인류는 아름다움을 추구하는 경향이 있으며, 진주는 부와 신분의 상징으로 수 천년 동안 많 은 사람들의 사랑을 받아 왔다. 현재의 인조진주는 밝은 색감을 갖고 코팅공정이 쉬운 유기색소를 이용 하였으나, 낮은 내후성 및 내구성과 천연진주의 고급스러운 광택 표현의 어려움으로 인해 새로운 코팅 기술이 필요한 실정이다. 본 연구는 코팅 결합제로 니트로셀룰로오스와 우레탄을 이용하였고, 색감을 표 현하기 위하여 무기 펄 안료를 사용하였다. 니트로셀룰로오스와 용매의 비, 우레탄과 경화제의 비, 펄의 첨가량, 코팅 횟수, 건조 온도 등의 실험변수를 조절하여 실험을 진행하였다. 코팅 된 인조진주는 색차 계, 자외선, 촉진내후성 등의 특성을 분석하였고, 우레탄을 이용한 경우 내약품성 및 내후성이 니트로셀 룰로오스 보다 뛰어난 것을 확인하였다.

NiAl2O4 nanoparticle was synthesized by a reverse micelle processing for inorganic pigment. N (NO3)2·6H2O and Al(NO3)3·9H2O were used for the precursor in order to synthesize NiAl2O4 nanoparticles. The aqueous solution, which consisted of a mixing molar ratio of Ni/Al, was 1:2 and heat treated at 800~1100 oC for 2h. The average size and distribution of synthesized NiAl2O4 powders are in the range of 10-20 nm and narrow, respectively. The average size of the synthesized NiAl2O4 powders increased with an increasing water-to-surfactant molar ratio and heating temperature. The crystallinity of synthesized NiAl2O4 powder increased with an increasing heating temperature. The synthesized NiAl2O4 powders were characterized by X-ray diffraction analysis(XRD), a field emission scanning electron microscop (FE-SEM), and a color spectrophotometer. The properties of synthesized powders were affected as a function such as a molar ratio and heating temperature. Results indicate that synthesis using a reverse miclle processing is a favorable process to obtain NiAl2O4 spinels at low temperatures. The procedure performed suggests that this new synthesis route for producing these oxides has the advantage of being fast and simple. Colorimetric coordinates indicate that the pigments obtained exhibit blue colors.

Inorganic pigments have high thermal stability and chemical resistance at high temperature. For these reasons, they are used in clay, paints, plastic, polymers, colored glass and ceramics. CoAl2O4 nano-powder was synthesized by reverse-micelle processing the mixed precursor(consisting of Co(NO3)2 and Al(NO3)3). The CoAl2O4 was prepared by mixing an aqueous solution at a Co:Al molar ratio of 1:2. The average particle size, and the particle-size distribution, of the powders synthesized by heat treatment (at 900; 1,000; 1,100; and 1,200˚C for 2h) were in the range of 10-20 nm and narrow, respectively. The average size of the synthesized nano-particles increased with increasing water-to-surfactant molar ratio. The synthesized CoAl2O4 powders were characterized by X-ray diffraction analysis(XRD), field-emission scanning electron microscopy(FE-SEM) and color spectrophotometry. The intensity of X-ray diffraction of the synthesized CoAl2O4 powder, increased with increasing heating temperature. As the heating temperature increased, crystal-size of the synthesized powder particles increased. As the R-value(water/surfactant) and heating temperature increased, the color of the inorganic pigments changed from dark blue-green to cerulean blue.

석록과 석청은 우리나라 전통 채색 문화유산에서 각각 녹색과 청색안료로 사용되어온 전통안료이며, 천연광물인 공작석과 남동석이 원료광물로 알려져 있다. 석록과 석청은 모두 중국, 일본 등지에서 수입된 것으로 알려져 있으며, 일부 청색계열의 안료가 국내에서 산출된 기록이 있으나, 탄산염 광물이 생성되기 어려운 우리나라의 지질환경을 고려하면 가능성은 높지 않다. 무기안료인 석록과 석청의 특성을 파악하기 위해 공작석과 남동석 원료를 확보하고 성분분석을 실시하였으며, 전통제법을 적용하여 안료를 제조하고 특성을 분석하였다. 제조한 석록의 L* 값은 59-83 정도, a* 값은 -20 이하로서, 시판제품에 비해 채도가 약간 높았다. 흡유량은 22-29 mL/100 g이고, 은폐력은 99.2 % 이상으로 우수하였다. 석청의 L* 값은 35-65 범위이고, b* 값은 -15 이하로서, 시판제품에 비해 상대적으로 채도가 낮았다. 흡유량은 21-26 mL/100 g이며, 석록과 마찬가지로 은폐력이 99.1 % 이상으로 우수하였다. 남동석의 원료광물은 남동석 외에 공작석, 석영 등의 불순물이 함유하고 있으며, 석청 제조 시 혼합된 불순물이 석청안료의 색도, 흡유량 등의 특성에 영향을 미치는 것으로 판단된다.