To enhance the thermal properties of epoxy composites, expanded graphite (EG) was oxyfluorinated and embedded into epoxy resin as a reinforcement. The maximum thermal conductivity was obtained for epoxy composites with oxyfluorinated EG, representing a 62% increase compared to that of neat epoxy. Additionally, the glass transition temperature (Tg) and integral procedural decomposition temperature of epoxy composites with oxyfluorinated EG show the increase of 6% (4.4 °C) and 106% (264 °C), respectively, which indicated the improvement in thermal stability. These results can be attributed to the interfacial interaction between epoxy and oxyfluorinated EG, which formed strong interfacial interactions between the epoxy resin and EG due to the presence of oxygen- and fluorine-containing functional groups in oxyfluorinated EG.

소수성의 폴리에틸렌 다공성막 표면에 오염물질이 흡착됨으로써 발생되는 파울링 현상으로 인한 투과도 감소 문 제를 해결하고자 함산소불소화법을 이용하여 막 표면을 친수화 하였다. 함산소불소화 처리 후 접촉각은 93°에서 50°까지 감 소하였고, 수투과량은 60% 이상 증가하였다. 또한, 모델오염물질 Albumin (form bovine serum, BSA), Humic acid sodium salt (HA), Alginic acid sodium salt (SA) 100 ppm의 수용액을 이용하여 투과도 평가 실험을 수행한 결과 막이 친수화 됨에 따라 오염물질이 흡착되는 정도가 감소하여 투과도가 향상된 것을 확인할 수 있었으며, 특히 SA에 대해서는 파울링 개선효 과가 크게 나타나 처리하지 않은 PE막에 비해 투과도가 두 배 이상 향상된 값을 나타내었다.

The oxyfluorination effects of activated carbon nanofibers (OFACFs) were investigated for CO2 storage. Electrospun CFs were prepared from a polyacrylonitrile/N,N-dimethylformamide solution via electrospinning and heat treatment. The electrospun CFs were chemically activated in order to generate the pore structure, and then oxyfluorination was used to modify the surface. The samples were labeled CF (electrospun CF), ACF (activated CF), OFACF-1 (O2:F2 = 7:3), OFACF-2 (O2:F2 = 5:5) and OFACF-3 (O2:F2 = 3:7). The functional group of OFACFs was investigated using X-ray photoelectron spectroscopy analysis. The C-F bonds formed on surface of ACFs. The intensities of the C-O peaks increased after oxyfluorination and increased the oxygen content in the reaction gas. The specific surface area, pore volume and pore size of OFACFs were calculated by the Brunauer-Emmett-Teller and density functional theory equation. Through the N2 adsorption isotherm, the specific surface area and pore volume slightly decreased as a result of oxyfluorination treatment. Nevertheless, the CO2 adsorption efficiency of oxyfluorinated ACF improved around 16 wt% due to the semi-ionic interaction effect of surface modificated oxygen functional groups and CO2 molecules.

In this study, the oxyfluorination of PAN-based carbon fibers was undertaken at room temperature using fluorine-oxygen mixtures, and the influence of oxyfluorination on properties was investigated. The surface characteristics of the modified fiber were determined by using X-ray photoelectron spectroscopy (XPS) and dynamic contact angle analyzer. The oxyfluorination of carbon fibers was one of the more effective methods to increase surface wettability by the formation of semicovalent C-F bond and C-O bond depending on reaction conditions. When oxygen mole fraction is increased from 0.5 to 0.9, it is probable that attached fluorine atoms at the surface of the fibers reacted with other components. As increased oxyfluorination time and decreased its pressures, semi-covalent peak is increased at 0.5 of oxygen mole fraction. The total surface free energy of oxyfluorinated carbon fibers decreased with increasing oxygen mole fraction over 0.5. These results indicate that the surface of carbon fibers became much more hydrophilic after the short oxyfluorination. The surface free energy of oxyfluorinated carbon fibers progressively decreased after 10 min treatment. The polar components of surface free energies were however, significantly higher for all oxyfluorinated samples than that for the untreated carbon fiber.

In this work, the effect of a direct oxyfluorination on surface and mechanical interfacial properties of PAN-based carbon fibers is investigated. The changes of surface functional groups and chemical composition of the oxyfluorinated carbon fibers are determined by FT-IR and XPS measurements, respectively. ILSS of the composites is also studied in terms of oxyfluorination conditions. As a result, FT-IR exhibits that the carboxyl/ester groups (C=O) at 1632 cm-1 and hydroxyl group (O-H) at 3450 cm-1 are observed in the oxyfluorinated carbon fibers. Especially, the oxyfluorinated carbon fibers have a higher O-H peak intensity than that of the fluorinated ones. XPS result also shows that the surface functional groups, including C-O, C=O, HO-C=O, and C-Fx after oxyfluorination are formed on the carbon fiber surfaces, which are more efficient and reactive to undergo an interfacial reaction to matrix materials. Moreover, the formation of C-Fx physical bonding of the carbon fibers with fluorine increases the surface polarity of the fibers, resulting in increasing ILSS of the composites. This is probably due to the improvement of interfacial adhesion between fibers and matrix resins.