본 연구에서는 해상가두리 양식장에서 북방전복과 둥근전복속 교잡종(왕전복♀*둥근전복♂)의 생물지표를 분석하여 교잡육종의 결과를 평가하고자 하였다. 생존율은 북방전복과 유사하였 으나, 성장(각장)은 교잡종에서 약 10% 빠른 것으로 분석되었다. 패각의 호흡공 기형율은 교잡 종이 북방전복보다 약 6% 낮았으며, 패각 함몰 및 부식율은 교잡종이 약 15% 낮았다. 생화학 적 조성에서는 조단백질의 경우 교잡종에서 약 3.1% 높았으며, 이를 제외한 나머지에서 유사 한 값을 나타냈다. 소화, 흡수 및 해독기능을 수행하는 간췌장의 조직학적 평가에서는 교잡종 에서 좋은 결과를 보였다. 이러한 결과로 보아 둥근전복속 교잡종은 추후 양식 환경에 접목 하였을 때 높은 양식 생산력을 가질 것으로 판단된다.

The purpose of this study was to investigate the improvement effect of biomarkers through the supply of natural diet in the juvenile hybrid abalone (Haliotis discus discus♀*H. madaka♂). For the study, the shell length of about 17 mm and the total weight of 0.83 g were used. The feeding conditions were set as the natural diet group (dried laver) and the formulated diet group, and the experiment duration was 16 weeks. The survival rate was about 14% higher in the natural diet group than the formulated diet group, and growth was also faster in the natural diet group. Shell malformation rate was lower in the natural diet group (7.5%) than the formulated diet group (21.5%). In the biochemical composition, except for carbohydrates, both experimental groups showed similar values. The degeneration of epithelial cells in the hepatopancreatic tubule was lower in the natural diet group than the formulated diet group, and the activity of basophilic cell was higher in the natural diet group. These results indicate that it is worth considering the supply of natural diet for the breeding of juvenile hybrid abalone and the improvement of the quality of the formulated diet (H. discus discus♀*H. madaka♂).

Nacre of abalone shell features a “brick-and-mortar” microstructure, in which micro-plates of calcium carbonate are bonded by nanometers-thick layers of chitin and proteins. Due to the microstructure and its unique toughening mechanisms, nacre possesses an excellent combination of specific strength, stiffness and toughness. This study deals with the possibility of using nacre fragments obtained from abalone shell for making a bulletproof armor system. A composite plate laminated with abalone shell fragments is made and compression and bend tests are carried out. In addition, a bulletproof test is performed with hybrid armor systems which are composed of an alumina plate, a composite plate, and aramid woven fabric to verify the ballistic performance of nacre. The compressive strength of the composite plate is around 258.3MPa. The bend strength and modulus of the composite plate decrease according to the plate thickness and are about 149.2MPa and 50.3 GPa, respectively, for a 4.85 mm thick plate. The hybrid armor system with a planar density of 45.2 kg/m2, which is composed of an 8 mm thick alumina plate, a 2.4 mm thick composite plate, and 18 layers of aramid woven fabric, satisfy the NIJ Standard 0101.06 : 2008 Armor Type IV. These results show that a composite plate laminated with abalone shell fragments can be used for a bulletproof armor system as an interlayer between ceramic and fabric to decrease the armor system’s weight.