In recent years, researchers have put a considerable effort to decrease the emission of harmful gaseous pollutants to the atmosphere. In order to remove simultaneously SO₂ and NOx from the flue gas of small and medium-sized ship, we designed minimal wet scrubber inside a compact multistage modular system. In this study we proceed experiment of elemental technology at each stage of the scrubber. The each stage is oxidation of NO which is the main component of NOx, and removal of SO₂, respectively. NaClO₂ was used to oxidize NO gas, and NaOH was used to remove SO₂gas. The maximum NO conversion efficiency and the SO₂ removal ficiency are both indicate 100%.

In this study, CO₂ adsorbent was produced for minimizing energy loss due to ventilation within the building. For improved selectivity about low concentration of CO₂ in multiple-use facilities, the ball type adsorbent was modified from a commercial zeolite, alumina, alkali metals and activated carbon with mixing LiOH, binder, and H₂O. We measured specific surface area, pore characteristic, and crystal structure of the modified adsorbent. Effects of alkalization on the absorptive properties of the adsorbents were investigated. Continuous column tests (2,000 ppm) and batch chamber tests (4m3, 5,000ppm) showed that the modified adsorbent indicated about the selectivity of CO₂ more than 9.7% (0.613 mmol/g) compared with ordinary adsorbents and CO₂ removal efficiency of 88.8% within l hour, respectively. It was estimated that the modified adsorbent was applicable to indoor environments.

The microstructure and positive temperature coefficient of resistivity (PTCR) characteristics of 0.1mol%Na2Ti6O13doped 0.94BaTiO3-0.06(Bi0.5Na0.5)TiO3 (BBNT-NT001) ceramics sintered at various temperatures from 1200oC to 1350oC wereinvestigated in order to develop eco-friendly PTCR thermistors with a high Curie temperature (TC). Resulting thermistors showeda perovskite structure with a tetragonal symmetry. When sintered at 1200oC, the specimen had a uniform microstructure withsmall grains. However, abnormally grown grains started to appear at 1250oC and a homogeneous microstructure with large grainswas exhibited when the sintering temperature reached 1325oC. When the temperature exceeded 1325oC, the grain growth wasinhibited due to the numerous nucleation sites generated at the extremely high temperature. It is considered that Na2Ti6O13 isresponsible for the grain growth of the 0.94BaTiO3-0.06(Bi0.5Na0.5)TiO3 ceramics by forming a liquid phase during the sinteringat around 1300oC. The grain growth of the BBNT-NT001 ceramics was significantly correlated with a decrease of resistivity.All the specimens were observed to have PTCR characteristics except for the sample sintered at 1200oC. The BBNT-NT001ceramics had significantly decreased ñrt and increased resistivity jump with increasing sintering temperature at from 1200oC to1325oC. Especially, the BBNT-NT001 ceramics sintered at 1325oC exhibited superior PTCR characteristics of low resistivityat room temperature (122Ω·cm), high resistivity jump (1.28×104), high resistivity temperature factor (20.4%/oC), and a highTc of 157.9oC.

For use in ultrasonic actuators, we investigated the structural and piezoelectric properties of (1 - x)Pb(Zr0.515Ti0.485)O3 - xPb(Sb1/2Nb1/2)O3 + 0.5 wt% MnO2 [(1 - x)PZT - xPSN + MnO2] ceramics with a variation of x (x = 0.02, 0.04, 0.06, 0.08). All the ceramics, which were sintered at 1250˚C for 2 h, showed a typical perovskite structure, implying that they were well synthesized. A homogeneous micro structure was also developed for the specimens, and their average grain size was slightly decreased to 1.3μm by increasing x to 0.8. Moreover, a second phase with a pyrochlore structure appeared when x was above 0.06, which resulted in the deterioration of their piezoelectric properties. However, the 0.96PZT-0.04PSN+MnO2 ceramics, which corresponds with a morphotropic phase boundary (MPB) composition in the (1 - x)PZT - xPSN + MnO2 system, exhibited good piezoelectric properties: a piezoelectric constant (d33) of 325 pC/N, an electromechanical coupling factor (kp) of 70.8%, and a mechanical quality factor (Qm) of 1779. The specimens with a relatively high curie temperature (Tc) of 305˚C also showed a significantly high dielectric constant (εr) value of 1109. Therefore, the 0.96PZT - 0.04PSN + MnO2 ceramics are suitable for use in ultrasonic vibrators.