Concrete structure for nuclear power plant is mass concrete structure with large wall depth and easily permits cracking in early age due to hydration heat and drying shrinkage. It always needs cooling water so that usually located near to sea shore. The crack on concrete surface permits rapid chloride intrusion and also causes more rapid corrosion in the steel. In the study, the effect of age and crack width on chloride diffusion is evaluated for the concrete for nuclear power plant with 6000 psi strength. For the work, various crack widths with 0.0~1.4 mm are induced and accelerated diffusion test is performed for concrete with 56 days, 180days, and 365 days. With increasing crack width over 1.0mm, diffusion coefficient is enlarged to 2.7~3.1 times and significant reduction of diffusion is evaluated due to age effect. Furthermore, apparent diffusion coefficient and surface chloride content are evaluated for the concrete with various crack width exposed to atmospheric zone with salt spraying at the age of 180 days. The results are also analyzed with those from accelerated diffusion test.

버어리종 대말림시 백화엽발생을 방지하고 건조기간을 단축하기 위하여 시험을 수행하였던 바, 결과를 요약하면 다음과 같다. 1. 건조실내 온도는 흑색비닐피복구 및 환기창이용구가 관행구보다 3℃ 정도 높았으며, 탈수속도는 환기창이용구가 훨씬 빨랐다. 2. 백화엽발생율은 완전대말림구가 높았고, 지면을 30cm 판 처리가 낮았다. 3. 수량감소는 완전대말림구가 컸다. 4. 품질 및 대금은 환기창이용구 및 지면을 30cm판 구가 높았다. 5. 물리성은 줄말림용 차광막처리가 비교적 양호하였다. 6. 백화엽발생을 억제하기 위하여는 첫째, 본포에서 치마름엽과 과숙엽을 방지하고, 둘째, 하위엽은 1-2회 수확한 후 대베기를 실시하며, 셋째, 갈변후에는 건조기간을 단축시키기 위한 온습도관리에 유의해야 할 것으로 생각된다. 7. 버어리종 담배의 물리성을 향상시키면서 건조중 백화의 원인이 되는 산소 및 수분과의 반응을 억제시킬 수 있는 방법에 대하여는 앞으로 더욱 검토가 요구된다.