PURPOSES : The process of extracting and recovering an asphalt binder from an asphalt mixture is harmful to the human body and can affect the properties of the asphalt binder owing to the presence of residual solvent quantities. This study was conducted to determine the properties of aged asphalt binders based on rejuvenator content without extracting and recovering the asphalt binders using RAP mortar. METHODS : After extracting and recovering aged binders from waste asphalt, a rejuvenator was added at a certain rate to evaluate the physical and rheological properties of the binder based on the added amount. RESULTS : When the rejuvenator content was greater than necessary, the absolute viscosity was not properly measured owing to the behavior of the rejuvenator. The phase angle was measured to be almost 90°, thus indicating that it acted as a liquid . In addition, the shear strain and nonrecovery compliance also increased significantly. CONCLUSIONS : If an excess rejuvenator quantity was added to the aged binder, the absolute viscosity was not properly measured, the phase angle was measured to be almost 90°, and the shear strain increased significantly. It is also necessary to conduct the same tests on different types of RAPs to ensure that the results of this study are reasonable.

본 연구에서는 기존 상용 SCR 촉매보다 비표면적, 경량성 및 온도 응답성이 우수한 SCR 촉매의 개발을 목적으로 바나듐과 텅스텐의 함량과 바인더의 첨가량을 달리하여 Metal foam 형태의 지지체에 코팅하여 SCR 촉매를 제조한 후, 실험실 규모의 마이크로 상압반응기상에서 공간속도별로 NOx 저감 성능을 측정하였다. 촉매의 특성은 Porosimeter, SEM(scanning electron microscope), EDX(energy dispersive x-ray spectrometer) 및 ICP(inductively coupled plasma), 실체현미경(Stereomicroscope) 기기를 이용하여 분석하였다. 연구 결과 NOx 저감 성능은 공간속도가 증가할수록 감소하였고, 바나듐과 텅스텐의 함량이 3.5 wt.% 일 때 가장 우수한 것으로 확인하였다. 또한, 바인더 첨가량이 많을수록 NOx 저감 성능이 감소하는 것으로 나타났는데, 이는 촉매 표면상의 활성점수가 바인더에 의해 점유되어 감소된 것에 따른 것으로 판단된다. 또한 표면 코팅 상태 분석을 통하여 바인더의 첨가량이 적절히 조절 되어야 함을 알 수 있었다.

Fe foam with above 90% porosity and 2 millimeter pore size was successfully fabricated by a slurry coating process. In this study, the binder contents were controlled to produce the Fe foam with different pore size, strut thickness and porosity. Firstly, the slurry was prepared by uniform mixing with Fe powders, distilled water and polyvinyl alcohol(PVA) as initial materials. After slurry coating on the polyurethane(PU) foam the sample was dried at 80oC. The PVA and PU foams were then removed by heating at 700oC for 3 hours. The debinded samples were subsequently sintered at 1250oC with holding time of 3 hours under hydrogen atmosphere. The three dimensional geometries of the obtained Fe foams with open cell structure were investigated using X-ray micro CT(computed tomography) as well as the pore morphology, size and phase.

실리카 바인더 함량이 지르콘 쉘 주형의 기계적 특성에 미치는 영향을 고찰하였다. 실리카 졸/지르콘 함량비 Rw는 0.18~0.43 범위에서 변화시켰으며, 주형의 소결온도는 871˚C~1400˚C 범위에서 변화시켰다. 생형의 상온강도는 실리카 졸/지르콘 함량비 Rw에 비례하여 증가하였다. 소결온도가 1300˚C 이하인 경우, Rw가 증가함에 따라 소결된 주형의 상온강도와 치밀화는 증가하였다. 그러나 Rw가 0.43이고 1400˚C에서 3시간 동안 소결시킨 경우 주형의 상온강도와 치밀화가 오히려 감소하였다. 이는 소결 중 내화물 입자와 실리카 바인더와 열팽창계수의 차이에 기인하는 것으로 판단된다. 정밀주조용 지르콘 쉘 주형 제작을 의한 최적의 Rw 값은 0.33인 것으로 나타났다.