This study was focused on the maximization of flame-retardancy of polyesters by a synergism of simultaneously introduced chlorine and phosphorus into polymer chains of modified polyesters. To prepare modified polyesters, reaction intermediates, TD-adduct (prepared from trimethylolpropane/2,4-dichlorobenzoic acid (2,4-DCBA)) and TMBO (prepared from tetramethylene bis(orthophosphate)), were prepared first, then condensation polymerization of the prepared intermediates, adipic acid, and 1,4-butanediol were carried out. In the condensation polymerization, the content of phosphorus was fixed to be 2%, and the content of 2,4-DCBA that provides chlorine component was varied to be 10, 20, and 30wt%, and we designated the prepared modified polyesters containing chlorine and phosphorus as ABTT-10C, -20C, -30C. Two-component PU flame-retardant coatings (ABTTC, ABTTC-10C, ABTTC-20C, ABTTC-30C) were prepared by the curing of synthesized ABTTs with a curing agent of allophanate/trimer at room temperature. To examine the film properties of the prepared PU flame-retardant coatings, film specimens were prepared with the prepared coatings. The film properties of ABTTC, ABTTC-10C and ABTTC-20C, which contain 0, 10 and 20wt% 2,4-DCBA, respectively, were proved to be good, whereas the film properties of ABTTC-30C, which contains 30wt% 2,4-DCBA, was proved to be a little bit poor. Two kinds of flame retardancy tests, ˚45Meckel burner method and LOI method were performed. With the ˚45Meckel burner method, three flame-retardant coatings except ABTTC showed less than 3.4cm of char length, and showed less than 2 seconds of afterflaming and afterglow. From this result, the prepared flame-retardant coatings were proved to have the 1st grade flame retardancy. With the LOI method, the LOI values of the coatings containing more than 10wt% 2,4-DCBA were higher than 30%, which means that the coatings possess good flame retardancy. From these results, it was found that synergistic effect in flame retardancy was taken place by the introduced phosphorus and chlorine.

The PU flame-retardant coatings (TTBAH, ATBAH-10C, -20C, and -30C) were prepared using the synthesized ATBAs and HDI-trimer as curing agent at room temperature. The physical properties of PU flame-retardant coatings with chlorine and phosphorus were inferior to those with phosphorus only and the properties were getting worse with increasing chlorine content. Flame retardancy was tested with three methods. With the vertical method, complete combustion time of ATBAHs were 259~347 seconds, which means that the prepared coatings are good flame-retardant. With the 45˚ Meckel burner method, char lengths of the three prepared coatings were less than 2.9 cm, which indicates that the prepared coatings are first grade. With the limiting oxygen index (LOI) method, the LOI values of the three prepared coatings were in the range of 30~35%, which proves good flame retardancy of the prepared coatings. from the result of flame retardancy tests of the specimens that contain the same amounts of flame retarding compounds. it was found that the coatings containing both phosphorus and chlorine show higher flame retardancy than the coatings containing only phosphorus. This indicates that there exists, some synergy effect between coexisting phosphorus and chlorine.

In order to obtain the maximum flame retardancy as well as the minimum deterioration of physical properties of PU flame-retardant coatings, chlorine and phosphorus functional groups were introduced into the pre-polymer of modified polyesters. In the first step, the tetramethylene bis(orthophosphate) (TBOP) and neohexanediol dichloroacetate (DCA-adduct) intermediates were synthesized. In the second step, 1,4-butanediol and adipic acid monomers were polymerized with the two kinds of intermediates to obtain copolymers. The modified polyesters containing chlorine and phosphorus (ATBA-10C, -20C, and -30C) were synthesized by adjusting that the content of phosphorus compound was fixed as 2wt% and the contents of chlorine compound (dichloroacetic acid) were varied as 10, 20, and 30wt%. Average molecular weight and polydispersity index of the preparation of ATBAs were decreased with increasing DCA content because of the increase in hydroxyl group that retards reaction.

