To co-fire with commercial LTCC (Low Temperature Co-fired Ceramic) materials at , different contents of were added to the (BZN) ceramics. According to the test results, the cubic phase of BZN was transformed into orthorhombic in all the test materials. phase was formed in test materials with of addition. The phase transformation of cubic BZN was controlled during the synthesis process with excess ZnO content. The Cubic and orthorhombic phases of BZN could coexist and be sintered densely at .

The influence of the internal current for the ZnO ceramics on the sintering behavior by pulse current sintering (PCS) method was investigated. To clear the dependence of inner current on the sintering behavior of ZnO ceramics, direct measurement of electric resistance of ZnO specimen under sintering by SPS device was carried out. It was observed that electric resistance of specimen decreases with increase in the temperature. The electric resistance begins to decrease from the low temperature of . The internal structure of sintered ZnO ceramics changed by the control of the internal current in the specimen using plate.