In recent years, supercapacitors have attracted extensive attention due to their advantages such as fast charge and discharge rate, high power density and long cycle life. Because of its unique porous structure and excellent electrochemical properties, heteroatom-doped porous carbon (HPC) is deemed as a promising electrode material for supercapacitors. However, it is a great challenge to synthesize electrode materials with large surface area, ultra-high porosity and good electrochemical performance. In this work, two-dimensional conjugated microporous polymers (CMPs) containing ketones were synthesized by a simple one-step coupling reaction and used as carbon precursors. A series of samples (CMP-Ts) were prepared with the procedures of coupling reaction and carbonization. The optimized carbon material has high specific surface area (up to 2229.85 m2 g− 1), porous structure, high specific capacitance (375 F g− 1 at 0.5 A g− 1), and good cycling stability (capacitance retention of 98.8% after 1000 cycles at 5 A g− 1). Further, the supercapacitor has an energy density of 28.8 Wh kg− 1 at a power density of 5000 W kg− 1. This work lays a foundation for the preparation of carbon materials using microporous polymer as a precursor system, provides a new way of thinking, and demonstrates a great potential of high-performance supercapacitors.

In this study, we synthesized pH-controlled resorcinol-formaldehyde (RF) gels through the polymerization of two starting materials: resorcinol and formaldehyde. The prepared RF gels were dried using an acetone substitution method, and they were subsequently carbonized under nitrogen atmosphere to obtain carbon xerogels (CX_Y) prepared at different pH (Y). The carbon xerogels were utilized as active materials for coin-type organic supercapacitor electrodes to investigate the influence of pH on the electrochemical properties of the carbon xerogels. The carbon xerogels prepared at lower pH (CX_9.5 and CX_10) exhibited sufficient particle growth, with a three-dimensional network of particles during the RF gel formation, resulting in the development of abundant mesopores. Conversely, the carbon xerogels prepared at higher pH (CX_11 and CX_12) retained densely packed structures of small particles, leading to pore collapse and low specific surface areas. Consequently, CX_9.5 and CX_10 showed high specific surface areas, and provided ample adsorption sites for the formation of electric double layers with electrolyte ions. Moreover, the three-dimensional particle network in CX_9.5 and CX_10 significantly enhanced electrical conductivity. The presence of well-developed mesopores in these materials further facilitated the effective transport of electrolyte ions, contributing to their superior performance as organic supercapacitor electrodes. This study confirmed that pH-controlled carbon xerogels are one of the promising active materials for organic supercapacitor electrodes. Furthermore, we concluded that pH during RF gel formation is a crucial factor determining the electrode performance of the carbon xerogels, highlighting the need for precise pH control to obtain high-performance carbon xerogel electrodes.

We have prepared MIL-101/graphene oxide (GO) composites with various mixing molar ratio of Fe-containing metal– organic frameworks (MOFs) against GO. When synthesizing MOFs, it was possible to synthesize uniform crystal powders using hydrothermal method. MIL-101 consists of a terephthalic acid (TPA) ligand, with the central metal composed of Fe, which was the working electrode material for supercapacitors. Field emission scanning electron microscopy, X-ray diffraction, Fourier transform infrared spectroscopy, and X-ray photoelectron spectroscopy analysis had been done to ascertain microstructures and morphologies of the composites. Cyclic voltammetry, electrochemical impedance spectroscopy, and galvanostatic charge–discharge measurements were performed to analyze the electrochemical properties of the composite electrodes in 6 M KOH electrolyte. By controlling the metal ligand mole ratio against GO, we prepared a changed MOF structure and a different composite morphology, which could be studied as one of the promising optimized electrode materials for supercapacitors.

In this report, we successfully prepared nitrogen-doped porous carbon (N-PC)/manganese dioxide ( MnO2) composite for a high-performance supercapacitor. X-ray diffraction data revealed the α-MnO2 phase. Transmission electron microscopy confirmed that the nanostructured α-MnO2 nanoparticles were coated on the surface of N-PC. The N-PC/α-MnO2 composite delivered a capacitance of 525.7 F g− 1 at the charging current of 1.0 A g− 1. The higher capacitance of the composite could be owing to the synergy of MnO2 and N-PC. Besides, the electrode exhibited a 14.7% capacitance loss after 6000 charge– discharge cycles at 10 A g− 1 indicating good electrochemical stability.

