In this paper, a shot peening was conducted to improve fatigue life by increasing resistance to hydrogen embrittlement of STS316 steel, which is widely used in hydrogen environments. First, considering the efficiency of the shot peening process, an effective Almen intensity was selected and applied to the specimen surface. Second, the specimen was hydrogen embrittled at room temperature (25°C) and high temperature (60°C) using electrochemical hydrogen charging. Third, the mechanical property tests (tensile, hardness, roughness) and 4-points rotational bending fatigue tests of the specimen were performed. All mechanical properties decreased, but the fatigue life of the shot peened specimens improved at the both temperature conditions. Ultimately, the fatigue characteristics against hydrogen embrittlement of STS316 steel, which is used in various industrial fields, are improved through an effective shot peening process, and the effect is believed to be very significant.

본 연구에서는 내식성이 우수한 동합금에 대하여 내구성 향상을 위해 쇼트피닝 시간을 변수로 표면 개질하여 전기화학적 특성과 조직 변화를 관찰하였다. 그 결과 쇼트피닝 후 표면에 전체적으로 요철이 발생하였으며, 시간이 증가할수록 커버리지 향상에 따른 균질화 현상이 관찰되었다. 또한 쇼트피닝된 모든 시험편에서 경도가 향상되었으며, 쇼트피닝 시간이 3.5분일 때 52 %의 경도향상을 나타냈다. 그리고 이때 전기화학적 특성은 쇼트피닝을 실시하지 않은 경우와 유사하였다