With the current increase in national income, consumers are favoring expensive home appliances. Many aluminum parts are used to improve the appearance of TV products. However, many losses are incurred due to production defects. There are many flaws in the bending process. This study studied the improvement of bending defects during fault handling. The material used is an aluminum alloy (6063), and the product is a serrated component on the surface of an aluminum part. After the bending process, it was identified how the sawtooth area was twisted. Then, while bending, experimented to find the main cause of the defect. The study tried to find maximum effectiveness with a minimum experiment using 6 sigma techniques. The experiment showed that there were many defects depending on the bending speed of the part and the distance it was fixed. The experiment used a method of finding optimal conditions by combining variables from each item. As a result, the failure was minimized when the distance between the two axes was maintained at 4.5-5mm and the bending speed was maintained at 15mm/sec. The component fixation force has a fixed hook in the middle of the product, and therefore it is found that changes in the amount of byte for the fixed part do not result in significant improvements in the defect.

InGaAs/InGaAsP 다층박막을 corrugation이 형성된 InP 기판위에 MOVPE 방법을 이용하여 성장 시킨 후 성장조건에 따른 corrugation 높이의 변화와 석출상에 대하여 투과전자현미경을 이용하여 시킨 후 성장조건에 따른 corrugation 높이의 변화와 석출상에 대하여 투과전자현미경을 이용하여 연구하였다. Corrugation이 형성된 InP 기판을 PH3 및 AsH3가스를 동시에 공급해 주었는데 AsH3 가스의 압력이 높으면(1.8x10-2torr)많은 양의 As를 포함한 In1-xAsxP(x=0.3)석출상이 격자결함과 더불어 형성되었다. 반면에 AsH3 가스의 압력이 낮을때는 (1.0x10-3torr) corrugation의 높이가 30nm이었고, 적은 양의 As를 포함한 In1-xAsxP(x<0.1)석출상이 격자결함이 없이 형성되었다.