Abstract This manuscript reports on compared color evolution about phase transformation of α-FeOOH@SiO₂ and β-FeOOH@SiO2 pigments. Prepared α-FeOOH and β-FeOOH were coated with silica for enhancing thermal properties and coloration of both samples. To study phase and color of α-FeOOH and β-FeOOH, we prepared nano sized iron oxide hydroxide pigments which were coated with SiO2 using tetraethylorthosilicate and cetyltrimethyl-ammonium bro- mide as a surface modifier. The silica-coated both samples were calcined at high temperatures (300, 700 and 1000°C) and characterized by scanning electron microscopy, CIE L*a*b* color parameter measurements, transmission electron microscopy and UV-vis spectroscopy. The yellow α-FeOOH and β-FeOOH was transformed to α-Fe2O3 with red, brown at 300, 700°C, respectively.

This manuscript reports on compared color evolution about phase transformation of α-FeOOH@SiO2 and β-FeOOH@SiO2 pigments. Prepared α-FeOOH and β-FeOOH were coated with silica for enhancing thermal properties and coloration of both samples. To study phase and color of α-FeOOH and β-FeOOH, we prepared nano sized iron oxide hydroxide pigments which were coated with SiO2 using tetraethylorthosilicate and cetyltrimethyl-ammonium bro- mide as a surface modifier. The silica-coated both samples were calcined at high temperatures (300, 700 and 1000°C) and characterized by scanning electron microscopy, CIE L*a*b* color parameter measurements, transmission electron microscopy and UV-vis spectroscopy. The yellow α-FeOOH and β-FeOOH was transformed to α-Fe2O3 with red, brown at 300, 700°C, respectively.

The phase Ti-Nb-Sn-HA bio materials were successfully fabricated by high energy mechanical milling and pulse current activated sintering (PCAS). Ti-6Al-4V ELI alloy has been widely used as biomaterial. But the Al has been inducing Alzheimer disease and V is classified as toxic element. In this study, ultra fine sized Ti-Nb-Sn-HA powder was produced by high energy mechanical milling machine. The phase Ti-Nb-Sn-HA powders were obtained after 12hr milling from phase. And ultra fine grain sized Ti-Nb-Sn-HA composites could be fabricated using PCAS without grain growth. After sintering, the microstructures and phase-transformation of Ti-Nb-Sn-HA biomaterials were analyzed by scanning electron microscope (SEM) and X-ray diffraction (XRD). The relative density was obtained by Archimedes principle and the hardness was measured by Vickers hardness tester. The -Ti phase was obtained after 12h milling. As result of hardness and relative density, 12h milled Ti-Nb-Sn-HA composite has the highest values.

We analyzed the high resolution H,6 line spectra of CH Cygni obtained at the Bohyunsan Astronomical Observatory (BOAO) on April 2004. The temporal changes in the Hβ line profiles are reported. We obtained the equivalent widths of the Gaussian components. Using this we estimated the length of the gaseous nebula which emits the Hβ line and the mass loss rate from the star.

(Fe0.98Mn0.02)xSi2(x≤1) 조성으로, 용융법으로 제조한 α-Fe2Si5상의 잉곳을 730~850˚C에서 4~20시간 열처리하거나, 기계적 합금화로 제조한 ε-FeSi과 Si상으로 구성된 분말을 760~850˚C에서 10분간 가압통전소결하므로써 β-FeSi2기지상에 Si이 분산된 미세조직을 얻을 수 있었다. 조성, 열처리 온도와 소결 온도에 따라 Si 분상의 크기와 간격이 각기 0.05~0.27μm와 0.2~0.6μm 범위에서 변화하였다. 이와 같은 Si 분산상에 의해 β-FeSi2의 격자 열전도도가 감소되어 성능지수가 향상될 수 있을 것으로 기대된다.