Doped porous carbon materials have attracted great interest owing to their excellent electrochemical performance toward energy storage applications. In this report, we described the synthesis of nitrogen-doped porous carbon (N-PC) via carbonization of a triazine-based covalent organic framework (COF) synthesized by Friedel–Crafts reaction. The as-synthesized COF and N-PC were confirmed by X-ray diffraction. The N-PC exhibited many merits including high surface area (711 m2 g−1), porosity, uniform pore size, and surface wettability due to the heteroatom-containing lone pair of electron. The N-PC showed a high specific capacitance of 112 F g−1 at a current density of 1.0 A g−1 and excellent cyclic stability with 10.6% capacitance loss after 5000 cycles at a current density of 2.0 A g−1. These results revealed that the COF materials are desirable for future research on energy storage devices.

Abstract In this study, we investigated that the activated carbon (AC)-based supercapacitor and introduced SIFSIX-3-Ni as a porous conducting additive to increase its electrochemical performances of AC/SIFSIX-3-Ni composite-based supercapacitor. The AC/SIFSIX-3-Ni composites are coated onto the aluminum substrate using the doctor blade method and conducted an ion-gel electrolyte to produce a symmetrical supercapacitor. The electrochemical properties of the AC/SIFSIX-3-Ni composite-based supercapacitor are evaluated through cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS), and galvanostatic charge/discharge tests (GCD). The AC/SIFSIX-3-Ni composite-based supercapacitor showed reasonable capacitive behavior in various electrochemical measurements, including CV, EIS, and GCD. The highest specific capacitance of the AC/SIFSIX-3-Ni composite-based supercapacitor was 129 F g−1 at 20 mV s−1.

본 연구에서는 다공성 활성탄소와 금속유기골격체 복합재료 기반의 전극 재료와 “이온젤” 이라고 불리는 고분자 고체 전해질을 이용하여 슈퍼커패시터를 제작 하였으며, 금속유기골격체의 함량에 따른 전기화학적 거동을 관찰하여 보았다. 슈퍼커패시터의 전기화학적 특성은 순환전압전류법(CV), 전기화학적 임피던스 분광법(EIS) 및 전정류 충·방전법(GCD)으로 분석하였으며, 그 결과로, 다공성 활성탄소 대비 금속유기골격체를 0.5 wt% 첨가 하였을 때 가장 높은 전기용량값을 확인 할 수 있었으며, 0.5 wt% 이상의 금속유기골격체의 함유량은 전기화학적 특성 감소에 영향을 주는 것으로 사료되며, 이러한 결과를 바탕으로 제조된 다공성 활성탄소/금속유기골격체 복합재료 기반의 슈퍼커패시터는 다양한 분야에 활용이 가능 할 것으로 판단된다.

In this study, we intensively investigated the effect of conductive additive amount on electrochemical performance of organic supercapacitors. For this purpose, we assembled coin-type organic supercapacitor cells with a variation of conductive additive(carbon black) amount; carbon aerogel and polyvinylidene fluoride were employed as active material and binder, respectively. Carbon aerogel, which is a highly mesoporous and ultralight material, was prepared via pyrolysis of resorcinolformaldehyde gels synthesized from polycondensation of two starting materials using sodium carbonate as the base catalyst. Successful formation of carbon aerogel was well confirmed by Fourier-transform infrared spectroscopy and N2 adsorptiondesorption analysis. Electrochemical performances of the assembled organic supercapacitor cells were evaluated by cyclic voltammetry, galvanostatic charge/discharge, and electrochemical impedance spectroscopy measurements. Amount of conductive additive was found to strongly affect the charge transfer resistance of the supercapacitor electrodes, leading to a different optimal amount of conductive additive in organic supercapacitor electrodes depending on the applied charge-discharge rate. A high-rate charge-discharge process required a relatively high amount of conductive additive. Through this work, we came to conclude that determining the optimal amount of conductive additive in developing an efficient organic supercapacitor should include a significant consideration of supercapacitor end use, especially the rate employed for the charge-discharge process.