Graphene oxide (GO) laminate is a new promising material for water purification system, which has extraordinary permeability only for water molecule. It consists of numerous nano-channels, in which water molecules could be nano-confined, resulting in slip of the molecules for very fast transportation speed. In this study, water penetration rate via different thickness of GO membrane according to driven pressures are measured experimentally, so that speed of water molecules and permeability are evaluated. Generally, water penetration rate via a membrane with macroscopic-sized channel increases linearly with pressure difference between up and bottom side of the membrane, but that via GO membrane approaches asymptotic value (i.e. saturation) as like a log function. Moreover, the permeability of GO membrane was observed in inverse proportion to its thickness. Based on the experimental observations, a correlation for volume flux via GO membrane was suggested with respect to its thickness and external pressure difference.

고분자 재질의 압력 구동 기반 분리막을 이용하여 담수를 얻기 위한 공정은 에너지 효율이 높은 방법으로 알려져 있다. 하지만, 분리막 운전 중에 투과성능을 떨어트리는 막 오염 문제가 발생 하기에, 막 오염을 제어하는 것은 분리막 공정의 에너지 효율을 높이는 데 필수적이다. 막 오염은 일반적으로 분리막 표면과 막 오염 물질과의 상호 작용으로 발생하며, 분 리막 표면을 개질하는 방법은 막 오염을 방지하여 높은 투과 특성을 지속적으로 유지하게 할 수 있는 좋은 방법 중 하나이다. 본 논문에서는 압력 구동 기반 분리막인 미세여과, 한외여과, 나노여과 및 역삼투용 분리막의 표면을 개질할 수 있는 방법을 정리하였다. 구체적인 개질 방법으로는 개질 물질의 흡착 및 코팅 방법인 물리적 방법과 가교제 이용, 자유 라디칼 중합 (FRP), 원자 이동 라디칼 중합(ATRP), 플라즈마 및 자외선 조사 기반 중합인 화학적 방법으로 나누어 정리하였다. 본 총설에서는 최근 논문상에 보고되고 있는 물리화학적 표면 개질 방법을 소개하고, 막 오염 저항성을 높일 수 있는 분리막 제조를 위한 연구방향을 제시하고자 한다.