A cold roll-bonding process is applied to fabricate an AA6061/AA5052/AA6061/AA5052 layered sheet. Two AA6061 and one AA5052 sheets of 2mm thickness, 40mm width and 300mm length are alternately stacked, then reduced to a thickness of 2.0 mm by multi-pass cold rolling after surface treatment such as degreasing and wire brushing. The rolling is performed at ambient temperature without lubricant using a 2-high mill with a roll diameter of 400 mm at a rolling speed of 6.0 m/sec. The roll-bonded AA6061/AA5052/AA6061/AA5052 layered sheet is then hardened by natural aging (T4) and artificial aging (T6) treatments. The microstructure of the as-roll bonded and the age-hardened Al sheets was revealed by SEM observation; the mechanical properties were investigated by tensile testing and hardness testing. After T4 and T6 aging treatment, the specimens had a recrystallization structure consisting of coarse equiaxed grains in both AA5052 and AA6061 regions. The as-roll-bonded specimen showed a clad structure in which the hardness of AA5052 regions was higher than that of AA6061 regions. However, after T4 and T6 aging treatment, specimens exhibited different structures, with hardness of AA6061 regions higher than that of AA5052 regions. Strengths of T6 and T4 age-treated specimens were found to increase by 1.55 and 1.36 times, respectively, compared to the value of the starting material.

알루미늄합금 6061-T6 판재에 대하여 마찰교반용접과 텅스텐 이너트 가스 용접의 교차 용접부의 미세조직과 기계적 특성에 있어서 용접 순서의 영향을 분석하기 위한 시험편을 성공적으로 제작하였다. FSW-ED 시험편이 다른 조합들보다 가장 좋은 기계적 특성을 나타내었다. 흥미롭게도, TIG-FSW ED 시험편이 FSW-TIG ED 시험편보다 높은 인장강도를 나타내었다. 용접부 경도의 경우, FSW 시편이 TIG-FSW 및 FSW-TIG 시험편보다 높은 값을 나타내었고, TIG-FSW 시험편이 FSW-TIG 시험편보다 높은 값을 나타내었다. FE-SEM을 이용한 인장 파면에 대한 관찰을 통하여, 모든 시험편에서 연성파괴를 나타내는 다양한 크기의 딤플들이 관찰되었다. FSW-TIG 시험편의 파면에서는 용융지(熔融池) 표면 영역에서 기공들이 관찰되는 반면, TIG-FSW 시험편에서는 기공의 형성은 관찰되지 않았다. 경도와 미세조직의 결과를 통해 TIG-FSW 공정이 FSW-TIG 공정보다 높은 인장강도를 확보할 수 있는 공정임을 확인하였다.

An aluminium sandwich sheet is the composite adhered by rolling two aluminum panels to one plastic core. If it has the same bending stiffness as an steel sheets, it is about 65% lighter than steel sheet and 30% lighter than aluminum sheet. In present study, we intend to develop application technologies of an aluminum sandwich sheet for auto body panels from selecting composed materials of aluminium sandwich sheets to fabricating prototype. For this study, for the application of a light sandwich sheet to an automotive hood part, ribbing process so called, hemming for which joined between an inner and an outer panel was introduced. From these results, it was found that the sandwich sheet could improve the weight and maintain the flexural rigidity simultaneously comparing to the steel sheet.

To fabricate the 5182 aluminum-polymer sandwich panels, the strength of 5182 aluminum panels, which are the skin sheets that constitutes the sandwich composite panels, is changed according to the degree of heat treatment after rolling, and the characteristics of sandwich panel are also changed. In addition, in the stress-strain curves of the sandwich panel, the serration behavior observed in the 5182 aluminum alloy sheet is also observed. This serration behavior causes surface roughness during sheet forming, which is a serious problem in application to automotive body sheet. In this study, the tensile properties of the 5182 aluminum sandwich panels at room and elevated temperature were carefully investigated by tensile test. It can be found that when the aluminum surface sheets having insufficient heat treatment time is applied, the serration behavior does not completely disappear from the temperature of the room temperature to 160℃.

The objective of this study was to develop formability evaluation techniques in order to apply aluminum sandwich panel for automotive body parts. For this purpose, formability evaluation by using FLD (forming limit diagram) was carried out in order to secure the fundamental data for the measurement of sheet metal forming and the establishment of optimum forming conditions of the aluminum sandwich panel. From the results of these formability evaluation, the formability of aluminum alloy sheet which was the skin component for the sandwich panel was higher than that of sandwich panel. In addition, the formability of sandwich sheet which was made by present study was same as that of sandwich panel made by foreign country. Also, it was found that sandwich panel made in present study could have the excellent deep draw-ability when it was compared to the foreign made sandwich panel.

The microstructural evolution of AA1050/AA6061 complex aluminum alloy, which is fabricated using an accumulative roll-bonding (ARB) process, with the proceeding of ARB, was investigated by electron back scatter diffraction (EBSD) analysis. The specimen after one cycle exhibited a deformed structure in which the grains were elongated to the rolling direction for all regions in the thickness direction. With the proceeding of the ARB, the grain became finer; the average grain size of the as received material was 45μm; however, it became 6.3μm after one cycle, 1.5μm after three cycles, and 0.95μm after five cycles. The deviation of the grain size distribution of the ARB processed specimens decreased with increasing number of ARB cycles. The volume fraction of the high angle grain boundary also increased with the number of ARB cycles; it was 43.7% after one cycle, 62.7% after three cycles, and 65.6% after five cycles. On the other hand, the texture development was different depending on the regions and the materials. A shear texture component 001<110> mainly developed in the surface region, while the rolling texture components 011<211> and 112<111> developed in the other regions. The difference of the texture between AA1050 and AA6061 was most obvious in the surface region; 001<110> component mainly developed in AA1050 and 111<110> component in AA6061.

An ultrafine grained complex aluminum alloy was fabricated by an accumulative roll-bonding (ARB) process using dissimilar aluminum alloys of AA1050 and AA5052 and subsequently annealed. A two-layer stack ARB process was performed up to six cycles without lubricant at an ambient temperature. In the ARB process, the dissimilar aluminum alloys, AA1050 and AA5052, with the same dimensions were stacked on each other after surface treatment, rolled to the thickness reduction of 50%, and then cut in half length by a shearing machine. The same procedure was repeated up to six cycles. A sound complex aluminum alloy sheet was fabricated by the ARB process, and then subsequently annealed for 0.5h at various temperatures ranging from 100 to 350˚C. The tensile strength decreased largely with an increasing annealing temperature, especially at temperatures of 150 to 250˚C. However, above 250˚C it hardly decreased even when the annealing temperature was increased. On the other hand, the total elongation increased greatly above 250˚C. The hardness exhibited inhomogeneous distribution in the thickness direction of the specimens annealed at relatively low temperatures, however it had a homogeneous distribution in specimens annealed at high temperatures.