Friction welding, which uses heat and plastic flow to join metals, is expanding across industries due to its ability to weld heterogeneous alloys and simple process. However, process research is essential for materials with complex geometries, and limited research has been conducted on friction welding between cast and sintered metals. This study analyzed the mechanical properties and microstructural evolution of the joint by controlling the rotational speed and friction pressure, which affect the removal of the heat-affected zone in friction welding of casted SCM440 and sintered F-05-140. Hardness mapping and microstructure observations with material transition were performed to investigate the correlation between phase behavior and welding conditions. These results are anticipated to reduce costs and improve the mechanical properties of key mobility components.

This study is to investigate the improvement of quality and cost reduction of welding materials for combat vehicles through localization. The existing imported welding wires and localized welding wires were evaluated. The evaluation of the welding wires was performed for the feedability, chemical/mechanical properties, macro testing, and weldability. As a result of evaluation, the localized welding material met all the evaluation standard values. In addition, it showed excellent performance in terms of weldability and feedability. It is judged that the welding quality is improved thanks to the improvement of feeding characteristics through the localization of the welding material, and the fatigue of the worker is also expected to be relieved.

Natural gas is the most realistic fuel among eco-friendly fuels. Natural gas production is limited, and in Korea, it is supplied and utilized in the form of liquefied natural gas (LNG). In the case of LNG, the vaporization point is 163 degrees below zero, so ordinary metal cannot be used due to its brittleness. The International Maritime Organization (IMO) defines metals that can be used in the IGC Code, and is used for storage containers, transportation containers, etc. based on the metals. Welding is essential in the manufacture of large structures such as LNG storage tanks. In this study, weldability studies related to cryogenic materials were conducted. In Part I of this study, high-manganese steel and part II were studied for two types of stainless steel (STS304L, STS316L), and in Part III, aluminum (AL5083). During laser welding, the shape of the Bead on Plate (BOP) was analyzed, and a total of nine cases were analyzed using laser power and welding speed as variables. It was confirmed that the penetration and the width of the welding width were linearly proportional to the amount of heat input. Based on this study, it is possible to conduct a follow-up study to find the optimal welding conditions for butt welding and fillet welding.

As the part of efforts to respond to the environmental pollution, the demand for clean energy is increasing. Natural gas is one of the most realistic alternatives, and interest in the storage and transportation containers to utilize the natural gas is growing. The production area of ​​natural gas is limited, and in Korea, it is imported in the form of liquefied natural gas. LNG is a cryogenic state with a vaporization point of -163°C, so the ordinary metal cannot be used due to its brittleness. The international maritime organization (IMO) defines the metals that can handle LNG in the IGC Code, and the research is ongoing. This study was a preliminary study to check the weldability of related metals and confirmed the shape of bead on plate (BOP) during the laser welding for each material. In part I, a study was conducted on the high manganese steel, and in part II, a study was conducted on the materials of STS304L and STS316L among the stainless steel. Based on this study, it can be used as an optimal welding condition for the butt and fillet welding.

As demand for eco-friendly energy increases, demand for natural gas and Liquefied natural gas (LNG) storage technologies continues to increase. LNG is a cryogenic environment with a temperature of -163°C, so ordinary metals cannot be used due to brittleness. Accordingly, IGC Code designates the cryogenic materials such as Invar, STS304L, Al5083-0, and High Manganese Steel. For fabricating those materials, research on welding possibility is the most important. Thus this study focused on the possibility of laser welding of the cryogenic materials. The weldability of High Manganese Steel was researched in this paper, the shape and the dimensions of the beads after bead on plate (BOP) welding were observed. The experiment was conducted on a total of 25 cases with laser power and welding speed of 5 cases each, and the width, height, and penetration of the beads were confirmed. It was confirmed that the paramenter of bead increased linearly with the laser power, and the paramenters of bead increased linearly with decreasing welding speed. Based on this study, high manganese steel can be applied in various industries by applying it to butt welding.

Recently, applied areas of nonferrous materials have been expanded in terms of efficiency of materials used and cost reduction. And, in accordance with compactness and accuracy of parts, the need of joining of dissimilar materials is raised. Accordingly, this study aimed at finding out the optimal welding current value(6.3～6.5kA) considering tensile strength, fracture test and welding residue after joining with various welding conditions by means of copper pipe(Φ7.0 × t0.5) and aluminium pipe(Φ7.0 × t0.7) using an eutectic diffusion bonding machine.

Friction welding of particulate reinforced aluminum composites was performed and the following conclusions were drawn from the study of interfacial bonding characteristics and the relationship between experimental parameters of friction welding and interfacial bond strength. Highest bonded joint efficiency (HBJE) approaching was obtained from the post-brake timing, indicating that the bonding strength of the joint is close to that of the base material. For the pre-brake timing, HBJE was . Most region of the bonded interface obtained from post-brake timing exhibited similar microstructure with the matrix or with very thin, fine-grained layer. This was attributed to the fact that the fine-grained layer forming at the bonding interface was drawn out circumferentially in this process. Joint efficiency of post-brake timing was always higher than that of pre-brake timing regardless of rotation speed employed. In order to guarantee the performance of friction welded joint similar to the efficiency of matrix, it is necessary to push out the fine-grained layer forming at the bonding interface circumferentially. As a result, microstructure of the bonded joint similar to that of the matrix with very thin, fine-grained layer can be obtained.

개조한 가스 금속 아아크 용접공정을 이용하여 SiC/AI 금속기 복합재료를 제조하고 그 특성을 조사하였다. AI 모재위에 강화입자의 크기와 부피분율을 변화하여 다양한 SiC/AI 복합재료층을 제조하였고, 만들어진 복합재료층의 특성은 미세조직관찰과 미소경도시험을 통하여 이루어졌다. 복합재료층의 두께는 약 7-8mm로 측정되었고 균일한 강화입자의 분포도를 얻을 수 있었다. 분산입자의 부피분률은 Ar가스의 유량에 의하여 조절하였고 분산입자의 부피분률이 증가하고 크기가 작아짐에 따라 기지의 수지상 응고조직은 더욱 미세화되었다. 복합재료의 부피경도는 분산입자의 부피분률이 감소함에 따라 낮아졌으나 입자 크기에는 크게 변화가 없는 것으로 나타났다.