철근의 부식 문제를 해결하기 위해 최근 복합재료 기반의 철근이 개발되어 사용되고 있으며 CFRP 그리드도 개발되어 구조부재로 사용되기 시작하고 있다. 그러나 CFRP 그리드의 부착 특성과 응력을 연구한 경우는 매우 드물다. 이에 본 실험은 CFRP 그리드의 부착거동, 부착응력을 평가하고 정착길이를 산정하기 위해 다양한 길이의 정착길이를 가진 인발실험체를 제작한 후 인발하였으며 실험 결과 부착력의 경우 정착길이가 길어질수록 커지며 반대로 부착응력은 정착길이가 길어질수록 작아지는 결과를 얻을 수 있었다. 이는 FRP 보강근도 같은 경향을 보이지만 CFRP 그리드와 FRP 보강근의 차이점은 부착응력의 추세선의 경향에서 두드러지며 또한, 최대 부착력 이후 거동에서 차이를 나타냈다. 위 실험 결과를 토대로 CFRP 그리드의 정착길 이를 산정한 결과 본 연구에서 사용된 CFRP 그리드의 보수적인 정착길이는 250mm로 나타났다.
Bond stress between cast-in-place ductile fiber reinforced cementitious composites and CFRP plank were experimentally analyzed. As failure shape, the mixture of failure between CFRP plank and epoxy, and failure between concrete and epoxy was shown. In case of RFCON from the suggested simple bond slip relationship, the maximum average bond stress was 5.39MPa, the initial slope was 104.09MPa/mm, and the total slip length was 0.19mm. PPCON showed the maximum average bond stress of 4.31MPa, the initial slope of 126.67MPa/mm, and the total slip length of 0.26mm, while RFCON+ appeared to have 8.71MPa, 137.69MPa/mm, 0.16mm. PPCON+ had 6.19MPa maximum average bond stress, 121.56MPa/mm initial slope, and 0.34mm total slip length. To comprehend the behavior of composite structure of FRP and concrete, local bond slip relation is necessary, and thus a simple relation is suggested to be easily applied on hybrid composite system
건축물의 고층화, 대형화에 따라 기둥이 부담해야할 하중이 증대되고, 이로 인한 기둥단면적의 증대에 효율적으로 대처하기 위해 CFT(콘크리트 충전강관)기둥의 형식을 개발하게 되었다. CFT기둥은 이질재료로 구성된 복합구조형식으로, 역학적 거동을 규명하기 위해 많은 연구가 이루어지고 있다. 본 연구는 원형과 각형의 CFT기둥에 있어서 콘크리트 코어와 강관, 두 이질재료간의 접촉면 부착응력에 대한 해석적 연구로서 비선형 해석프로그램인 ABAQUS/Standard Version 5.8을 이용하여 shear-connector의 부착형태 및 위치에 따른 부착응력을 비교하고, 접촉면의 역학적 특성에 대한 개선된 해석기법을 제시하고자 한다.
건축물이 고층화, 대형화 되어감에 따라 기둥이 부담해야할 내구성이 커진다. 이런 요구로 인하여 콘크리트 충전강관기둥의 형식을 개발하게 되었고, 역학적 거동을 규명하기 위해 연구가 이루어지고 있다. 본 연구는 실험에서 규명하기 힘든 콘크리트코어와 원형강관의 두 이질재료간의 접촉면에서의 상호작용에 대한 해석적 연구로써 비선형 해석프로그램인 ABAQUS/Standard Version 5.8을 이용하여 쉬어코넥트의 부착형태 및 위치에 따른 부착응력을 비교하고, 접촉면에 대한 역학적 특성을 나타낼 수 있는 모델링기법, 해석기법에 대하여 제시하고, 역학적 특성을 규명하고자 한다.
This paper is presented an experimental studies on bond stress between steel and concrete in concrete filled Rectangular steel tubes. In the actual building frames, vertical dead and live loads on beams are usually transferred to columns by beam-to-column connections. In case when concrete filled steel tubes are used as columns of an actual building frame which has a simple connection, shear forces in the beam ends are not directly transferred to the concrete core but directly to the steel tube. Provided that the bond effect between steel tube and concrete core should not be expected, none of the end shear in the beams would be transferred to the concrete core but only to the steel tube. Therefore, it is important to investigate the bond strength between steel tube and concrete core in the absence of shear connectors.
An analytic study on the bond stress between steel tube and concrete in concrete filled steel(CFT) rectangular column is presented in this paper. Recently buildings need members which are enhanced durability and ductility. Concrete filled rectangular column system is proposed as alternative plan. In this paper, ABAQUS/Standard Version 5.8 which is identified as usefulness for finite element analysis and has various element library is used. The variables in this study are the location and type of shear-connector. The modeling on contact problem practiced by Contact Pair and Contact Pressure method. In the step of physical bond, it is practiced by Change friction option After yielding of models, analytic results is less than that of experimental results.
