is fiber volume fraction; 0, 0.5, 1, 1.5, 2%, and aggregate size; 8, 13, 20mm. Specimen cross-sectional is 100 x 100 x 400mm. In order to induce the shear failure 2mm notch was sawed all around the specimen. Test result, there are little different between the aggregate size, and the improvements in shear strength of SFRC were more significant for 1% steel fiber volume fraction.

폴리프로필렌섬유보강 시멘트 복합재료와 구조용 합성섬유의 부착특성을 평가하였다. 폴리프로필렌섬유는 0.10%, 0.15% 및 0.20%의 체적비로 적용하여 dog-bone 시험을 실시하였다. 구조용 합성섬유와 폴리프로필렌섬유보강 시멘트 복합재료 사이의 부착강도는 폴리프로필렌섬유의 혼입률이 증가할수록 증가하였으나 0.20% 이상이 되면 감소하였다. 또한 폴리프로필렌섬유의 첨가는 계면인성과 마찰저항을 증가시킨다. 인발시험 후 구조용 합성섬유 표면의 미소구조 분석은 폴리프로필렌섬유의 혼입률이 증가할수록 긁힘 현상이 증가하였다.