In this experimental work, a p-type c-Si (100) substrate with 8 × 8 × 2 mm dimension was taken for TiCN thin-film coating deposition. The whole deposition process was carried out by chemical vapor deposition (CVD) process. The Si substrate was placed within the CVD chamber at base pressure and process pressure of 0.75 and 500 mTorr, respectively, in the presence of TiO2 (99.99% pure) and C (99.99% pure) powder mixture. Later on, quantity of C powder was varied for different set experiments. The deposition of TiCN coating was carried out in the presence of N2– H2–TiCl4–CH3CN gas mixture and 600 ℃ of fixed temperature. The time for deposition was fixed for 90 min with 10 and 5 ℃ min− 1 heating and cooling rate, respectively. Later on, heat treatment process was carried out over these deposited TiCN samples to investigate the changing characteristics. The heat treatment was carried out at 800 ℃ within the CVD chamber in the absence of any gas flow rate. The morphological properties of heat-treated samples have been improved significantly, evidence is observed from SEM and AFM analyses. The structural analysis by XRD has been suggested, upgradation in crystallinity of the heat-treated film as it possessed with sharp and higher intensity peaks. Evidence has been found that the electrochemical properties are enhanced for heat-treated sample. Raman spectroscopy shows that the intensity of acoustic phonon modes predominates the optic phonon modes for untreated samples, whereas for heat-treated samples, opposite trends have been observed. However, significant degradation in mechanical properties for heat-treated sample has been observed compared to untreated sample.

The ultra-fine and less agglomerated titanium carbonitride particles were successfully synthesized by magnesiothermic reduction with low feeding rate of solution. The sub-stoichiometric titanium carbide () particles were produced by reduction of chlorine component by liquid magnesium at of gaseous and the heat treatments in vacuum were performed for 5 hours to remove the residual magnesium and magnesium chloride mixed with produced . The final particle with near 100 nm in mean size and high specific surface area of was obtained by nitrification under nitrogen gas at for 2 hrs.

The ultrafine titanium carbonitride particles () below 100nm in mean size were successfully synthesized by Mg-thermal reduction process. The nanostructured sub-stoichiometric titanium carbide () particles were produced by the magnesium reduction at 1123K of gaseous and the heat treatments in vacuum were performed for five hours to remove residual magnesium and magnesium chloride mixed with . And final phase was obtained by nitrification under normal gas at 1373K for 2 hrs. The purity of produced particles was above 99.3% and the oxygen contents below 0.2 wt%. We investigated in particular the effects of the temperatures in vacuum treatment on the particle refinement of final product.

The increasing demand of PM parts for automobile and aerospace applications has caused a strong development of the aluminium based metal matrix composites (MMCs).Aluminium alloys are one of most widely used materials as matrix in MMCs, both in research and development as well as in industrial applications. In the present work, the influence of the ceramic reinforcement addition to a 2xxx series aluminium alloy is studied. Several percentages of TiCN have been added to the Al-Cu alloy using PM techniques, in order to analyze its influence on the liquid phase sintering process and on the final properties of the material.

Multilayered coatings on tungsten carbide cutting tools are widely used for enhancing cutting performance. In this paper, we review the CVD TiC/TiCN multilayer as a function of the multilayer period. The TiC/TiCN multilayers in initial stage show preferred (220) orientation but shifts to (200) orientation with decreasing multilayer period. The nanohardness of TiC/TiCN multilayers were found to increase with decreasing multilayer period and shows a maximum of 23.8 GPa at a period = 33.5 nm.

공구강 등 산업용 재료로 널리 사용되는 카바이드 계 재료는 입자 크기 및 분포에 따라 기계적 성질이 변화하므로, 이를 제어하고 조절하는 기술에 관하여 많은 연구가 진행되어 왔다. 본 연구에서는 TiCN-WC-Co 복합초경계 에서 소결 공정 및 조성변화에 따른 입자 모양을 관찰하고 이에 따른 업자 성장 거동을 고찰하였다. 일반적으로 입자 조대화 양상과 고상 입자의 모양과는 밀접한 관계가 있다. 각진 입자의 경우에 는 계면이 원자적으로 singular 하여