Modified polyesters (TTBA-10C, -20C, -30C) that contain phosphorus and chlorine were synthesized by the condensation polymerization of tetramethylene bis(orthophosphate), neohexanediol trichlorobenzoate, 1,4-butanediol and adipic acid, in which tetramethylene bis(orthophosphate) and neohexanediol trichlorobenzoate were prepared previously in our laboratory. In this study, two-component flame-retardant polyurethane coatings (TTBA-10C/HDI-trimer=TTHD-10C, TTBA-20C/ HDI-trimer= TTHD-20C, TTBA-30C/HDI-trimer= TTHD-30C) were obtained by curing at room temperature with the synthesized TTBAs and hexamethylene diisocyanate (HDI)-trimer as a curing agent. The obtained TTHDs were made into coating samples and used as test samples for various physical properties. The physical properties of the flame-retardant coatings containing chlorine and phosphorus groups were generally inferior to those containing only phosphorus group. Flame retardancy was tested by vertical and horizontal combustion method, and 45˚ Meckel burner method. Since the retardancy of flame-retardant coatings containing chlorine and phosphorus groups was better than that containing only phosphorus group, it could be concluded that the retardancy by the synergism effect of chlorine and phosphorus groups exhibited.

The aim of this study is to synthesis basic resins for the preparation of PU flame-retardant coatings that contain phosphorus and chlorine. After synthesizing intermediates of tetramethylene bis(orthophophate) (TMBO) and neohexanediol trichlorobenzoate (TBA-adduct), the condensation polymerization was performed with the intermediates, 1,4-butanediol, and adipic acid to obtain four-component copolymers. In the condensation polymerization, the content of phosphorus was fixed to be 2%, and the content of trichlorobenzoic acid (TBA) that provides chlorine component was varied to be 10, 20, and 30wt%, and we designated the prepared modified polyesters containing chlorine and phosphorus as TTBA-10C, TTBA-20C and TTBA-30C. Average molecular weight and polydispersity index of the prepared TTBAs decreased with increasing TBA content because of the increase in the number of hydroxyl groups that retards reaction. We found that the thermal stability of the prepared TTBAs increased with chlorine content at high temperatures.

To maximize a synergy effect in flame-retardancy of flame-retardant coatings, phosphorus and chlorine were introduced in polymer chains. Two-components PU flame-retardant modified polyesters (ABTTC-10C, -20C, -30C) were prepared by curing, at room temperature, of isocyanate (allophanate-trimer) and prepared modified polyesters which contain phosphorus and chlorine. To examine the film properties of the prepared flame-retardant coatings, film specimens were prepared with the prepared coatings. The film properties of ABTTC, ABTTC-10C and ABTTC-20C, which contain 0, 10 and 20wt%, 2,4-dichlorobenzoic acid (2,4-DCBA), respectively, were proved to be good, whereas the film properties of ABTTC-30C, which contains 30wt% 2,4-DCBA, were proved to be a little bit poor. Two kinds of flame retardancy tests, 45˚Meckel burner method and LOI method, were performed. With the 45˚Meckel burner method, three flame-retardant coatings except ABTTC showed less than 3.4 cm of char length, and showed less than 2 seconds of afterflaming and afterglow. From this result, the prepared flame-retardant coatings were proved to have the 1st grade flame retardancy. With the LOI method, the LOI values of the coatings containing more than 10wt% 2,4-DCBA were higher than 30wt%, which means that the coatings possess good flame-retardancy. From these results, it was found that synergistic effect in flame-retardancy was taken place by the introduced phosphorus and chlorine.

This study was focused on the maximization of flame-retardancy of polyesters by a synergism of simultaneously introduced chlorine and phosphorus into polymer chains of modified polyesters. To prepare modified polyesters, reaction intermediates, TD-adduct (prepared from trimethylolpropane /2,4-dichlorobenzoic acid (2,4-DCBA)) and TMBO (prepared from tetramethlene bis (orthophosphate)), were prepared first, then condensation polymerization of the prepared intermediates, adipic acid, and 1,4-butanediol were carried out. In the condensation polymerization, the content of phosphorus was fixed to be 2wt%, and the content of 2,4-DCBA that provides chlorine component was varied to be 10, 20, and 30wt%, and we designated the prepared modified polyesters containing chlorine and phosphorus as ABTTs. The prepared intermediates and modified polyesters were characterized with FT-IR, NMR, GPC, and TGA analysis. Average molecular weight and polydipersity index of the preparation of ABTTs were decreased with increasing 2,4-DCBA content because of the incease in hydroxyl group that retards reaction. We found that the thermal stability of the prepared ABTTs increased with chlorine content at high temperatures.