We report the effect of Standard Clean-1 (SC-1) cleaning to remove residual Ti layers after silicidation to prevent Al diffusion into Si wafer for Ti Schottky barrier diodes (Ti-SBD). Regardless of SC-1 cleaning, the presence of oxygen atoms is confirmed by Auger electron spectroscopy (AES) depth profile analysis between Al and Ti-silicide layers. Al atoms at the interface of Ti-silicide and Si wafer are detected, when the SC-1 cleaning is not conducted after rapid thermal annealing. On the other hand, Al atoms are not found at the interface of Ti-SBD after executing SC-1 cleaning. Al diffusion into the interface between Ti-silicide and Si wafer may be caused by thermal stress at the Ti-silicide layer. The difference of the thermal expansion coefficients of Ti and Ti-silicide gives rise to thermal stress at the interface during the Al layer deposition and sintering processes. Although a longer sintering time is conducted for Ti-SBD, the Al atoms do not diffuse into the surface of the Si wafer. Therefore, the removal of the Ti layer by the SC-1 cleaning can prevent Al diffusion for Ti-SBD.

본 실험에서는 반응성 스퍼터링법으로 N2/Ar 유속비를 달리하여 약 200 과 650 두께의 비정질 Ti-Si-N막을 증착한 후 Cu (750 )와 Si사이의 barrier 특성을 면저항측정, XRD, SEM, RBS 그리고 Ti-Si-N막에서 질소 함량의 영향에 초점을 둔 ABS depth profiling 등의 분석방법을 통해 조사되었다. 질소 함량이 증가함에 따라 처음에는 불량 온도가 46%까지 증가하다가 그 이상에서는 감소하는 경향을 보였다. 650 의 Ti-Si-N barrier막을 800˚C에서 열처리 후에는 Cu3Si 피크만 관찰될 뿐 Cu피크는 거의 완전히 사라졌으므로 Barrier 불량기구는 Cu3Si상을 형성하기 위해 Si 기판내로의 Cu의 확산에 의해 일어난 것으로 보인다. 본 실험에서 Ti-Si-N의 최적 조성은 Ti29Si25N46이었다. 200 과 650 두께의 Ti29Si25N46 barrier 층의 불량온도는 각각 650˚C와 700˚C이었다.이었다.