A novel sintering process is proposed for bonding of and layers. Common commercial glass was used and infilterated among filler particles. As the kind of commercial glass, the phenomenon of the infilteration is different. Although Sud-1140 glass forms a glass/filler composite, it is not completely infilterated into the filler particles at . However as the increase of sintering temperature the infilteration of glass was improved. In this study, GA-1 and GA-12 glasses were infilterated the more than Sud-1140 glass. However, they are reacted by layer. The results of the experiment show that constrained sintering and the co-firing of the different materials were possible for glass infilteration using Sud-1140 glass at .