Aluminum-based powders have attracted attention as key materials for 3D printing owing to their low density, high specific strength, high corrosion resistance, and formability. This study describes the effects of TiC addition on the microstructure of the A6013 alloy. The alloy powder was successfully prepared by gas atomization and further densified using an extrusion process. We have carried out energy dispersive X-ray spectrometry (EDS) and electron backscatter diffraction (EBSD) using scanning electron microscopy (SEM) in order to investigate the effect of TiC addition on the microstructure and texture evolution of the A6013 alloy. The atomized A6013-xTiC alloy powder is fine and spherical, with an initial powder size distribution of approximately 73 μm which decreases to 12.5, 13.9, 10.8, and 10.0 μm with increments in the amount of TiC.

The effect of TiC content on oxidation behavior of the sintered WC-TiC-TaC alloys with 2 mass% TaC and different TiC amounts of 3-45 mass% was investigated through oxidation tests in air at 973K. As a result of the tests, it was revealed that with increasing TiC content in the alloys, mass changes caused by oxidation and thickness of the scale decreased. Thus, it is considered that the main component of the scales changed gradually from to with increasing TiC content in the alloys, and oxygen diffusion through the scale to the alloys was inhibited gradually.