In the automotive industry, the platinum titanium anodes (Pt/Ti anode) play a significant role in electroplating of chromium coating on the vehicle’s shock absorber piston rod. In this paper, the structure of Pt/Ti anode was designed to obtain high quality and save time for the electroplating process. The structure of anode was designed in 2D & 3D modeling and analyzed by CATIA and ABAQUS program, respectively. The structural modeling of the anode was analyzed and carried out using a finite element method (FEM) by applied various loads. The manufacture anodes were installed in an electroplating bath in order to test the efficiency of chromium coating on shock absorber piston rod and safety of anode structure. The results presented indicate that the structural analysis is safe after applied loads due to the allowable stress is higher than the maximum equivalent stress about 4 times, and the chromium coating test obtained high-efficiency results.

본 연구에서는 투명도와 기계적 특성을 향상시키기 위해 저온 공정의 졸-겔 법을 이용하여 하이브리드 복합체의 코팅 박막을 제조하였다. 하이브리드 복합체로는 ZrO2/TiO2/organosilane을 사용하였으며, 그 중 organosilane은 3-(trimethoxysilyl)propyl methacrylate을 사용하였고 이는 저온 공정의 광경 화 반응을 위해 도입되었다. 다양한 조성비로 합성된 복합체를 폴리 카보네이트 기판 위에 저온 공정의 졸 -겔 법을 이용하여 광경화와 열처리 공정을 거처 코팅 박막을 제조하였고 이 코팅 박막의 광학 특성 및 기계적 강도를 확인하였다. 코팅 박막은 가시광선 영역에서 97.5 % 이상의 투과도를 가짐을 확인하였고 기계적 강도는 9H 이상의 연필 경도를 가진 것을 확인하였다. 특히 ZTS-2-1 코팅 박막의 나노 압입 경도는 1.14 GPa로 가장 높게 측정되었다.

Transparent organic-inorganic hybrid hard coating films were prepared by the addition of SiO2 or ZrO2, as an inorganic filler to improve the hardness property, filler was highly dispersed in the acrylic resin. To improve the compatibility in the acrylic resin, SiO2 or ZrO2 is surface-modified using various silanes with variation of the modification time and silane content. Depending on the content and kind of the modified inorganic oxide, transparent modified inorganic sols were formulated in acryl resin. Then, the sols were bar coated and cured on PET films to investigate the optical and mechanical properties. The optimized film, which has a modified ZrO2 content of 4 wt% markedly improved in terms of the hardness, haze, and transparency as compared to neat acrylate resin and acrylate resin containing modified SiO2 content of 8 wt%. Meanwhile, the low transparency and high haze of these films slowly appeared at SiO2 content above 10 wt% and ZrO2 content of 5 wt%, but the hardness values were maintained at 2H and 3H, respectively, in comparison with the HB of neat acrylate resin.

안경렌즈 하드코팅막의 광학상수를 얻기 위해 실리콘 웨이퍼를 하드코팅액에 침지 후 열처리하여 실리콘 위에 하드막을 코팅한 시료를 제작하였다. 제작된 시료는 가변 입사각 분광 타원계를 이용하여 65 0 , 70 0 , 75。로 빛을 입사하여 W와 A를 얻은 후 곡 선맞춤으로 파장에 따른 굴절률과 아베수를 구했다. 하드코팅막의 두께는 시료A( 굴절률 (nd) 이 1.56 인 안경렌즈의 하드코팅막)인 경우는 약 1.611m 이고， 시료B( 굴절률 (nd) 이 1.67 인 안경렌즈의 하드코팅막)인 경우는 약 3.611m 임을 SEM사진 분석으로부터 알 수 있었다. 하드코팅막의 성분과 구조는 XRD 피크 로부터 주로 silicon으로 되어 있으며 결정방향은 (111) 임을 알 수 있었다. 시료A의 굴절률은 1.551 이며， 시료B 인 경우는 하드코팅막의 굴절률이 1.668 이였으며， 인-경렌즈 의 굴절률과 거의 비슷한 하드코팅막을 사용하여 간섭에 의한 반사 현상을 없댔으며， 아베수는 시료A와 시료B에서 각각 46 .577과 24.923임을 굴절률 분산 곡선으로부터 알 수 있었다.