In the present work, we synthesize nano-sized ZnO, SnO2, and TiO2 powders by hydrothermal reaction using metal chlorides. We also examine the energy-storage characteristics of the resulting materials to evaluate the potential application of these powders to dye-sensitized solar cells. The control of processing parameters such as pressure, temperature, and the concentration of aqueous solution results in the formation of a variety of powder morphologies with different sizes. Nano-rod, nano-flower, and spherical powders are easily formed with the present method. Heat treatment after the hydrothermal reaction usually increases the size of the powder. At temperatures above 1000oC, a complete collapse of the shape occurs. With regard to the capacity of DSSC materials, the hydrothermally synthesized TiO2 results in the highest current density of 9.1 mA/cm² among the examined oxides. This is attributed to the fine particle size and morphology with large specific surface area.

금속산화물 반도체 중 하나인 산화아연은 인체에 무해하고 친환경적이며, 우수한 화학적, 열 적 안정성의 특성을 지니며 3.37 eV의 넓은 밴드갭 에너지와 60 meV의 높은 엑시톤 바인딩 에너지로 인해 태양전지, 염료페기물의 분해, 가스센서 등 다양한 분야에 응용이 가능한 물질이다. 산화아연은 입 자 형상 및 결정성의 변화에 따라 광촉매 활성이 변하게 된다. 따라서, 다양한 실험변수와 첨가제를 사 용하여 입자를 합성하는 것이 매우 중요하다. 본 논문에서는 마이크로파 수열합성법을 사용하여 산화아연을 합성하였다. 전구체로는 질산아연을 사 용하였고, 수산화나트륨을 사용하여 용액의 pH를 11로 조정하였다. 첨가제로는 계면활성제인 에탄올아 민, 세틸트리메틸암모늄브로마이드, 소듐도데실설페이트, 솔비탄모노올레이트를 첨가하였다. 합성된 입자 는 별모양, 원추형, 씨드형태, 박막형태의 구형의 형상을 보였다. 합성된 산화아연의 물리・화학적 특성 은 XRD, SEM, TGA을 통하여 확인하였고, 광학적 특성은 UV-vis spectroscopy, PL spectroscopy, Raman spectroscopy으로 확인하였다.

Nano Pd spot-coated active carbon powders were synthesized by a hydrothermal-attachment method (HAA) using PVP capped Pd colloid in a high pressure bomb at , 450 psi, respectively. The PVP capped Pd colloid was synthesized by the precipitation-redispersion method. PVP capped Pd nano particles showed the narrow size distribution and their particle sizes were less than 8nm in diameter. In the case of nano Pd-spot coated active carbon powders, nano-sized Pd particles were adhered in the active carbon powder surface by HAA method. The component of Pd was homogeneously distributed on the active carbon surface.

본 연구에서는 올레산을 표면개질제로 사용하여 수열법을 통해 수산화 마그네슘을 합성하였다. 수산화 마그네슘은 알카리 조건에서 올레인산과의 반응을 통해 표면 개질된 마이크로 크기의 플레이크 형상을 갖는다. 수열합성에서 수산화 마그네슘 입자 생성의 조건은 pH, 온도 그리고 반응시간이 표면개질과 입자 형상의 주요 변수임을 확인하였다. 생성된 수산화 마그네슘 입자는 FE-SEM, XRD, FT-IR 그리고 TGA를 통해 확인하였다. 유기 용매 내에서의 분산성의 확인은 개질되지 않은 수산화 마그네슘과의 침전 테스트 비교를 통해 확인하였다.

Ag spot-coated Cu nanopowders were synthesized by a hydrothermal-attachment method (HA) using oleic acid capped Ag hydrosol. Cu nano powders were synthesized by pulsed wire exploding method using 0.4 mm in diameter of Cu wire (purity 99.9%). Synthesized Cu nano powders are seen with comparatively spherical shape having range in 50 nm to 150 nm in diameter. The oleic acid capped Ag hydrosol was synthesized by the precipitation-redispersion method. Oleic acid capped Ag nano particles showed the narrow size distribution and their particle size were less than 20 nm in diameter. In the case of nano Ag-spot coated Cu powders, nanosized Ag particles were adhered in the copper surface by HAA method. The components of C, O and Ag were distributed on the surface of copper powder.

The pearlesent pigment has received attention in a diversity of fields like cosmetics, inks, paints and so on. Ferric Ferrocyanide, one of the nano sized pearlescent pigment, is a kind of surface modification pigment that covers a metal oxidized substance or a coloring agent with uniform thickness. Characteristics of pearlescent pigment are various interference color, intense gloss effect and a three-dimensional effect. We synthesised the pearlesent pigment that ferric ferrocyanide can be deposited on the titania/mica surface by hydrothermal synthesis method. The process parameters are concentration of precursor, controlling pH and reaction temperature. The optimun conditions is that amount of iron(III) chloride hexahydrate is 3.1 wt% and amount of potassim ferrocynide trihydrate is 3.6 wt% in the started pH 4.5 at 70℃. The coating rate and coating efficiency of ferric ferrocyanide was about 1.47 % and 96.7 %, respectively. The synthesised pearlesent pigment was characterized by SEM, XRD, FT-IR and EDS.

nanowires were synthesized by a hydrothermal reaction of metallic Y with aqueous solution of LiOH. The morphology and the size of the nanowires changed with varying the volume of the LiOH solution inside the autoclave. nanowires transformed to by a subsequent heat-treatment without morphological change. By a proper control of hydrothermal reaction parameter and heat-treatment, the yield of pure nanowires up to 97% was attained.

우리는 마이카, boron nitride, bismuthoxychloride와 같은 판상 분체에 ZnO 나노입자를 코팅한 고 기능성 무기 분체를 합성하였다. 본 실험에서 우리는 수열침전법을 이용하여 합성 분체를 합성하였다. 출발물질은 ZnCl2를 사용하였고 침전제로는 hexamethylenetetramine(HMT)와 urea를 사용하였다. 본 실험의 반응변수로는 출발물질의 농도, 침전제 및 반응온도를 변화시켜 실험하였다. 합성물의 형태, 결정성 및 UV-차단능은FE-SEM, XRD, FT-IR, TGA-DTA, in vitro SPF 테스트를 활용해 분석하였다. 본 실험의 결과, 나토입자 크기를 갖는 ZnO는 동일한 최적의 합성조건하에서 다양한 판상 분체의 종류에 관계없이 균일하게 코팅되었다.

산소 결핍 페라이트 (oxygen deficient ferrites, ODF) MeFe2O4-δ는 약 300˚C의 낮은 온도에서 CO2를 C와 O2로 분해한다. 본 연구에서는 (Nix, Zn1-xFe24 초미세 페라이트 분말을 수열합성법으로 제조하여 CO2 분해특성을 살펴보았다. 제조된 페라이트는 XRD 분석 결과, 페라이트의 전형적인 스피넬 구조를 보여주고 있으며, ICP-AES, EDS 정량분석에 의하여 초기 혼합 조성비와 거의 동일한 조성비로 합성되었음을 알 수 있었다. 제조된 (Ni, Zn)-ferrites 분말의 BET 비표면적은 약 110mg2/g 이상의 큰 값으로 나타났으며, 입자크기는 약 5~10nm로 매우 작았다. 산소결핍 페라이트 (Nix, Zn1-x)Fe2O4-δ</TEX>의 CO2 분해 효율은 조성에 따라 큰 차이를 보이지 않았으며 3원계 (Ni, Zn)-ferrite가 Ni-ferrite보다 더 높았다.