This study investigated the microstructure and wear resistance property of HPHT (high pressure high temperature) sintered PDC (polycrystalline diamond compact) in accordance with initial molding pressure. After quantifying an identical amount of diamond powder, the powder was inserted in top of WC-Co sintered material, and molded under four different pressure conditions (50, 100, 150, 200 kgf/cm2). The obtained diamond compact underwent sintering in high pressure, high temperature conditions. In the case of the 50 kgf/cm2 initial molding pressure condition, cracks were formed on the surface of PDC. On the other hand, PDCs obtained from 100~200 kgf/cm2 initial molding pressure conditions showed a meticulous structure. As molding pressure increased, low Co composition within PDC was detected. A wear resistance test was performed on the PDC, and the 200 kgf/cm2 condition PDC showed the highest wear resistance property.

High-energy mechanical milling (HEMM) and sintering into Al-Mg alloy melt were employed tofabricate an Al alloy matrix composite reinforced with submicron and micron sized Al2O3 particles. Al-basedmetal matrix composite (MMC) reinforced with submicron and micron sized Al2O3 particles was successfullyfabricated by sintering at 1000oC for 2h into Al-Mg alloy melt, which used high energy mechanical milled Al-SiO2-CuO-ZnO composite powders. Submicron/micron-sized Al2O3 particles and eutectic Si were formed by in situdisplacement reaction between Al, SiO2, CuO, and ZnO during sintering for 2h into Al-Mg alloy melt and werehomogeneously distributed in the Al-Si-(Zn, Cu) matrix. The refined grains and homogeneously distributedsubmicron/micron-sized Al2O3 particles had good interfacial adhesive, which gives good wear resistance withhigher hardness.

Austenitic stainless steel has been used as a corrosion resistance material. However, austenitic stainless steel has poor wear resistance property due to its low hardness. In this investigation, we apply powder composite process to obtain hard layer of Stainless steel. The composite material was fabricated from planetary ball milled SUS316L stainless steel powder and WC powder and then sintered by Pulsed Current Sintering (PCS) method. We also added TiC powder as a hard particle in WC layer. Evaluations of wear properties were performed by pin-on-disk wear testing machine, and a remarkable improvement in wear resistance property was obtained.