This research developed the fiber pullout impact test machine to investigate interfacial bond strength between fiber and cement based matrix under high velocity. To achieve the goal, firstly the existing pullout test machines were investigated. And then, these drawback were comprehended. Finally, Fiber pullout impact test machine base on strain energy frame impact machine was proposed.

This study performed gas-gun propelled projectile impact tests with high strength steel fiber reinforced concrete. Also, from the impact tests, failure modes and protection performances of HIgh Performance Concrete which is reinforced by steel fibers were assessed. High strength steel fiber reinforced concrete showed excellent protection performances against impact loads.

This research developed the fiber pullout impact test machine to investigate interfacial bond strength between fiber and cement based matrix under high velocity. To achieve the goal, firstly the existing pullout test machines were investigated. And then, these drawback were comprehended. Finally, Fiber pullout impact test machine base on strain energy frame impact machine was proposed.

공공시설물의 대형화 및 도심지로의 인구 밀집화에 따라 충돌 또는 폭발과 같은 하중조건 하에서의 구조물 방호성능의 중요성이 대두되고 있다. 그러나 구조물의 방호설계 및 시공에 있어서 필수적이라 할 수 있는 구조 재료 또는 자재에 대한 방호성능 평가기준은 현재 정 립되어 있지 않은 실정이다. 따라서 본 연구에서는 구조용 자재의 내충격 성능평가 기준 개발 연구의 일환으로 가스건을 사용한 발사체 충격 파 괴시험을 콘크리트 시험체에서 수행함과 동시에, 다양한 접촉식 계측 센서의 적용 가능성을 확인하고자 하였다. 또한, 충격 파괴시험을 통해 일반 콘크리트 및 강섬유가 보강된 초고성능콘크리트의 파괴모드 및 방호성능에 대한 평가를 수행하였다. 실험 수행 결과, 접촉식 계측센서 중 LVDT 변위계의 적용 가능성을 확인하였으며, UHPC의 경우 혼입된 보강섬유의 효과로 인해 일반 콘크리트에 비해 우수한 방호성능을 보여주 었다.

Shock wave caused by the high-velocity impact causing the tensile strain and stress on the rear side. When the tensile strain and stress exceeds the tensile strength of the concrete, crack and fracture were occurred. The strain on the rear side was reduced due to Improvement of the tensile strength by fiber reinforcement and increasing the specimen thickness.

In this study, impact of high-velocity projectile by mixing steel fiber, polyamide, nylon, polyethylene fiber which have different shape and properties respectively. Scabbing is restrained because of micro-crack caused by the shock wave offset effect and energy dispersive of synthetic fibers are mixed populations.

본 연구에서는 강섬유와 FRP 시트에 의한 충격 저항성능 향상 효과를 평가하기 위하여 고속 충격하중을 받는 2방향 RC 슬래브에 대한 유한요소 해석을 수행하였다. 유한요소 해석 프로그램으로는 충격해석에 탁월하다고 알려진 LS-DYNA를 사용하였으며, 실험결과와의 비교를 위하여 핀란드 VTT 연구소에서 수행한 고속 충격 실험과 동일한 조건으로 해석을 수행하였다. 2100×2100×250 mm의 RC 슬래브에 강 (steel)발사체를 통해 충격하중을 가하였으며 발사체의 무게는 47.5kg, 속도는 134.9m/s였다. 본 연구에서는 별도의 재료부재에 대한 충격실험을 통해 해석에 사용할 재료 모델을 검증하였다. 본 해석에서는 SFRC의 비선형적 연화 현상을 모사하기 위해 elastic-plastic hydro model을 적용하였으며, 보통콘크리트와 FRP의 재료모델을 모사하기 위해서 concrete damage model과 orthotropic elastic model을 각각 사용하였다. 해석 결과, 제안된 해석 기법은 충분한 신뢰성을 가지고 있으며, 보강 재료와 보강 기법의 유효성을 평가하는데 효과적으로 적용할 수 있을 것으로 판단된다. 또한 강섬유와 FRP Sheets 보강방법은 고속충격하중에서 우수한 충격 저항 성능을 보여주는 것을 확인하였다.