SUS hexagonal bar have been widely used to manufacture the hexagonal bolt/nut, adapter and fittings. Raw SUS circular bar is used to make SUS hexagonal bar using drawing system. The purpose of this study is to investigate the characteristics, for instance, such as stress, strain and reduction ratio of area for bar. As the results, it was confirmed that the maximum stresses were occurred at edge of hexagonal bar, thus it could be worked as residual stress of hexagonal bar. The phenomenon of spring back was almost no found in all parts of hexagonal bar. Furthermore it showed that the reduction ratios of area were about mean 26% when SUS circular bar was changed to SUS hexagonal bar in this study.

In order to remove rust and impurities from surface of raw SUS circular bar, peeling machine is used to make lustrous and clean surface of SUS circular bar. Drawing process system is used to manufacture SUS hexagonal bar. SUS hexagonal bar have been widely used to make hexagonal bolt/nut, adapter and fittings and so on. The purpose of this study is to investigate the stabilities for guide bar of clamp in drawing process system. As the results, the guide bar showed structural stability in cases of below load of 50 Ton and over hook radius of 3.0mm. Further as the thickness of guide bar hooking with jaw was increased, minimum safety factor was decreased.

SUS hexagonal bar has been widely used to make many kinds of hexagonal bolt/nuts and fittings. Peeling machine is used to make lustrous and clean surface of SUS circular bar in order to remove rust and impurities from surface of raw SUS circular bar. Similarly, roll unit system is used to make SUS hexagonal bar from SUS circular bar with lustrous and clean surface. Roll unit system is mainly divided into two parts ; one is roll unit and the other is mold frame. The purpose of this study was to evaluate the structural stability of mold frame supporting roll unit with numerical analysis. As the numerical analysis result, higher structural stability was gradually shown in order of models 4, 2, 3 and 1. It was considered that the structural stability of this study was influenced by the decrease of mold frame size, especially height decrease.

SUS hexagonal bar, which is manufactured by drawing process of SUS circular bar, have been widely used to make various adapters and fittings. The purpose of this study is to investigate the characteristics and stability of variable roll unit including stand module. Stand module is essential part of variable roll unit. Structural analysis was performed to predict the stability of stand module using 3 loads (50, 75, 100 Ton), thus it may be of help to the manufacture of stand module. As the results, internal ring of bearing showed maximum equivalent stress, and moreover bearing, shaft and roller had to be preferentially considered in order to maintain its stability. In cases of 50 and 75 Ton, there were no problems for stabilities, respectively, on the other hand, problem for stability may occur in case of 100 Ton.

It has been more than twenty years since the application of GFRP bridge decks in construction fields. Recently, a few studies by governments and individual researchers have investigated in-use GFRP bridge decks. Areas of trouble include the problems of cracking, spalling and the de-bonding of the pavement or the wearing surface on GFRP bridge decks, all of which affect the long-term durability and serviceability of these new construction materials. Related to these problems, reflective cracks on asphalt pavement are directly related to pultruded GFRP bridge decks. This study investigates the behavior of an adhesive joint under weak-axis bending by tests and FE analyses to identify the causes of pavement cracks in in-use pultruded GFRP bridge decks. In detail, the flexural stiffness and the load-carrying capacities in strong and weak axes are measured during bending tests on pultruded GFRP decks. Next, tensile local failures of an epoxy adhesive due to the concentration of deformations at adhesive joints are identified via a weak-axis bending test. Finally, the tensile failure of an epoxy adhesive due to the local concentration of deformation at an adhesive joint under weak-axis bending is verified through a finite element analysis.

복합재료(FRP)는 재료적 고비강도, 고내구성 등으로 인하여 건설분야에 널리 사용되고 있어, 본 연구에서는 인발성형된 FRP 바닥판의 형상최적설계를 수행하였다. 최적설계의 정식화에서 목적함수는 단위모듈의 체적을 최소화하도록 하였으며, 설계변수는 바닥판 단면의 기하적 치수와 재료적 물성을 사용하였다. 반면 바닥판의 성능을 최대한 효율적으로 설계하기 위하여 설계 제약조건으로 처짐규정, 재료파괴 기준, 좌굴하중, 바닥판 최소두께와 응력을 사용하였다. 단면형상의 효율적 결정과 시공성을 고려하여 구조적 보조부재를 포함하지 않는 튜브 모양의 형상으로 제한하였으며, 최적화 알고리즘은 Index기법을 적용하여 수렴성을 극대화한 개선된 GAs를 사용하였다. 상용 프로그램인 ABAQUS를 사용하여 3차원 유한요소해석을 수행하였고, 구조해석 결과를 최적화 과정에 필요한 제약조건으로 활용하고, 민감도 분석을 수행하였다. 본 연구를 통하여 개발한 최적화 프로그램을 검증하기 위하여, 40m의 지간, 폭 12.14m에 주형 간격이 2.5m인 단순교를 대상으로 하였으며, 도로교 설계 기준을 만족하는 DB-24하중을 적용하였다. 복합재료의 재료로 E-glass섬유를 사용하였으며, 최적설계를 수행한 결과 인발성형공법에 의한 실용적인 단면을 제안하였다.