Magnesium and magnesium alloys are promising materials for light weight and high strength applications. In order to obtain homogeneous and high quality products in powder compaction and powder forging processes, it is very important to control density and density distributions in powder compacts. In this study, a model for densification of metallic powder is proposed for pure magnesium. The mode] considers the effect of powder characteristics using a pressure-dependent critical density yield criterion. Also with the new model, it was possible to obtain reasonable physical properties of pure magnesium powder using cold iso-state pressing. The proposed densification model was implemented into the finite element method code. The finite element analysis was applied to simulating die compaction of pure magnesium powders in order to investigate the density and effective strain distributions at room temperature.

In the present study, Zr-base metallic glass (MG) and Zr-base BMG/diamond composites were fabricated using a combination of gas atomization and spark plasma sintering (SPS). The microstructure, thermal stability and mechanical property of both the specimens as atomized and sintered were investigated. The experimental results showed that the SPSed specimens could be densified into nearly 100% and maintained the initial thermal stability at the sintering temperature of 630K. In addition, MG/diamond powder composites were successfully synthesised using SPS process. The composites, even a very low diamond volume fraction, generated a significant increase in compressive strength. With increasing the diamond volume fraction, the compressive strength was also increased due to the addition of hardest diamonds. It suggests that these composites would be potential candidates for a new cutting tool material.

This work is to report not only the effect of rapid solidification of alloys on the micro-structure, but also the extrusion behavior on the materials properties. The average grain size of the atomized powders was about . The alloy powders of , consisted of I-Phase (Icosahedral, ) as well as Cubic structured W-Phase (), which was finely distributed within matrix. The oxide layer formed along the Mg surface was about 48 nm in thickness. In order to study the consolidation behavior of Mg alloy powders, extrusion was carried out with the area reduction ratio of 10:1 to 20:1. As the ratio increased, fully deformed and homogeneous microstructure could be obtained, and the mechanical properties such as tensile strength and elongation were simultaneously increased.

Bulk metallic glass (BMG) composite was fabricated by consolidation of milled metallic glass composite powders. The metallic glass composite powder was synthesized by a controlled milling process using the Cu-based metallic glass powder blended with 30 vol% Zr-based metallic glass powders. The milled composite powders showed a layered structure with three metallic phases, which is formed as a result of mechanical milling. By spark plasma sintering of milled metallic glass powders in the supercooled liquid region, a fully dense BMG composite was successfully synthesized.

Using Spark Plasma Sintering process (SPS), consolidation behavior of gas atomized alloys were investigated via examining the microstructure and evaluating the mechanical properties. In the atomized ahoy powders, fine particles were homogeneously distributed in the matrix. The phase distribution was maintained even after SPS at 723 K, although particles were newly precipitated by consolidating at 748 K. The density of the consolidated bulk Mg-Zn-Y alloy was . The ultimate tensile strength (UTS) and elongation were varied with the consolidation temperature.

Using spark plasma sintering process (SPS), Ti-6Al-4V alloy powders were successfully consolidated without any contamination happened due to reaction between the alloy powders and graphite mold. Variation of microstructure and mechanical properties were investigated as a function of SPS temperature and time. Compared with hot isostatic pressing (HIP), the sintering time and temperature could be lowered to be 10 min. and , respectively. At the SPS condition, UTS and elongation were about 890 MPa and 24%, respectively. Considering the density of 98.5% and elongation of 24%, further improving the tensile strength would obtain by increasing the SPS pressure.

Mg-4.3Zn-0.7Y (at%) alloy powders were prepared using an industrial scale gas atomizer, followed by warm extrusion. The powders were almost spherical in shape. The microstructure of atomized powders and those extruded bars was examined using Scanning Electron Microscopy (SEM), Energy Dispersive X-ray Spectroscope (EDS) and X-ray Diffractometer (XRD). The grain size of the powders was coarsen as the initial powder size increased. After the extrusion, the grain size became fine due to the severe plastic deformation during the extrusion with the ratio of 10:1. Both the ultimate strength and elongation were enhanced with the decrease of initial particle size.

