One of the main purposes of architectural history is the analysis of existing designs in order to find laws and orders of certain types, while space planning emphasizes the generation of design. In this study, relational space planning methodology is used to generate Chosun upper-class housing prototypes based on 'Yaejae' logic model. During the Chosun Dynasty era in Korea, Confucianism was the ruling ideology for its society. The patio type house was the main upper-class housing type during the Chosun Dynasty, and it can be viewed that space planning was heavily influenced by the law of 'Yaejae' in Confucianism. The logic of 'Yaejae' can be interpreted as relationships between spaces. Relational space planning methodology that reasons through constraint propagation is used to generate prototypes. Prototypes are compared in order to verify actual applications of the logic into space planning.

니켈-흑연 복합분말은 고온 고압하에서 수소개스를 사용하여 ammoniacal황산니켈염 수용액으로 부터 니켈이온을 흑연코어표면에 석출시켜 제조하였으며, SEM. X-선 회절분석, 입도 및 화학분석 등을 이용하여 환원속도 및 니켈코팅층의 특성에 미치는 코팅 촉매제 Anthraquinone(C6H4COC6H4 CO) 의 영향을 조사하였다. 코팅촉매제의 입도 및 첨가량 변호에 따라 수소개스 주입 후 환원반응이 시작되기 까지 필요한 잠복기는 22~70분 정도 이었으며, 흑연코어 표면의 니켈코팅층은 포도송이 모양(botryoidal)인 미립의 니켈 nodule(2-4μm)로 형성되었다. 또한 코팅촉매제의 첨가량이 증가함에 따라 코팅용액중 니켈이온의 환원속도는 증가하여 0.2gr/ℓ첨가시 4.5gr/ℓ/min를 나타내었다.

본 연구에서는 다공성 니켈재료의 원료분말로 활용될 수 있는 hollw 니켈금속분말 계조를 위한 니켈-흑연복합분말의 흑연코어 기화과정에 관하여 실험을 행하였다. 수증개-수소 혼합가스에 의한 복합분말중 흑연코어의 기화온도는 800˚C~900˚C였으며, 약 1시간의 기화반응에 의해 내부가 텅 빈 hollw니켈금속분말을 얻을 수 있었다. 흑연코어의 평균입도가 21μm인 82.2tw,% 니켈-17.87tw.5 흑연 복합분말로부터 제조된 hollw니켈금속분말을 100Kg/c m2의 압력으로 압축, 성형한 성형체의 겉보기 기공도는 45%이었으며, 이성형체를 진공로에서 1150˚C 의 온도로 1시간 소결하여 30%의 기공도와 소재내에 균질한 기공분포를 갖즌 소결체를 얻음으로써 다공성재료 제조시 hollow분말을 원료로 사용하여 재료 내의 기공에 관한 제반사항을 쉽게 조절할 수 있다는 가능성을 확인하였다.