PURPOSES : The objective of this study is to evaluate the mechanical characteristics of castor oil based bio-polymer concrete for use of ultra thin overlays. METHODS : To evaluate the mechanical properties of bio-polymer concrete, the various laboratory tests including compressive, tensile, and flexural strength, and elongation tests were conducted on bio-polymer concrete specimens in this study. The mechanical characteristics of bio-polymer concretes were examined by changing the content of hardener and polymer binder to determine the optimum content for ultra-thin overlays. The bio-polymer concrete developed in this study was used for field trial test of the ultra-thin bridge deck pavement for verifying the workability and monitoring the long-term performance of materials. RESULTS : Test results showed that tensile and the flexural strength of bio-polymer concretes increase and the elongation of bio-polymer concrete decreases with increase of binder content. A field adhesive strength tests conducted on bridge deck pavement indicates the bio-polymer concrete has more than 2MPa of adhesive strength satisfy with the design criteria. CONCLUSIONS : The bio-polymer concrete with more than 20% content of castor oil was developed for ultra-thin overlays in this study. It is found from this study that the 35% of hardener content is most appropriate for maintaining the strength characteristics and flexibility.

농촌진흥청 국립농업유전자원센타로부터 국내외에서 수집되어진 피마자 40종을 분양받아 바이오디젤 가능 작물로서 생육 특성을 조사한 바 그 결과는 다음과 같다. 피마자 수집종의 출아소요일수는 15~16일에 82.5%가 출현하였으며, 출현에서 개화까지의 소요일수는 63~68일이었다. 경장의 분포는 전체 평균이 211.8 cm로 173~251 cm의 변이폭을 보였으며, 줄기 굵기는 평균 24.2 mm로 20.4~24.9 mm가 52.5%로 가장 많이 분포하였다. 절수는 평균 18.9개 였으며 그 범위는 13~22개로 넓게 분포하였다. 삭수는 주당 7~33개로 폭 넓게 분포하였으며, 종실 1l 무게는 평균 502.9 g으로 최소 432.3 g, 최대 572.5 g로 140.2 g의 큰 차이가 있었다. 100립중은 최소 20.3 g에서 최대 38.3 g으로 소립종과 대립종 간 18.0 g의 많은 차이를 보였다. 주당 종 실수는 최소 72개에서 최대 1,011개로 큰 차이를 보였으며, 평균 465.2개이었다. 주당 종실수량은 평균 128.1 g이었으며, 최저 20 g, 최고 266.2 g으로서 다양하게 분포하였다.