Nd-Fe-B type powder was sintered using spark plasma sintering method. Fabricated compact sintered at the temperature of , is found to be a composite magnet with Nd-Fe-Co-B and . The compact sintered at shows slightly low coercivity and large remanent magnetization comparing to the compact sintered at due to the formation of phase, resulting in the large maximum energy product. Maximum energy product tends to decrease with decreasing thickness of sintered compacts below 0.5 mm in thickness.