        Two sintering methods of a pressureless sintering and a spark-plasma sintering are tested to densify the Fe-TiC composite powders which are fabricated by high-energy ball-milling. A powder mixture of Fe and TiC is prepared in a planetary ball mill at a rotation speed of 500 rpm for 1h. Pressureless sintering is performed at 1100, 1200 and 1300oC for 1-3 hours in a tube furnace under flowing argon gas atmosphere. Spark-plasma sintering is carried out under the following condition: sintering temperature of 1050oC, soaking time of 10 min, sintering pressure of 50 MPa, heating rate of 50oC, and in a vacuum of 0.1 Pa. The curves of shrinkage and its derivative (shrinkage rate) are obtained from the data stored automatically during sintering process. The densification behaviors are investigated from the observation of fracture surface and cross-section of the sintered compacts. The pressureless-sintered powder compacts show incomplete densification with a relative denstiy of 86.1% after sintering at 1300oC for 3h. Spark-plasma sintering at 1050oC for 10 min exhibits nearly complete densification of 98.6% relative density under the sintering pressure of 50 MPa.
        4,000원
        73.
        2015.06 KCI 등재 구독 인증기관 무료, 개인회원 유료
        Fe-TiC composite powders are fabricated by planetary ball mill processing. Two kinds of powder mixtures are prepared from the starting materials of (a) (Fe, TiC) powders and (b) (Fe, TiH2, Carbon) powders. Milling speed (300, 500 and 700 rpm) and time (1, 2, and 3 h) are varied. For (Fe, TiH2, Carbon) powders, an in situ reaction synthesis of TiC after the planetary ball mill processing is added to obtain a homogeneous distribution of ultrafine TiC particulates in Fe matrix. Powder characteristics such as particle size, size distribution, shape, and mixing homogeneity are investigated. In case of (Fe, TiC) powder many coarse TiC particulates with size of several μm are unevenly distributed in Fe-matrix. The composite powder prepared from (Fe, TiH2, C) powder mixture showed a homogeneous dispersion of ulatrafine TiC particulates.
        4,000원
        74.
        2014.12 KCI 등재 구독 인증기관 무료, 개인회원 유료
        Super air heater devices have some advantages such as compact structure, energy-saving, long service life and convenient installation. In this paper, an automatic production process for air heaters is proposed to compensate some disadvantages of the manual process. The enhancement of production efficiency and productivity is confirmed through the heat treatment performance test decreasing defectiveness rate of 0.23% compared with the previous device.
        4,000원
        77.
        2013.10 KCI 등재 구독 인증기관 무료, 개인회원 유료
        Fe-TiC composite was fabricated from Fe and TiC powders by high-energy milling and subsequent spark- plasma sintering. The microstructure, particle size and phase of Fe-TiC composite powders were investigated by field emission scanning electron microscopy and X-ray diffraction to evaluate the effect of milling conditions on the size and distribution of TiC particles in Fe matrix. TiC particle size decreased with milling time. The average TiC particle size of 38 nm was obtained after 60 minutes of milling at 1000 rpm. Prepared Fe-TiC powder mixture was densified by spark- plasma sintering. Sintered Fe-TiC compacts showed a relative density of 91.7~96.2%. The average TiC particle size of 150 nm was observed from the FE-SEM image. The microstructure, densification behavior, Vickers hardness, and frac- ture toughness of Fe-TiC sintered compact were investigated.
        4,000원
        78.
        2013.03 KCI 등재 구독 인증기관 무료, 개인회원 유료
        We present a multi-dimensional reduction method of the surveyed cube database obtained using a single- dish radio telescope in Taeduk Radio Astronomy Observatory (TRAO). The multibeam receiver system installed at the 14 m telescope in TRAO was not optimized at the initial stage, though it became more stabilized in the following season. We conducted a Galactic Plane survey using the multibeam receiver system. We show that the noise level of the first part of the survey was higher than expected, and a special reduction process seemed to be definitely required. Along with a brief review of classical methods, a multi-dimensional method of reduction is introduced; It is found that the ‘background’ task within IRAF (Image Reduction and Analysis Facility) can be applied to all three directions of the cube database. Various statistics of reduction results is tested using several IRAF tasks. The rms value of raw survey data is 0.241 K, and after primitive baseline subtraction and elimination of bad channel sections, the rms value turned out to be 0.210 K. After the one-dimensional reduction using ‘background’ task, the rms value is estimated to be 0.176 K. The average rms of the final reduced image is 0.137 K. Thus, the image quality is found to be improved about 43% using the new reduction method.
        4,000원
        80.
        2012.06 구독 인증기관·개인회원 무료
        The reactive oxygen species (ROS) generated during the somatic cell transfer nuclear (SCNT) procedures may cause the mitochondrial dysfunction and DNA damage, which may result in restricts the reprogramming of SCNT embryos and play a key direct role in apoptosis. The present study was conducted to investigate the effect of antioxidant treatment during the SCNT procedures on the inhibition of mitochondria and DNA damages in bovine SCNT embryos. The reconstituted oocytes were treated with antioxidants of 25 μM β-mercaptoethanol (β-ME) or 50 μM vitamin C (Vit. C) during the SCNT procedures. In vitro fertilization (IVF) was performed for controls. Mitochondrial morphology and membrane potential (ΔΨ) were evaluated by staining the embryos with MitoTracker Red or JC-1. Apoptosis was analyzed by Caspase-3 activity assay and TUNEL assay, and DNA fragmentation was measured by comet assay at the zygote stage. Mitochondrial morphology of non-treated SCNT embryos was diffused within cytoplasm without forming clumps, while the IVF embryos and antioxidant treated SCNT embryos were formed clumps. The ΔΨ of β-ME (1.3±0.1, red/green) and Vit. C-treated (1.4±0.2, red/green) SCNT embryos were significantly higher (p<0.05) than that of non-treated SCNT embryos (0.9±0.1, red/ green), which similar to that of IVF embryos (1.3±0.1, red/green). Caspase-3 activity was not difference among the groups. TUNEL assay also revealed that little apoptosis was occurred in SCNT embryos as well as IVF embryos regardless of antioxidant treatment. Comet tail lengths of β-ME and Vit. C-treated SCNT embryos (337.8±23.5 μm and 318.7 ±27.0 μm, respectively) were shorter than that of non-treated SCNT embryos (397.4± 21.4 μm) and similar to IVF embryos (323.3±10.6 μm). These results suggest that antioxidant treatment during SCNT procedures can inhibit the mitochondrial and DNA damages of bovine SCNT embryos.
        1 2 3 4 5