The purpose of this study is to evaluate salt attack durability of the concrete structure which has experienced the fire. Mechanical properties and chloride ion diffusivity of concrete specimens were measured after 2 hours heating at 200℃, 400℃, 600℃, 800℃. FEM analysis was conducted to predict the life expectancy of RC structure using the property values by a series of experiment.

The purpose of this study is to evaluate salt attack durability of the concrete structure which has experienced the fire. Mechanical properties and chloride ion diffusivity of concrete specimens were measured after 2 hours heating at 200℃, 400℃, 600℃, 800℃. FEM analysis was conducted to predict the life expectancy of RC structure using the property values by a series of experiment

Changes in temperature and humidity inside a concrete has correlation with movement speed and reaction rate of deterioration factors such as carbon dioxide and chloride ions. comparison was performed between temperature and relative humidity inside the concrete and meteorological data for exposure environment through measurement at the site for two years.

Even though high performance concrete was developed according to becoming bigger and higher of reinforced concrete building, the rheological evaluation is not enough to use as input data to accomplish the numerical analysis of construction design. Consistency curves were measured by the viscometer as hydration reaction time passed. There are a sudden change of viscosity and yield stress around initial setting in case of low W/B. The increase of workability by the change of free water in cement paste was offset by the coating effect of impermeable layer in case of W/B 40%.

Based on the study of chloride migration coefficient and hydration heat evolution, it was found that the use of ternary blended cement was effective to achieve desired service life and minimum crack index. On the other hand, a high level of compressive strength is required for marine concrete mix design.

The purpose of this study is to examine whether cementitious powder separated from waste concrete can be used as the alternative raw material for limestone and reducing the usage of natural resource (limestone) and CO2emission based on recycling cementitious powder from waste concrete. Therefore, to reduce waste and CO2 emission in the cement industry and develop recycled cement, mix design was deducted by multi-objective optimization.

영도대교는 부산 최초의 연륙교로서 1934년 준공된 이후, 수차례의 보수보강 공사를 거쳤으며 2011년 이후 현재까지 확장 복원을 위하여 철거공사를 실시하고 있다. 본 조사연구의 목적은 영도대교 건설 당시의 교량 기술 및 재료적 특성 분석 함으로써 근대 구조에 사용된 콘크리트의 당시 재료적 특성을 파악하고 근대 교량문화유산의 보존 및 활용을 위한 기초적 자료를 구축하는 데 있다. 일련의 실험을 통하여 콘크리트 구성재료는 시멘트 : 세골재 : 굵은골재 비율이 부위에 따라 1 : 2 : 4 또는 1 : 3 : 6 인 것으로 밝혀졌고, 압축강도는 50~55MPa, 탄성계수는 25~35GPa의 범위로 나타났다. 역학적 물성의 편차가 10%이하인 점을 미뤄봐서 당시의 품질관리가 비교적 우수했던 것을 알 수 있었다. 중성화 깊이는 높은 상대습도로 상당히 낮은 값을 나타내었고, 염소이온 확산계수는 1.052e-12(m2/s)로서 현대 콘크리트와 비교하면 물시멘트비 35%에 상응하는 것으로 밝혀졌다.

Quantification of incoming-salt in the air is absolutely critical for the use of the boundary conditions in chloride resistance design. Thus, as a result of collecting incoming-salt by using multidirectional incoming-salt collector, it was confirmed that incoming-salt was collected not only in the direction of viewing the coast but also in the opposite direction. For this, it is believed that it is necessary to analyze the relationship between the effective defense incoming-salt and the non-effective defense incoming-salt that is delivered through a local flow of surrounding wind

콘크리트는 물시멘트비에 상응하는 공극을 가지게 되며, 공극을 통한 염소이온의 확산을 평가하기 위하여 해안가 폭로 및 해수 침지실험이 널리 사용된다. 이상의 실험은 경우에 따라서 다년간의 시간을 요하는 경우도 있어, 최근에는 전기 영동법에 기초한 급속 염소이온 확산시험을 실시하는 경우가 많으나, 그 값이 폭로 및 침지 시험에서 얻은 값과 상이한 경우가 많아 데이터의 실용성을 높이기 위하여 그 원인 규명이 절실한 실정이다. 본 연구에서는 평가 방법으로써 Nernst-Einstein의 식을 통한 염화물 이온 이동계수의 산정방법을 사용하였으며, NT BUILD 492법 및 해수 침지실험을 통한 확산 특성과 비교하여 값의 차이에 대하여 고찰하였다. 그 결과 실험인자의 변화가 염소이온 확산에 미치는 영향은 미비한 것으로 평가되어져 실험조건에서 발생하는 영향은 거의 없는 것으로 규명되었으며, NT BUILD 492법과도 거의 동일한 값이 구해졌다. 침지실험 결과와의 상이는 염소이온 확산에서 경계조건의 차이 및 염소이온의 시멘트 수화물과의 고정화에 의한 것으로 판단되어진다.

해안철근콘크리트 구조물은 해수 또는 비래염분에 의하여 철근이 부식하게 되고 결과적으로 콘크리트에 균열로 발전하여 성능을 다하게 된다. 본 연구에서는 염해에 대한 해안 철근콘크리트 구조물의 내구성능 평가를 위하여 수치해석에 의한 결정론적 방법이 아니라 확률론에 입각한 성능평가를 위하여 확률론적 시뮬레이션 수법을 구축하였다. 시뮬레이션 수법으로는 몬테카를로법이 적용되었으며, 파괴확률에 대한 설계확률변수(표면염화물 농도, 초기 함유 염소이온농도, 철근의 피복두께, 염소이온 확산계수) 및 각각의 변동계수의 영향을 평가하였다. Fick의 확산방정식을 이용한 해석결과, 해안에서의 거리의 차 및 확산계수의 차에 의한 영향은 컸으며 상대적으로 변동계수의 영향은 그다지 높지 않다는 것을 알 수 있었다.