Plant growth and morphology are affected by light environments. The morphogenesis and growth of the plants growing in plant factories are different from those grown under sunlight due to the effect of far-red light included in sunlight. The objective of this study was to compare the morphogenesis and growth of cucumber plants grown under artificial sunlight, high pressure sodium lamp (HPS), and HPS with additional far-red light (HPS+FR). The artificial solar (AS) with a spectrum similar to sunlight was manufactured using sulfur plasma lamp, incandescent lamp, and green-reducing optical film. HPS was used as a conventional electrical light source and far-red LEDs were added for HPS+FR. The optical properties of each light source was analyzed. The morphogenesis, growth, and photosynthetic rate were compared in each light source. The ratio of red to far-red lights and phytochrome photostationary state were similar in AS and HPS+FR. There were significant differences in morphology and growth between HPS and HPS+FR, but there were no significant differences between AS and HPS+FR. SPAD was highest in HPS, while photosynthetic rate was higher at AS and HPS. Although the photosynthetic rate in HPS+FR was lower than HPS, the growth was similar in AS. It was because canopy light interception was increased by longer petioles and larger leaf areas induced by FR. It is confirmed that the electrical light with additional far-red light induces similar photomorphogenesis and growth in sunlight spectrum. From the results, we expect that similar results will be obtained by adding far-red light to electrical light sources in plant factories.

Eu3+ -doped Y2O3 red phosphor was synthesized in a flux method using the chemicals Y2O3, Eu2O3,H3BO3 and BaCl2·2H2O. The effect of a flux addition on the preparation of Y2O3:Eu3+ red phosphor used asa cold cathode fluorescence lamp was investigated. H3BO3 and BaCl2·2H2O fluxes were used due to theirdifferent melting points. The crystallinity, thermal properties, morphology, and emission characteristics weremeasured using XRD, TG-DTA, SEM, and a photo-excited spectrometer. Under UV excitation of 254nm, Eu2O33.7mol% doped Y2O3 exhibited a strong narrow-band red emission, peaking at 612nm. From this result, thephosphor synthesized by firing Y2O3 with 3.7mol% of Eu2O3, 0.25mol% of H3BO3 and 0.5mol% of BaCl2·2H2Ofluxes at 1400oC for 2 hours had a larger particle size of 4µm on average compared to the phosphor of theH3BO3 flux alone. In addition, a phosphor synthesized by the two fluxes together had a rounder corner shape,which led to the maximum emission intensity.

The objective of this GM Red-X project was to reduce customer complaints on Kalos, Lacetti, Magnus as reported through 2004.1 - 2005.1 warranty performance. Seatbelt alarm lamp mal-function problem is connected with safety. So it is critical issue. Seatbelt alarm lamp mal-function which caused by buckle occurred 22 cases from 2004.1 to 2005.1.