본 연구에서는 합성가스 CO를 생산하기 위해 저급 석탄-CO2 촉매 가스화 실험을 수행하였 다. 제조된 CO가스 특성은 키데코 탄과 신화 탄에 KOH, K2CO3, Na2CO3 촉매들의 화학적 활성화 방 법을 이용하여 조사되었다. CO 제조공정은 석탄과 화학약품 활성화 비율, 가스 유량, CO2 전환 반응온 도와 같은 실험 변수 분석을 통해 최적화되었다. 제조된 합성 가스는 가스 크로마토그래피(GC)에 의해 분석 되었다. 실험조건 T = 950 °C, CO2 유량 100 cc/min에서, 20 wt% Na2CO3가 혼합된 키데코 탄 에 대해 98.6%, 20 wt% KOH가 혼합된 신화탄에 대한 98.9% CO2 전환율을 얻었다. 또한, 저급 석탄-촉매 가스화 반응은 동일한 공급 비와 반응 조건에서 97.8%, 98.8%의 CO 선택도를 얻었다.

large amount of effluent water would be produced from low temperature coal catalytic gasification (LTCCG) developed by ENN Co, Ltd, which located at Langfang, Hebei Province. Many phenol homologous compounds and a large amount of other organic compounds were contained in this effluent water, but the overall concentration of the organic compounds was not very high (CODCr value was about several thousands mg/L). Too high cost would occur if treating it with a traditional liquid-liquid extraction process, and it was a waste of resources if the effluent water was directly purified with biochemical technology. In this paper, a decontaminating and recycling technique was developed for an effluent water, and a two-step technique includes flocculation-recycling and ion exchange adsorption-elution processes. By this two-step process, the CODCr value of the final outlet water was decreased to meet the related national standards, and at least 90% of the organics in the effluent water could be recovered.

본 연구는 석탄가스화 슬래그를 재활용하기 위한 방안으로 콘크리트용 혼화재로서 사용하기 위해 석고혼입유무에 따른 콘크리트 건조수축 길이변화량을 측정하였다. 실험결과 석고 미혼입타입에서는 최대 15x10-3 의 길이변화량을 나타내어 OPC에 비해 굉장히 큰 변화량을 보이는 반면, 석고 혼입타입에서는 최대 10x10-3 의 길이변화량을 나타내어 OPC와 거의 동일한 수준으로 나타났고, 치환율에 따라서 적은 수준의 길이변화량도 확인하였다. 따라서 고로슬래그 미분말을 콘크리트 혼화재로 사용하는 것과 마찬가지로 CGS를 콘크리트용 혼화재로 사용하기 위해서는 석고의 혼입이 수반되어야 할 것으로 판단된다.

본 논문에서는 혼합골재 종류 변화 및 CGS 치환율에 따른 콘크리트의 내구성 특성을 분석하였다. 실험결과 CGS 치환율이 증가할수록 AE공기량의 영향으로 내동해성은 저하, 조직치밀화의 영향으로 탄산화는 지연되는 것으로 나타났다.

In this study, as series of studies to provide how to apply coal gasification slag(CGS) as one of byproducts for high strength concrete, from a newly introduced power generation method in Korea, the possibility of using a mixed aggregate with 25 percent of CGS as a concrete residual were investigated. The results indicated that the compressive strength of concrete using CGS at early age was lower than that using CS, but compressive strength at 28 days showed similar levels of strength enhancement.

This study is a basic study to CGS, which originates from the IGCC, as fine aggregate for concrete. The study measured density, water absorption ratio, solid volume percentage for grain shape, fineness modulus, grading curve of physical properties of fine aggregate. As a result, the density and solid volume percentage for grain sheet were found to be satisfactory in the aggregate for content (KS F 2527).Water evaluation ratio, fitness modulus, and grinding curve did not meet KS standards. Therefore, it is deemed necessary to adjust the grain size through sieving in case of fineness modulus and grinding curve.

석탄가스화는 청정석탄이용기술의 한 분야로 최근 국제 유가의 급격한 변동과 더불어 매우 각광을 받고 있는 기술이다. 본 연구에서는 중국 내몽고 지역의 저급석탄을 출발물질로 가스화를 위한 광학적 특성, X선 분광특성, X선 회절특성, 광물학적 특성, 건조특성 등을 분석하였다. 분석결과 석탄의 등급은 slagging성과 fouling성이 매우 낮으며 착화온도가 250℃ 정도인 brown coal인 것으로 조사되었고, 석영, 능철석, 점토광물 등이 주요 불순물로 혼재하는 것을 알 수 있었다. 또한 초기 수분이 28%로 매우 높기 때문에 이를 쉽게 건조하기 위한 방법으로 열풍건조와 마이크로웨이브 건조기술을 적용하여 비교한 결과, 마이크로웨이브를 이용한 건조가 좀 더 효과적인 것을 알 수 있었다.

The coal gasification fuel is important to replace petroleum fuel. Also they have many benefits for reducing the air pollution. Measurements on the combustion characteristics of synthetic gas from coal gasification have been conducted as compared with LPG in constant volume combustion chamber. The fuel is low caloric synthetic gas containing carbon monoxide 30%, hydrogen 20%, carbon dioxide 5%, and nitrogen 45%. To elucidate the combustion characteristics of the coal gasification fuel, the combustion pressures, combustion durations, and pollutants(NOx, CO2, CO) are measured with equivalence ratios(ø), and initial pressures of fuel-air mixture in constant volume chamber. In the case of the coal gasification fuel, maximum combustion pressure and NOx concentration are lower rather than LPG fuel. However CO and CO2 emission concentration are similar to that of LPG fuel.