This work is to present a new synthesis of metallic glass (MG)/metallic glass (MG) composites using gas atomization and spark plasma sintering (SPS) processes. The MG powders of (CuA) and (NiA) as atomized consist of fully amorphous phases and present a different thermal behavior; (glass transition temperature) and (crystallization temperature) are 716K and 765K for the Cu base powder, but 836K and 890K for the Ni base ones, respectively. SPS process was used to consolidate the mixture of each amorphous powder, being in weight. The resultant phases were Cu crystalline dispersed NiA matrix composites as well as NiA phase dispersed CuA matrix composites, depending on the SPS temperatures. Effect of the second phases embedded in the MG matrix was discussed on the micro-structure and mechanical properties.

본 연구에서는 소수성 PTFE (Polytetrafluoroethylene) 분리막의 산소동위원소 분리특성을 확인하기 위해 물의 온도에 따른 수증기의 막 투과특성을 Air Cap Membrane Distillation (AGMD)과 Vacuum Enhanced Membrane Distillation (VEMD) 방법을 이용하여 각각 측정하였다. 투과된 수증기는 트랩에서 수거하여 투과플럭스 (permeation flux)를 측정하였고 H216O와 H218O의 성분비는 다이오드 레이저 흡수분광법을 이용하여 측정하였다. 분리막을 투과한 수증기에서 무거운 산소동위원소의 성분비가 감소함을 확인하였고 분리계수는 실험 조건에 따라 1.004~1.01로 측정되었다. 또한 분리막의 기공에 있는 공기가 산소동위원소의 분리에 미치는 영향을 확인하였고 기공내 공기가 없을 때 동위원소 분리계수가 증가함을 관찰하였다.

나노입자는 일반적인 크기의 입자에서 볼 수 없는 특성을 나타내므로 촉매, 광학, 자성기록매체, 자성유체로의 자유로운 응용이 기대되어지고 있으며, 다양한 조성의 나노재료 및 제조공정에 관한 연구개발이 활발히 이루어지고 있는 추세이다. 이중 나노재료제조공정은 기상응축, 열분해법, 플라즈마법 및 볼밀링법 등이 상용화되어 있으며, 본 연구에서는 화학적균일성과 다양한 조성으로의 응용이 용이한 화학기상응축공정을 이용하여 Fe/N나노분말을 제조하였다. 제조된 Fe/

Ni coated composite was successfully Prepared by the electroless deposition Process. The average size of Ni particles coated on the matrix powder was about 20 nm. It was hard to find any reaction compound as an impurity at interface between and Ni particles after sintering. The characterization of microstructure crystal structure and fracture behavior of the sintered body were investigated using XRD, TEM and Victors hardness tester, and compared with those of the sintered monolithic body. Many dislocations were observed in the Ni phase due to the difference of thermal expansion coefficient between and Ni phase, and no observed microcracks at their and Ni interface. In the /Ni composite, the main fracture mode showed a mixed fracture with intergranular and transgranuluar type having some ,surface roughness. The fracture toughness was slightly increased due to the plastic deformation mechanism of Ni phase in the /Ni composite.

Hybrid ceramic particle reinforced 6061 and 5083 Al composite powders were prepared by the combination of twin rolling and stone mill crushing process, followed by consolidating processes of cold compaction, degassing and hot extrusion. The composite bar consists of lamellar structure of ceramic particle rich area and matrix area, in which the hybrid was decomposed into each TiC of about and particles of about in diameter. It also found that fine precipitates of about 30 nm were embedded in the matrix, which have grains of about 3 . Higher UTS was measured at the 5083 composite bar compared to the conventionally fabricated composite, due to again refinement effect by the rapid solidification. No particle was shown to form in the interface between the matrix and reinforcement, whereas carbon was diffused into the matrix.