This study was conducted to compare the mechanical properties of NAB (Ni-Al-Bronze) material manufactured using WAAM (wire arc additive manufacturing) technology and cast NAB that has been used. Two types of mechanical property test pieces were collected from the deposited bulk NAB material according to the direction of deposition, and compared with each other. As a result of mechanical property evaluation, the deposited NAB exhibited anisotropy according to the direction of deposition, and showed high tensile strength, hardness, and shock absorption in the longitudinal direction of the welding line.

In order to accelerate the sintering of Al-Bronze powder covered with passive oxide film, we focused on the way to add Al-Ca fluoride consisting of and , examined the effect of the mixing rate in Al-Ca fluoride, the amount of the added Al-Ca fluoride and the sintering temperature on sintering properties of Al-Bronze powder and considered the mechanism of the sintering acceleration. Al-Bronze powder was sintered most effectively by adding Al-Ca fluoride with the mixing rate of 20mass%. If the amount of added fluoride was over 0.05mass% and the sintering temperature was over 1123K, the sintering acceleration of the Al-Bronze powder appears. Regarding the mechanism of the sintering acceleration, it was presumed that film on the surface of the Al-Bronze particles was removed in the process of the formation of gaseous AlOF by the reaction with , and the reaction was accelerated further by the presence of the liquid phase which is formed in Al-Ca fluoride.