In this study, soybean oil, which is used in a large variety of processed foods, is used as a carbon source. Soybean oil is successfully coated onto the surface of LiNi1/ 3Co1/3Mn1/3O2 (NCM) by a simple method. The physical and electrochemical properties of NCM/C hybrid materials are determined. As a result, a 5 nm thickness carbon coating layer is formed on the surface of the NCM, resulting in improved capability and cyclic performance in the battery. The NCM/C battery shows an initial discharge capacity of 159 mAh g−1 and 95% capacity retention after 100 cycles (a discharge capacity of 120 mAh g−1 and 94% retention are observed after 100 cycles for the NCM cathode).

2019년에 서남해안 지역인 고창군의 옥수수 밭 주변에서 성페로몬을 이용하여 열대거세미나방(Spodoptera frugiperda) 성충을 효과적으로 모니터 링하는 방법을 조사하였다. 총 함량이 300 또는 1000 ㎍인 2종류 성분 조성의 성페로몬 미끼[(100%) (Z)-9-tetradecenyl acetate and (2%) (Z)-7-dodecenyl acetate]를 설치한 깔대기형 트랩과 델타형 트랩 중에서 열대거세미나방은 300 ㎍ 미끼의 깔대기형 트랩에서 8월 6일에 처음 잡혔고 가장 많이 포획되었다. 또한 깔대기형 트랩 모두에서 비표적 종인 뒷흰가는줄무늬밤나방(Mythimna loreyi)이 많이 포획되었다. 총 함량이 1000 ㎍인 위의 2종류 성분 조성과 4종류 성분 조성의 미끼[(100%) (Z)-9-tetradecenyl acetate, (8%) (Z)-11-hexadecenyl acetate, (2%) (Z)-7-dodecenyl acetate, and (1%) (Z)-9-dodecenyl acetate]를 설치한 날개형 트랩에서 열대거세미나방은 비슷한 수준의 낮은 포획수를 보였으나 뒷흰가는줄무늬밤나방은 4종류 성분 조성의 미끼에서 훨씬 더 많이 포획되었다. 성페로몬 트랩에 포획된 열대거세미나방 70마리의 미토콘드리아 시토크롬 옥시다제 1(CO1)의 부분 염기서열(1,004 bp)을 이용하여 계통수를 분석한 결과, 두 개의 종내 변이군으로 나눠졌으며 66마리가 CO1-RS로, 나머지 4마리는 CO1-CS로 분지되었다. 또한 두 개의 CO1 변이군과 기주식물계통(벼, 옥수수)에서 일관되게 차이가 있는 총 12개의 CO1 단일염기다형성(SNP)이 확인되었으며, 전체 73마리 중 4마리만 CO1-CS 그룹(옥수수계통 포함)과 동일한 패턴을 보였으며 나머지 69마리는 CO1-RS그룹(벼계통 포함)과 같았다.

Ni1/3Co1/3Mn1/3(OH)2 powders have been synthesized in a continuously stirred tank reactor via a co-precipitation reaction between aqueous metal sulfates and NaOH using NH4OH as a chelating agent. The co-precipitation temperature is varied in the range of 30-80oC. Calcination of the prepared precursors with Li2CO3 for 8 h at 1000oC in air results in Li Ni1/3Co1/3Mn1/3O2 powders. Two kinds of obtained powders have been characterized by X-ray diffraction (XRD), scanning electron microscopy, particle size analyzer, and tap density measurements. The co-precipitation temperature does not differentiate the XRD patterns of precursors as well as their final powders. Precursor powders are spherical and dense, consisting of numerous acicular or flaky primary particles. The precursors obtained at 70 and 80oC possess bigger primary particles having more irregular shapes than those at lower temperatures. This is related to the lower tap density measured for the former. The final powders show a similar tendency in terms of primary particle shape and tap density. Electrochemical characterization shows that the initial charge/discharge capacities and cycle life of final powders from the precursors obtained at 70 and 80oC are inferior to those at 50oC. It is concluded that the optimum co-precipitation temperature is around 50oC.

As precursors of cathode materials for lithium ion batteries, Ni1/3Co1/3Mn1/3(OH)2 powders are prepared in a continuously stirred tank reactor via a co-precipitation reaction between aqueous metal sulfates and NaOH in the presence of NH4OH in air or nitrogen ambient. Calcination of the precursors with Li2CO3 for 8 h at 1,000°C in air produces dense spherical cathode materials. The precursors and final powders are characterized by X-ray diffraction (XRD), scanning electron microscopy, particle size analysis, tap density measurement, and thermal gravimetric analysis. The precursor powders obtained in air or nitrogen ambient show XRD patterns identified as Ni1/3Co1/3Mn1/3(OH)2. Regardless of the atmosphere, the final powders exhibit the XRD patterns of LiNi1/3Co1/3Mn1/3O2 (NCM). The precursor powders obtained in air have larger particle size and lower tap density than those obtained in nitrogen ambient. NCM powders show similar tendencies in terms of particle size and tap density. Electrochemical characterization is performed after fabricating a coin cell using NCM as the cathode and Li metal as the anode. The NCM powders from the precursors obtained in air and those from the precursors obtained in nitrogen have similar initial charge/discharge capacities and cycle life. In conclusion, the powders co-precipitated in air can be utilized as precursor materials, replacing those synthesized in the presence of nitrogen injection, which is the usual industrial practice.

김해를 비롯한 전국 11개 지역에서 미국선녀벌레를 채집하여 미토콘드리아의 Cytochrome Oxidase I 유전자를 분리, 염기서열을 조사하였으며, 이들을 NCBI에 기록 보관된 지역별 미국선녀벌레의 염기서열과 비교, 분석하였다. 분석 결과, 우 리나라의 미국선녀벌레 유전자 타입은 크게 3가지로 분류되며 이들의 유전적 거리 는 매우 가까운 것으로 밝혀졌다. 이 결과를 바탕으로 침입 경로를 유추하면 약 2번 에 걸쳐 우리나라에 침입한 것으로 추정된다. 원산지는 플로리다로 추정되며, 이들 이 프랑스와 북아메리카 전체로 퍼지며, 프랑스에 유입된 미국선녀벌레가 슬로베 니아와 스페인으로 전파된 것으로 생각된다. 우리나라는 첫째로 김해로 침입한 계 통은 미국으로부터 오래전에 들어와 있던 것으로 생각되며, 두 번째는 최근 스페인 과 슬로베니아로부터 침입하여 중부지방 전역에 급격히 전파된 것으로 사료된다.

아메리카동애등에 (Hermetia illucens)와 동애등에 (Ptecticus tenebriefer)는 파 리목 동애등에과 (Family Stratiomyidae)에 속하는 곤충이다. 두종의 유충은 유기 물의 분해에 탁월한 능력을 가지고 있어서 환경 곤충으로 많은 주목을 받고 있다. 이 두 종의 미토콘드리아 CO1유전자의 haplotype의 다양성을 비교한 결과 도입 종인 아메리카동애등에의 haplotype은 10개로 매우 낮은 반면, 동애등에의 haplotype은 약 30개로 매우 높았다. 이러한 이유는 아메리카동애등에는 미국 원산으로 1990년대 말에 한국에서 도 입되었으며, 도입 과정 중 유전적 병목현상 (genetic bottleneck)을 겪은 것으로 생 각된다. 반면 동애등에는 국내 토착종으로서 국내 생태조건에 적응하여 진화한 결과로 외국에서 유입된 종 보다 매우 다양한 haplotype을 가지고 있는 것으로 생각된다.