In this study, we studied the method of using general architectural glass instead of using the existing acrylic material for high luminance flat lighting. The flat panel lighting used the side illumination method to increase the ease of installation and aesthetic satisfaction. In general, glass has an amorphous structure with a lower angle of refraction than acrylic, so it is not suitable for use in flat panel lighting as a light guide, but in this study, the role of light distribution characteristics and diffusion patterns in the case of using such a glass light guide. Quantitative simulations were conducted to confirm new possibilities. In the simulation, the backlight estimation method was used, and about 10,000,000 rays were placed within a unit area in order to obtain a result similar to the real thing. As a result of the simulation, the geometry of the diffusion pattern could be specified, and the value of the geometry could be quantified using the ratio of the diameter and height of the pattern. As a result of the calculation, it was found that the maximum amount of light was generated around 75 degrees by quantitatively calculating the ratio and the outgoing light angle at which the maximum value of the outgoing light occurred between 05 and 1.0. As a result of these studies, it was confirmed that it is possible to use ordinary glass at the same time as a transparent window and light-emitting lighting at night.

태양광 발전의 효율을 높이기 위한 실란 커플링제와 나노 무기산화물을 첨가한 계면활성제를 이용한 친수성 코팅액을 제조하여 태양광 모듈의 유리 표면에 도포하여 김서림 방지(antifogging) 및 내오염성(antifouling)을 부여하였다. 1% 친수성 코팅액에 나노 무기산화물인 LudoxⓇ를 첨가한 경우 LudoxⓇ의 농도에 관계없이 초친수성 과 우수한 antifogging 효과를 나타내었다. 그러나 유리에 대한 antifouling 효과는 LudoxⓇ를 10% 이상 첨가하였을 때부터 발현되었다. 또한, pH 4에서 가수분해한 TEOS를 첨가한 코팅액의 경우 TEOS를 0.7% 첨가한 경우 steam test 결과 antifogging 효과를 유지하였으며, 코팅한 유리 표면을 젖은 킴와이 프로 100회 문지른 후에도 pollution test 결과 antifouling 효과를 유지하였다. 또한, AFM을 이용하여 표면 거칠기(Rq)를 확인한 결과 TEOS를 너무 많이 첨가하면 가장 높은 표면 거칠기 값을 보였으며 코 팅된 표면의 상태도 매우 불규칙하였다. TEOS가 0.7% 첨가된 경우 비교적 높은 표면 거칠기 값과 안 정된 표면 상태를 나타내었다. 결론적으로 김서림 방지 특성만을 위하여는 나노 무기산화물인 LudoxⓇ는 필요없으나, antifouling의 효과를 나타내기 위해서는 최소 10%의 LudoxⓇ가 첨가되어야 하며, 우수한 내구성을 나타내기 위해서 는 0.7%의 TEOS를 첨가해야 한다.

In order to select the supporting points for large glass panels used for TFT-LCD monitors, an optimization method selecting the supporing points is presented. In this method we reduce the problem of 1 degree of freedom. ANSYS optimization module is used and optimization criterion is to minimize the maximum deflection.

A laser glass cutting system using a femto-second laser was evaluated for Flat Panel Display (FPD) glass. A theoretical analysis of the ablation threshold and depth is described using an explicit analytic form. Experiments for clean and deep grooves were performed using a 3W femto-second laser, and the relationships between the input energy and the scribing depth as well as the threshold energy are presented. Mechanical breaking after the scribing process was carried out and the results are compared with a theoretical method. It was found that a two-sided LCD panel glass can be cut clearly using the laser cutting method. The methodology was found to be very effective as a mass-production cutting system.

평판디스플레이용 진공패널의 제작시 진공으로 유지된 패널을 구성하는 유리판이 받는 응력과 변위를 계산하였다. 유리판의 두께, 패널의 크기 및 실링폭의 크기를 변수로 하여 실제로 진공패널을 제작한 후 패널의 파괴양상과 변위를 측정하였다. 유리판의 파괴양상과 변형측정을 통하여 유리판에 걸리는 최대응력은 테두리부분에 걸리는 것을 확인하였다. 제작된 진공패널이 갖는 응력분포 및 변위의 분포는 패널을 진공실링할 때 사용한 실런트의 폭에 크게 의존하였다. 패널의 실링폭이 커질수록 모서리가 완전 고정된 조건으로 계산한 결과와 유사하였다. 두께가 3mm인 유리판을 사용해서 80×120textrmmm2</TEX> 크기의 패널을 제작할 때 실링폭이 20mm인 경우 측정된 변위는 57μm였으며, 이 값은 모서리가 완전히 고정된 조건으로 계산한 갈인 54μm와 비슷하였다.

Municipal solid wastes incinerator (MSWI) bottom ash and melting slag are used to prepare external panel for increasingthe recycling rate of them in this study. In case of external panel, the most important property is flexural strength. Becauseit is easily distorted by external force. Wasted glass fiber (below WGF) is used to increase the flexural strength of externalpanel. Flexural strength of prepared panel was 14.6MPa of the mixing ratio of 3.0wt% WGF. But compressive strengthwas decreased with the addition of WGF. Because L/S ratio has to be increased to enhance the workability at high additionamount of WGF. High liquid content hinders geopolymer formation. But compressive strength (about 20MPa) was notlow at this condition.