        검색결과 5

        3.
        2000.03 KCI 등재 구독 인증기관 무료, 개인회원 유료
        Al2O3SiC particle was prepared was prepared by the self-propagting high temperature sYthesis(SHS) process from a mixture of SiO2, Al and C powders, The fabricated Al2O3SiC particle was applied to 2024Al/(Al2O3SiC)pcomposite as a reinforcement. Aluminum matix composites were fabricares by the powder extrusion method using the synthesized Al2O3SiC particle and commercial 2024Al powder. Theoptimum preparation conditions for Al2O3SiC partticle by SHS process were described. The influence of the Al2O3SiC voiume fraction on the mechanical was composite was also discussed. Despite adiabatic temperature was about 2367K, SHs reaction was completed not by itself, but by using pre-heating. Mean particle size of final particle synthesized was 0.73 m and most of the particle was smaller than 2m. Elastic modulus and tensile strength of the composite increased with increase the volume fraction of reinforcement but, tensile strength depreciated at 30 vol% of reinforcement.
        4,000원
        4.
        1999.08 KCI 등재 SCOPUS 구독 인증기관 무료, 개인회원 유료
        Al2O3-SiC 화합물 분말이 SiO2, A1 그리고 C 분말들을 원료분말로 하여 SHS(self-propagating High-temperature Synthesis)법에 의해 제조되었다. 원료 분말에서의 몰비, 성형압력, 반응물의 초기온도의 영향이 생성물과 연소과정에 대해 연구되었다. SiO2/A1/C계의 자전연소합성은 낮은 연소온도 때문에 400˚C 이상으로 예열되어야 한다. 연소반응의 결과로서 최종생성물의 순도는 반응물의 순도보다 높았다. 이 계에서 SiO2:Al:C의 적당한 몰비는 3.0:4.0:6.0이었고, free carbon은 30min 동안 650˚C에서 배소함으로써 제거되었다. 본 연구에서 상압소결은 1700˚C에서 powder bed를 사용한 표본의 분해를 제어하고 치밀한 소결체를 얻는데 매우 효과적이었다. hot-pressing으로 생성된 소결체는 이론비교밀도의 약 98%이었다.
        4,000원
        5.
        1996.10 KCI 등재 SCOPUS 구독 인증기관·개인회원 무료
        알루미나 매트릭스 복합재료를 AIZnMg(7075)-합금의 직접적인 용융산화를 통하여 제조하였다. 충전재료는 17μm 크기의 모서리가 둥근 연마재용 SiC 입자를 사용하였다. 산화촉진재 SiO2를 사용한 경우와 사용하지 않은 경우를 비교하였다. 매트릭스 형성 매카니즘과 반응거동을 온도와 SiO2사용량을 중심으로 연구하였으며, 얻어진 AI2O3/SiC/금속 복합재료의 미세구조를 관찰하였다.