This paper is presented an experimental studies on bond stress between steel and concrete in concrete filled steel tubes. In the actual building frames, vertical dead and live loads on beams are usually transferred to columns by beam-to-column connections. In case when concrete filled steel tubes are used as columns of an actual building frame which has a simple connection, shear forces in the beam ends are not directly transferred to the concrete core but directly to the steel tube. Provided that the bond effect between steel tube and concrete core should not be expected, none of the end shear in the beams would be transferred to the concrete core but only to the steel tube. Therefore, it is important to investigate the bond strength between steel tube and concrete core in the absence of shear connectors.
In this paper, the bond stress of Fe based Shape Memory Alloy(Fe-SMA) with near surface mounted strengthening was investigated. An lab-shear test using Fe-SMA strips glued with cementitious matrix was performed to evaluate bond stress. Bond length (250 mm, 350 mm, 450 mm) was considered as experimental variable. The bond stress and utilization of Fe-SMA are 1.487MPa and 80%, respectively, at the bond length of 450 mm.
Because significant difference between normal concrete and fiber reinforced ultra-high strength concrete under tension and compression, bond behavior also have significant difference. Bond behavior may affect to the flexural behavior and shear behavior of reinforced concrete beams. Especially, because ultra high strength concrete usually be used as precast members, bond between concrete and steel rebar should be safely and accurately evaluated for design. In this study, bond test results about ultra high strength fiber reinforced concrete were investigated and evaluated with various types of prediction methods, especially for empirical equations.
최근 들어 FRP 판을 영구 거푸집 및 주요 인장보강재로 활용하기 위한 새로운 콘크리트 교량 바닥판 시스템 개발에 대한 연구가 활발히 진행되고 있다. 영구거푸집과 인장 보강재로의 병행이용은 기존의 콘크리트 바닥판 보다 공사비와 공사기간을 절감 할 수 있다. 본연구에서 는 영구거푸집 및 주요인장재로 활용한 FRP 판의 종류에 따른 현장타설 콘크리트와 부착응력에 대해 실험을 수행하였다. 부착성능 평가를 실시하였고, 부착특성을 나타내는 중요한 변수중에 하나로서 부착 강도 및 부착면의 파괴 매커니즘 특성을 알 수 있는 계면 파괴에너지를 나타내었다. 일반콘크리트에서 계면 파괴에너지는 GF11의 경우 0.24kN/m이고, GF21의 경우에는 0.43kN/m, GF31과 CF11의 경우에는 각각 0.46kN/m와 0.44kN/m로 나타났고, RFCON에서는 GF12의 경우 0.52kN/m, GF22와 CF12에서는 각각 0.36kN/m와 0.51kN/m로 나타났다.
FRP has higher design tensile strength than steel bar and outstanding characteristics such as light-weight, non-corrosion, and lower conductivity. And, current researchers evaluated flexural performances of flexural members using FRP and suggested the development length and splice length by using bonding failure test. This Researchers has the main purpose to examine the quality of bonding failure in the lap spliced FRP and deformed bar. Variables in this test with total 208 specimens planned are re-bar location, embedment length, covering depth, re-bar diameter. And, this study describes the result of our review on the bonding strength of the lap-spliced FRP and the deformed bar located at the bottom.
최근 지진, 노후화 등에 따라 손상된 많은 콘크리트 구조물을 보강하기 위하여 고강도이면서 가볍고 내구성이 뛰어난 특성을 가지고 있는 FRP(Fiber-reinforced polymer) 시트가 구미에서 뿐만 아니라 우리나라에서도 널리 사용되고 있으며 관련연구도 활발히 체계적으로 이루어지고 있다. 일반적으로 FRP 시트로 보강된 RC구조물은 지진, 교통, 온도 등에 의해 자주 반복하중을 받는다. 그러나 대부분의 연구가 일축 하중하에 이루어진 경우가 대부분이며 이러한 연구결과를 토대로 FRP의 부착특성을 확인하고 있으며 다양한 부착모델을 제안하고 있다. 이러한 관점에서 본 연구에서는 아라미드섬유, 탄소섬유, 폴리아세탈 섬유와 매수를 변수로 하여 총 18개의 시험체를 제작하고 최대부착강도, 최대변위, 변형률을 측정하고 그 결과에 근거하여 부착응력, 슬립을 계산하여 반복하중하의 FRP 시트와 콘크리트의 부착특성을 미시적으로 살펴보았다.
최근에 상용 FRP 판(plank)을 콘크리트 구조물의 영구 거푸집 및 보강재로 이용하기 위한 연구가 진행되고 있다. FRP 판과 타설 콘크리트가 합성효과를 발휘하기 위해서는 두 재료간의 부착이 중요한 요인 중의 하나이다. 이러한 부착을 확보하기 위하여 FRP 판에 모래를 일반적으로 건설현장에서 많이 사용하는 에폭시를 이용하여 부착하였다. FRP 판과 콘크리트 합성구조의 구조적 거동을 이해하기 위해서는 FRP판과 타설 콘크리트 사이의 정량적인 국부 부착모델이 필요하다. 본 연구에서는 이와 같은 합성구조 시스템에 간단히 적용할 수 있는 단순 부착모델을 제안한다.