Carbon nanotubes (CNTs) have attracted remarkable attention as reinforcement for composites owing to their outstanding mechanical properties. The CNT/Cu nanocomposite is fabricated by a novel fabrication process named molecular level process. The novel process for fabricating CNT/Cu composite powders involves suspending CNTs in a solvent by surface functionalization, mixing Cu ions with CNT suspension, drying, calcination and reduction. The molecular level process produces CNT/Cu composite powders whereby the CNTs are homogeneously implanted within Cu powders. The mechanical properties of CNT/Cu nanocomposite, consolidated by spark plasma sintering of CNT/Cu composite powders, shows about 3 times higher strength and 2 times higher Young's modulus than those of Cu matrix.

This study investigated a mechanism for controlling the shape of Cu nanocrystals fabricated using the polyol process, which considers the thermodynamic transition from a facetted surface to a rough surface and the growth mechanisms of nanocrystals with facetted or rough surfaces. The facetted surfaces were stable at relatively low temperatures due to the low entropy of perfectly facetted surfaces. Nanocrystals fabricated using a coordinative surfactant stabilized the facetted surface at a higher temperature than those fabricated using a non-coordinative surfactant. The growth rate of the surface under a given driving force was dependent on the surface structure, i.e., facetted or rough, and the growth of a facetted surface was a thermally activated process. Surface twins decreased the activation energy for growth of the facetted surface and resulted in rod- or wire-shaped nanocrystals