Chromium nitride (CrN) samples with two different layer structures (multilayer and single layer) were coated on bipolar plates of polymer electrolyte membrane fuel cells (PEMFC) using the reactive sputtering method. The effects with respect to layer structure on corrosion resistance and overall cell performance were investigated. A continuous and thin chromium nitride layer (Cr0.48 N0.52) was formed on the surface of the SUS 316L when the nitrogen flow rate was 10 sccm. The electrochemical stability of the coated layers was examined using the potentiodynamic and potentiostatic methods in the simulated corrosive circumstances of the PEMFC under 80˚C. Interfacial contact resistance (ICR) between the CrN coated sample and the gas diffusion layer was measured by using Wang's method. A single cell performance test was also conducted. The test results showed that CrN coated SUS316L with multilayer structure had excellent corrosion resistance compared to single layer structures and single cell performance results with 25 cm2 in effective area also showed the same tendency. The difference of the electrochemical properties between the single and multilayer samples was attributed to the Cr interlayer layer, which improved the corrosion resistance. Because the coating layer was damaged by pinholes, the Cr layer prevented the penetration of corrosive media into the substrate. Therefore, the CrN with a multilayer structure is an effective coating method to increase the corrosion resistance and to decrease the ICR for metallic bipolar plates in PEMFC.

Cell behavior of the transformed cells is known to affect by interaction with extracellular matrix (ECM) proteins and integrin. To investigate the alterations of both integrin expression and cell-matrix interaction during neoplastic conversion of human oral kerationcytes, we studied expression levels of integrin subunits by flow cytometry and cellular responses to the ECM proteins in normal human oral keratinocytes (NHOKs), HPV-immortalized HOK-16B line, and three oral cancer cell lines established from HOK-16B line, CTHOK-16B-BaP, CTHOK-16B-DMBA, and CTHOK-16B-Dexa lines. The expression levels of α and β integrin subunits were shown decreased tendency in human oral keratinocytes undergoing immortalization and tumorigenic transformation except CTHOK-16B-DMBA line tested. Although αuβ6 integrin is known to be highly expressed in squamous cell carcinomas, and the altered integrin expression is suspected to be associated with cellular carcinogenesis, αu integrin subunit and αuβ6 egrin did not express in oral cancer cell lines tested. Cell behavior to the ECM proteins in HOK-16B line was generally similar to that of exponentially proliferating NHOKs. The adhesion activity profiles of type I collagen were very similar to that of its laminin counterparts, but fibronectin showed minimal adhesion activity under our conditions compared to the BSA control. The ability of the CTHOK-16B-BaP line to spread upon type I collagen and laminin markedly decreased, but migration was notably increased on type I collagen. In contrast, CTHOK-16B-DMBA and CTHOK-16B-Dexa lines spread less but migrated more upon type I collagen than immortalized HOK-16B line. These data indicate that downregulation of integrin subunits causes the changes of cellular responses to the ECM proteins during neoplastic conversion of human oral keratinocytes, and that cellular responses to the ECM proteins in oral cancer cell lines established by exposing different carcinogens are variable according to chemical carcinogens treatment.

The molten carbonate fuel cell has conspicuous features and high potential in being used as an energy converter of various fuels to electricity and heat. However, the MCFC which use strongly corrosive molten carbonate at 650℃ have many problem. Systematic investigation on corrosion behavior of Fe/20Cr/Ti has been done in (62+38)mol % (Li+K) CO3 melt at 923K by using. steady state polarization and electrochemical impedance spectroscopy method. It found that the corrosion current of these Febased alloys decreased with increasing Ti content, and this attribute to the formation of LiCrO2 layer at the surface.