OBJECTIVES: This study is to develop the optimum mixing proportions for cement concrete pavement with using recycled aggregates. METHODS: The mixture varied recycled coarse aggregates content from 50 % to 100 % to replace the natural coarse aggregates by weight. Tests for fundamental properties as a cement concrete pavement were conducted before and after hardening of the concrete. RESULTS: It was found that the variation in the amount of the recycled aggregate affected the compressive and flexural strength development, as well as the chloride ion penetration resistance. As the amount of the recycled aggregate content increased the compressive and flexural strength and the resistance to chloride ion penetration decreased. However, the resistance to freeze-thaw reaction was affected significantly. In addition, the gradation of the aggregate became worse and hence so did the coarseness factor as the recycled aggregate amount increased. CONCLUSIONS : The fundamental properties of the concrete with recycled aggregate does not seem to be appropriate when the recycled aggregate quality is not guaranteed up to a some level and its replacement ratio is over 50%. The optimized gradation of the aggregates should also be sought when the recycled aggregate is used for the cement concrete pavement materials.

Background : Constipation is can refer to bowel movements that are rare or hard for pass. Constipation is common symptom in current people and the treatment of constipation focused on the use of medicines or physical intervention. The aim of this study are investigates the effects of modified-extracts of Salicornia herbacea (S. herbacea) L. on constipation model. Methods and Results : To investigate the effect of these extracts on constipation model with Sprague-Dawley rats by loperamide administration, we orally administered various dosage of modified-extracts of S. herbacea. L. Then, we checked constipation-related parameters such as fecal number, colon weight, colonic transmit length, colon length as compared to the controls and ameliorated in a dose dependent manner. The results indicated that modified-extracts of S. herbacea. L. was ameliorated constipation in SD rat model. Conclusion : Based on the results, modified-extracts of S. herbacea L. and its many ingredients were considered to have effects on constipation.

본 연구는 SIFCON 형태의 고성능 강섬유보강 시멘트 복합체의 섬유혼입률에 따른 휨실험을 수행하였고, 실험결과를 바탕으로 휨성능을 평가하였다. 슬러리를 충전하는 형태로 일반 섬유보강시멘트와 달리 높은 섬유혼입률을 확보할 수 있는 장점을 가지고 있다. 주요 실험변수는 섬유혼입률 8.0%, 7.5%, 7.0%, 6.5% 및 6.0% 이며, 각 변수에 대한 휨강도 및 휨인성 특성을 분석하였다. 그 결과, 높은 섬유혼입률로 인하여 초기균열 발생 이후에도 계속적으로 하중이 증가하였으며, 최대강도 이후 충분한 잔류강도를 확보하였다. 또한 최대 50MPa 수준의 높은 휨강도를 발현하였으며, 섬유혼입률에 따른 휨강도 및 휨인성은 비례하여 증가하는 경향으로 나타났다.

Sustainable and eco-friendly polymers, natural polymers, bio-based polymers, and degradable polyesters, are of growing interest because of environmental concerns associated with waste plastics and emissions of carbon dioxide from preparation of petroleum-based polymers. Degradable polymers, poly(butylene adipate-co-terephthalate) (PBAT), poly(propylene carbonate) (PPC), and poly(L-lactic acid) (PLLA), are related to reduction of carbon dioxide in processing. To improve a weak mechanical property of a degradable polymer, a blending method is widely used. This study was forced on the component separation of degradable polymer blends for effective recycling. The melt-mixed blend films in a specific solvent were separated by two layers. Each layer was analysed by FT-IR, DSC, and contact angle measurements. The results showed that each component in the PPC/PLLA and PPC/PBAT blends was successfully separated by a solvent.

본 연구의 목적은 황토의 식이 첨가에 의한 돼지의 성장 특성과 혈중 조성물의 변화를 규명하는 것이다. 총 153마리의 돼지(1주령 자돈 60마리 및 성돈 93마리)를 공시하였다. 자돈군은 일반사료 식이군, 0.5% 황토 + 일반사료 식이군, 1% 황토 + 일반사료 식이군으로 무작위로 3군으로 재배치하였다. 각 군간 증체량을 비교하였을 때 1% 황토가 포함된 사료를 식이한 군에서 일반사료와 0.5% 황토 + 일반사료 투여군에 비해 체중 증가가 관찰되었으나 통계적으로 유의하지는 않았다. 혈액학적 분석을 실시한 결과, 총 백혈구 수, 총 적혈구 수, 헤모글로빈 수, 혈액 중 혈구용적율, 평균 세포용적율, 평균 세포 내 헤모글로빈량, 평균 세포 내 헤모글로빈 농도, 평균 적혈구 폭, 혈소판 수치 등에서 각 군간의 유의한 차이가 없음을 확인하였다. 성돈군은 일반사료 식이군과 1% 황토 + 일반사료 식이군으로 구분하였으며, 혈청학적 분석에서 혈청 알부민의 농도는 1% 황토 + 일반사료 투여군에서 다른 군에 비하여 유의하게 증가하여 있는 것을 확인하였으나(p<0.01), 다른 지표들에서는 유의한 차이를 발견할 수 없었다. 황토가 포함된 사료를 투여한 군에서 획득한 분변의 조지방 함량은 다른 군에 비하여 유의하게 감소하는 것을 확인하였으며(p<0.001), 조단백 함량 및 조회분 함량은 유의한 차이를 보이지 않았다. 도체의 무게와 등지방 두께의 측정 결과 각 군간의 유의한 차이는 발견할 수 없었으나, 도체의 등급 판정 결과 황토를 투여한 군의 도체 등급은 비투여군에 비해 유의하게 등급이 향상된 것을 확인하였다. 이러한 결과는 황토의 식이 첨가는 돼지의 영양소 흡수를 개선시킴으로서 도체의 등급을 향상시키는 것을 확인하였다.

본 연구에서는 도라지 추출물에 대한 세포 독성을 확인하였으며, Aβ에 의한 PC12 세포 독성에 대한 보호효과를 관찰하였다. 또한 도라지 추출물과 도라지 추출물 연양갱을 4주간 강제 경구 투여하여 Morris 수중미로시험에서 도달지점까지의 도달시간이 도라지 추출물 및 도라지 추출물 연양갱 투여에 의해서 모두에서 유의하게 감소하였다. 이와 유사하게 수동회피시험에서도 자극이 있는 어두운 방을 나오는 시간이 도라지 추출물 및 도라지 추출물 연양갱 투여에 의해서 현저하게 감소하였다. 따라서 도라지 추출물 및 도라지 추출물 연양갱은 인지능 개선에 도움을 줄 것으로 생각된다.